Solar control window film

• US 5,956,175 A
• Filed: 07/31/1998
• Issued: 09/21/1999
• Est. Priority Date: 07/31/1998
• Status: Expired due to Term

• Current Assignee: Saint-Gobain Performance Plastics Corporation (Compagnie De Saint-Gobain)
• Original Assignee: MSC Specialty Films, Inc. (Compagnie de Saint-Gobain SA)
• Inventors: Hojnowski, Steven L.
• Primary Examiner(s): HENRY, JON W
• Application Number:
  US09/127,311
• Time in Patent Office: 417 Days
• Field of Search: 359/360, 359/361, 359/350, 359/885, 359/890, 359/891, 428/216, 428/430, 428/34, 428/458
• US Class Current: 359/360
• CPC Class Codes: B32B 17/10018 comprising only one glass sheet
• CPC Class Codes: B32B 17/10174 Coatings of a metallic or dielectric material on a constituent layer of glass or polymer
• CPC Class Codes: B32B 27/36 comprising polyesters
• CPC Class Codes: G02B 5/208 for use with infrared or ultraviolet radiation, e.g. for separating visible light from infrared and/or ultraviolet radiation

Abstract

A solar control window film having high visible light transmission and low transmission of near infrared heat energy is comprised of a transparent substrate bearing a thin, optically transparent layer of metal, an optically transparent layer of near infrared energy absorbing material and a transparent layer of protective material overlying and protecting the near infrared energy absorbing material and the metal. The near infrared reflecting properties and the near infrared absorbing properties of the respective layers are balanced to provide selective solar heat rejection without excessive transfer of heat into the window glass or glazing material.

Claims

1. A solar control window film consisting essentially of a substantially transparent substrate bearing thereon an optically transparent metal coating having selected transmission of visible light and selected reflection of visible light and near infrared energy, and an optically transparent layer comprising near infrared energy absorbing material,

said window film on clear glass having visible light transmission of from about 50% to about 80%, near infrared energy reflectance of from about 40% to about 60%, near infrared energy absorptance from about 5% to about 35%, and near infrared energy transmission of from about 5% to about 35%.

2. A window film as set forth in claim 1 wherein the substrate comprises a transparent polymer containing an ultraviolet absorber.

3. A window film as set forth in claim 1 wherein the film has a water vapor transmission rate of 0.4 or more grams per square meter over twenty-four hours at one atmosphere.

4. A window film as set forth in claim 1 wherein the layer comprising near infrared energy absorbing material comprises a protective coating overlying the metal coating.

5. A window film as set forth in claim 1 wherein the near infrared energy absorbing material absorbs energy primarily within the wavelength range of from about 800 to about 1100 nanometers.

6. A window film as set forth in claim 1 wherein the film on clear glass has visible light transmission of from about 65% to about 75% and, on average in the near infrared band of about 800 to about 1100 nanometers, near infrared energy reflectance in the order of about 50%, near infrared energy absorptance in the order of about 25% and near infrared energy transmission in the order of about 25%.

7. A window film as set forth in claim 1 having a shading coefficient in the order of about 0.52 at a visible light transmission of about 65%.

8. A window film as set forth in claim 1 having a solar selectivity index in the order of about 1.23 at a visible light transmission of about 65%.

9. A solar control window film consisting essentially of

a substantially transparent substrate bearing thereon an optically transparent metal coating having selected transmission of visible light and selected reflection of visible light and near infrared energy,

an optically transparent layer of adhesive on one side of the metal coated substrate,

a substantially transparent layer of protective material on the other side of the metal coated substrate, and

near infrared energy absorbing material comprising one or more near infrared energy absorbing substances dispersed in the adhesive or incorporated into or coated onto the substrate or the layer of protective material,

said window film on clear glass having visible light transmission of from about 50% to about 80%, near infrared energy reflectance of from about 40% to about 60%, near infrared energy absorptance from about 5% to about 35%, and near infrared energy transmission of from about 5% to about 35%.

10. A window film as set forth in claim 9 wherein the layer of protective material comprises a clear polymer bearing on its exposed surface a scratch and wear resistant hard coat.

11. A window film as set forth in claim 10 wherein the near infrared energy absorbing material is dispersed in the hard coat.

12. A window film as set forth in claim 9 for application to a window having an exterior surface exposed to solar energy and an interior surface proximate to a space to be protected from solar energy, said layer of adhesive affixing the substrate to the interior surface of the window with the near infrared energy absorbing material proximate to said space.

13. A solar control window film consisting essentially of

a substantially transparent substrate bearing thereon an optically transparent metal coating having selected transmission of visible light and selected reflection of visible light and near infrared energy,

an optically transparent layer of pressure sensitive adhesive on one side of the metal coated substrate for adhering the film to a window,

a substantially transparent layer of protective material adhesively laminated to the other side of the metal coated substrate, and

near infrared energy absorbing material comprising one or more near infrared energy absorbing substances dispersed in either or both of the pressure sensitive adhesive and the laminating adhesive or incorporated into or coated onto the substrate or the layer of protective material,

said window film on clear glass having visible light transmission of from about 50% to about 80%, near infrared energy reflectance of from about 40% to about 60%, near infrared energy absorptance from about 5% to about 35%, and near infrared energy transmission of from about 5% to about 35%.

14. A window film as set forth in claim 13 wherein the layer of protective material comprises a clear polymer bearing on its exposed surface a scratch and wear resistant hard coat.

15. A window film as set forth in claim 14 wherein the near infrared energy absorbing material is dispersed in the hard coat.