First Claim
1. A dual porosity tube made by a method comprising the steps of:
- a. concentrically joining a first preformed tubular billet and a second preformed tubular billet each of the first and second preformed tubular billets comprising;
i. PTFE resin particles having an average particle size greater than or equal to 355 μ
; and
ii. a lubricant, the first and second tubular billets having predetermined lube levels in the range of 50 to 150 grams of lubricant to 500 grams PTFE resin and different from one and other;
b. co-extruding the first and second preformed tubular billets to meld the inner and outer billets into a composite tubular extrudate having an inner surface with a first porosity and an outer surface with a second porosity different from the first porosity;
c. longitudinally expanding the extrudate; and
d. sintering the extrudate.
0 Assignments
0 Petitions
Accused Products
Abstract
A dual porosity PTFE tube including an inner surface of expanded PTFE material having a first porosity and an outer surface of expanded PTFE material having a porosity different from that of the inner surface. The preferred method includes the step of forming inner and outer preformed tubular billets of PTFE resin particles mixed with a lubricant; the outer billet is adapted to closely fit around and concentric to the inner billet. Porosity of the inner and outer surfaces is varied by changing, in the respective billets, the lubrication level and/or the PTFE resin characteristic average particle size. The inner billet is placed inside the outer billet, and the two are extruded together, thereby melding the two billets. The extrudate is then longitudinally expanded and sintered. The inner surface of the resulting PTFE tube exhibits a different porosity than the outer surface of the tube; the porosities of the inner and outer surfaces are both within a range of about 0.10-200 μ.
77 Citations
25 Claims
-
1. A dual porosity tube made by a method comprising the steps of:
-
a. concentrically joining a first preformed tubular billet and a second preformed tubular billet each of the first and second preformed tubular billets comprising; i. PTFE resin particles having an average particle size greater than or equal to 355 μ
; andii. a lubricant, the first and second tubular billets having predetermined lube levels in the range of 50 to 150 grams of lubricant to 500 grams PTFE resin and different from one and other; b. co-extruding the first and second preformed tubular billets to meld the inner and outer billets into a composite tubular extrudate having an inner surface with a first porosity and an outer surface with a second porosity different from the first porosity; c. longitudinally expanding the extrudate; and d. sintering the extrudate. - View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9)
-
-
10. A dual porosity tube made using a method comprising the steps of:
-
a. forming a first preformed tubular billet of PTFE resin particles and a lubricant, the lubricant being present at 10 to 30 weight percent of the PTFE resin; b. forming a second preformed tubular billet of PTFE resin particles and a lubricant, the lubricant being present at 10 to 30 weight percent of the PTFE resin and different from that of the first preformed tubular billet; c. concentrically joining the first preformed billet and the second preformed billet to form a co-extrusion billet; d. extruding the co-extrusion billet to meld the first and second preformed tubular billets into a composite tubular extrudate; e. longitudinally expanding the extrudate to create a porous PTFE microstructure in which an inner surface of the longitudinally expanded PTFE tubular extrudate has a first average internodal distance within the range of about 8 to 60 μ
m, and an outer surface of the longitudinally expanded PTFE tubular extrudate has a second average internodal distance within the range of about 16 to 68 μ
m and is different from the first average internodal distance; andf. sintering the extrudate. - View Dependent Claims (11, 12)
-
-
13. A dual porosity PTFE tube made in accordance with the method comprising the steps of:
-
a. preforming a first preformed compressed tubular billet comprised of an admixture of PTFE resin particles and lubricant, the lubricant being present at a ratio in the range of 50 to 150 grams of lubricant to 500 grams PTFE resin; b. preforming a second preformed compressed tubular billet comprised of an admixture of PTFE resin particles and lubricant, the lubricant being present at a ratio in the range of 50 to 150 grams of lubricant to 500 grams PTFE resin and at a value different from that of the first preformed compressed tubular billet; c. concentrically joining the first preformed compressed tubular billet within the second preformed compressed tubular billet a first preformed tubular billet and a second preformed tubular billet to form a co-extrusion billet; d. extruding the co-extrusion billet through an extrusion barrel and die and about an extrusion mandrel to meld the first and second preformed tubular billets into a composite tubular extrudate having an inner surface with a first average internodal distance within the range of about 8 to 60 μ
m, and an outer surface with a second average internodal distance within the range of about 16 to 68 μ
m and is different from the first average internodal distance;e. longitudinally expanding the extrudate; and f. sintering the extrudate. - View Dependent Claims (14, 15, 16, 17, 18, 19, 20, 21)
-
-
22. A dual porosity tube made by a method comprising the steps of:
-
a. forming a first preformed tubular billet of PTFE resin particles and a lubricant, the lubricant being present at 10 to 30 weight percent of the PTFE resin; b. forming a second preformed tubular billet of PTFE resin particles and a lubricant, the lubricant being present at 10 to 30 weight percent of the PTFE resin and different from that of the first preformed tubular billet; c. concentrically joining the first preformed tubular billet and the second preformed tubular billet to form a co-extrusion billet; d. extruding the co-extrusion billet to meld the first and second preformed tubular billets into a composite tubular extrudate; e. longitudinally expanding the extrudate to create a porous PTFE microstructure in which an inner surface of the longitudinally expanded PTFE tubular extrudate has a first average internodal distance within the range of about 8 to 60 μ
m, and an outer surface of the longitudinally expanded PTFE tubular extrudate has a second average internodal distance within the range of about 16 to 68 μ
m and is different from the first average internodal distance; andf. sintering the extrudate wherein the step of longitudinally expanding the extrudate further comprises the steps of; i. inserting an expansion plug into each of two opposing ends of the tubular extrudate; ii. concentrically engaging a deformable band about each of the two opposing open ends of the tubular extrudate and the inserted expansion plug; and iii. deforming the deformable band about the inserted expansion plug and the tubular extrudate at each of the two opposing open ends of the tubular extrudate, thereby creating an interference fit between the deformable band and the expansion plug to retain each opposing open ends of the tubular extrudate there between. - View Dependent Claims (23)
-
-
24. A dual porosity PTFE tube, consisting essentially of:
-
a first bias layer of expanded polytetrafluoroethylene characterized by a node-fibril microporous microstructure and having a first average internodal distance within the range of about 8 to 60 μ
; anda second bias layer of expanded polytetrafluoroethylene characterized by a node-fibril microstructure and having a second average internodal distance within the range of about 16 to 68 μ and
which is different from the first average internodal distance of the first bias layer, the second bias layer of expanded polytetrafluoroethylene being concentrically joined to and in intimate contact with the first bias layer of expanded polytetrafluoroethylene.
-
-
25. A dual porosity tube made by a method comprising the steps of:
-
a. concentrically joining a first preformed tubular billet and a second preformed tubular billet, the first preformed tubular billet comprising PTFE resin particles having an average particle size less than or equal to about 200 μ and
a lubricant, and the second preformed tubular billet comprising PTFE resin particles having an average particle size greater than or equal to about 700 μ and
a lubricant, the lubricant being present in the first and second tubular billets at a concentration within the range of about 50 to 150 grams of lubricant to 500 grams PTFE resin and different within the first tubular billet than the second tubular billet;b. co-extruding the separately preformed compressed inner and outer billets to meld the inner and outer billets into a composite tubular extrudate having an inner surface with a first porosity and an outer surface with a second porosity different from the first porosity; c. longitudinally expanding the extrudate; and d. sintering the extrudate.
-
Specification