• US 5,963,121 A
• Filed: 11/11/1998
• Issued: 10/05/1999
• Est. Priority Date: 11/11/1998
• Status: Expired due to Term

• Current Assignee: Ferro Corporation
• Original Assignee: Ferro Corporation
• Inventors: Ekis, John J., Pointer, Brian T., Stygar, Vernon E., Osuna, Jesus E.
• Primary Examiner(s): Picard, Leo P.
• Assistant Examiner(s): Vortman, Anatoly
• Application Number:
  US09/190,032
• Time in Patent Office: 328 Days
• Field of Search: 337/155, 337/297, 337/290, 337/295, 337/167, 337/180, 337/181, 337/26, 337/31, 337/251, 337/14, 338/204, 338/205, 338/22 R, 338/23, 252/511, 252/512
• US Class Current: 337/155
• CPC Class Codes: H01C 7/028 consisting of organic substances
• CPC Class Codes: H01H 85/046 Fuses formed as printed circuits
• CPC Class Codes: H01H 87/00 Protective devices in which a current flowing through a liquid or solid is interrupted by the evaporation of the liquid or by the melting and evaporation of the solid when the current becomes excessive, the circuit continuity being reestablished on cooling
• CPC Class Codes: H05K 1/0293 Individual printed conductors which are adapted for modification, e.g. fusable or breakable conductors, printed switches
• CPC Class Codes: H05K 1/095 for polymer thick films, i.e. having a permanent organic polymeric binder
• CPC Class Codes: H05K 2201/10181 Fuse

Abstract

The present invention relates to compositions for use in forming resettable electronic circuit protection devices or fuses, methods of forming resettable fuses using the compositions, and resettable fuses formed from the compositions. Resettable fuse compositions according to the present invention include a mixture of the reaction product of polyethylene glycol and a diepoxide having a molecular weight of at least 18,000, solvent, conductive particles, and optional solvent volatility adjusters. In a preferred embodiment, resettable fuses according to the present invention are formed by screen printing the compositions directly onto printed electric circuits to form fuses. During current overload conditions, the temperature of the resettable fuse material rapidly increases due to resistive heating generated by excessive current flow through the conductive particle chains or pathways. In such current overload conditions, resettable fuses according to the present invention rapidly convert from a low resistance solid state to a high resistance liquidus state wherein the chains of conductive particles become highly separated thus causing the flow of electric current through the fuse to become completely cut off. After the overload condition has been cleared, resettable fuses according to the present invention self cool, re-solidify, and return to their prior low resistance solid state without exhibiting any change in resistance or switching temperature due to changes in the degree of crystallinity of the heat cured reaction product.

Claims

1. A resettable fuse comprising a fuse section and a first and a second fuse terminal disposed on a substrate, at least one of said fuse terminals being formed from a silver-filled epoxy resin material, said fuse section comprising a mixture of the reaction product of polyethylene glycol and a diepoxide having an average molecular weight of at least 18,000, solvent, conductive particles, and said solvent volatility adjusters, said mixture having been applied to said substrate so as to form a connection between said first and second fuse terminals and heated to flash off said solvent and said solvent volatility adjusters and cure said reaction product.

2. The resettable fuse of claim 1 wherein said reaction product prior to heat curing has an average molecular weight of at least 20,000.

3. The resettable fuse of claim 1 wherein said solvent is polar.

4. The resettable fuse of claim 3 wherein said solvent is water.

5. The resettable fuse of claim 1 wherein said conductive particles comprise one or more selected from the group consisting of silver, conductive carbon black, metal powders, alloy powders, conductive metal salts, and conductive metal oxides.

6. The resettable fuse of claim 5 wherein said conductive particles comprise silver flake having, a D₅₀ of 4.5 microns.

7. The resettable fuse of claim 1 wherein said conductive particles have a particle size of from about 0.01 to about 200 microns.

8. The resettable fuse of claim 7 wherein said conductive particles have a particle size of from about 3.0 to about 6.0 microns.

9. The resettable fuse of claim 1 wherein the shape of said conductive particles is one or more selected from the group consisting of flakes, rods, and spheroids.

10. The resettable fuse of claim 1 wherein said solvent volatility adjusters comprise one or more compounds selected from the group consisting of alcohols, ketones, and aldehydes.

11. The resettable fuse of claim 10 wherein said solvent volatility adjusters comprise isopropyl alcohol.

12. The resettable fuse of claim 1 wherein said mixture comprises by weight from about 10% to about 30% of said reaction product, from about 10% to about 30% of said solvent, from about 35% to about 65% of said conductive particles, and less than about 15% of said solvent volatility adjusters.

13. The resettable fuse of claim 1 wherein said mixture comprises by weight from about 15% to about 25% of said reaction product, from about 15% to about 25% of said solvent, from about 45% to about 55% of said conductive particles, and from about 5% to about 10% of said solvent volatility adjusters.

14. The resettable fuse of claim 1 wherein said mixture is applied to said substrate by screen printing.

15. The resettable fuse of claim 1 wherein said mixture prior to heat curing has a viscosity of from about 20,000 cps to about 70,000 cps at 25°

C.

16. The resettable fuse of claim 15 wherein said mixture prior to heat curing has a viscosity of from about 50,000 cps at 25°

C.

17. The resettable fuse of claim 1 wherein said substrate comprises a material selected from the group consisting of polyimide, FR4, alumina, glass and alumina nitride.

18. The resettable fuse of claim 1 wherein said mixture is heated for about 15 minutes to about 2 hours at from about 100°

C. to about 175°

C. to flash off said solvent and said volatility adjusters and cure said reaction product.

19. The resettable fuse of claim 1 wherein the melt temperature of said reaction product is within the range of from 60°

C. to about 150°

C.

20. The resettable fuse of claim 19 wherein upon reaching said melt temperature, said cured reaction product changes from an electrically conductive solid state to an electrically non-conductive liquidus state.