Sunshield film transparent to radio frequency energy and shielded articles

• US 5,916,668 A
• Filed: 12/22/1995
• Issued: 06/29/1999
• Est. Priority Date: 12/22/1995
• Status: Expired due to Term

• Current Assignee: Hughes Aircraft Company (Rtx Corporation)
• Original Assignee: Hughes Electronics Corporation (Rtx Corporation)
• Inventors: Hironaka, Frank D., Long, Lynn E.
• Primary Examiner(s): Thibodeau, Paul
• Assistant Examiner(s): TARAZANO, DONALD LAWRENCE
• Application Number:
  US08/577,983
• Time in Patent Office: 1,285 Days
• Field of Search: 428/447, 428/212, 428/213, 428/216, 428/473.5, 428/215, 343/873, 343/846, 343/872, 343/885
• US Class Current: 428/215
• CPC Class Codes: H01Q 1/002 Protection against seismic waves, thermal radiation or other disturbances, e.g. nuclear explosion; Arrangements for improving the power handling capability of an antenna
• CPC Class Codes: H01Q 1/288 Satellite antennas
• CPC Class Codes: H01Q 17/001 for modifying the directional characteristic of an aerial
• CPC Class Codes: Y10T 428/24967 Absolute thicknesses specified
• CPC Class Codes: Y10T 428/24975 No layer or component greater than 5 mils thick
• CPC Class Codes: Y10T 428/31663 As siloxane, silicone or silane
• CPC Class Codes: Y10T 428/31721 Of polyimide

Abstract

A structure protected by a sunshield film includes an article, for example a spacecraft radio-frequency antenna, and a sunshield film protecting the article surface. The sunshield film is formed as a sheet substrate made of a material that is transparent to radio frequency energy, a white coating on one side of the sheet substrate, and a black coating on the other side of the sheet substrate. The white coating and the black coating each have a surface resistivity of from about 10⁸ to about 10⁹ ohms per square.

Claims

1. A sunshield film, comprising

a sheet substrate made of a material that is transparent to radio frequency energy, the sheet substrate having a first side and a second side;

a white coating on the first side of the sheet substrate, the white coating having a surface resistivity of from about 10⁸ to about 10⁹ ohms per square; and

a black coating on the second side of the sheet substrate, the black coating having a surface resistivity of from about 10⁸ to about 10⁹ ohms per square.

2. The sunshield film of claim 1, wherein the sheet substrate is a polymeric material.

3. The sunshield film of claim 1, wherein the sheet substrate is a polyimide.

4. The sunshield film of claim 1, wherein the sheet substrate has a thickness of from about 0.001 inch to about 0.003 inch.

5. The sunshield film of claim 1, wherein the white coating comprises a silicone polymeric matrix having doped zinc oxide pigment particles distributed therein, the zinc oxide pigment particles being doped with an element that forms shallow donorlike states in the zinc oxide.

6. The sunshield film of claim 1, wherein the white coating has a thickness of from about 0.004 inch to about 0.006 inch.

7. The sunshield film of claim 1, wherein the black coating comprises a silicone polymeric matrix having carbon pigment particles distributed therein.

8. The sunshield film of claim 1, wherein the black coating has a thickness of from about 0.001 inch to about 0.002 inch.

9. The sunshield film of claim 1, wherein

the sheet substrate is a polyimide having a thickness of from about 0.001 inch to about 0.003 inch,

the white coating comprises a silicone polymeric matrix having doped zinc oxide pigment particles distributed therein, the zinc oxide pigment particles being doped with an element that forms shallow donorlike states in the zinc oxide, and wherein the white coating has a thickness of from about 0.004 inch to about 0.006 inch;

and

the black coating comprises a silicone polymeric matrix having carbon pigment particles distributed therein, and wherein the black coating has a thickness of from about 0.001 inch to about 0.002 inch.

10. The sunshield film of claim 1, wherein the white coating comprises a silicone polymeric matrix having doped zinc oxide pigment particles distributed therein, the zinc oxide pigment particles being doped with an element selected from the group consisting of aluminum, boron, gallium, indium, zinc, tin, and hydrogen.

11. The sunshield film of claim 1, wherein

the sheet substrate is a polyimide having a thickness of from about 0.001 inch to about 0.003 inch,

the white coating comprises a silicone polymeric matrix having doped zinc oxide pigment particles distributed therein, the zinc oxide pigment particles being doped with an element selected from the group consisting of aluminum, boron, gallium, indium, zinc, tin, and hydrogen, and wherein the white coating has a thickness of from about 0.004 inch to about 0.006 inch;

and

the black coating comprises a silicone polymeric matrix having carbon pigment particles distributed therein, and wherein the black coating has a thickness of from about 0.001 inch to about 0.002 inch.