Ultrafine cementitious grout

• US 5,968,257 A
• Filed: 01/15/1998
• Issued: 10/19/1999
• Est. Priority Date: 08/29/1994
• Status: Expired due to Term

• Current Assignee: Sandia Corporation (Martin Marietta Corporation)
• Original Assignee: Sandia Corporation (Martin Marietta Corporation)
• Inventors: Ahrens, Ernst H.
• Primary Examiner(s): MARCHESCHI, MICHAEL A
• Application Number:
  US09/007,715
• Time in Patent Office: 642 Days
• Field of Search: 106/672, 106/676, 106/677, 106/678, 106/724, 106/725, 106/726, 106/737, 106/809, 106/816, 106/819, 106/823, 106/708
• US Class Current: 106/737
• CPC Class Codes: C04B 14/16 porous, e.g. pumice
• CPC Class Codes: C04B 20/008 Micro- or nanosized fillers, e.g. micronised fillers with particle size smaller than that of the hydraulic binder colloidal silica C04B14/062 ; silica fume C04B18/146
• CPC Class Codes: C04B 2103/32 Superplasticisers
• CPC Class Codes: C04B 2111/70 Grouts, e.g. injection mixtures for cables for prestressed concrete
• CPC Class Codes: C04B 24/226 Sulfonated naphtalene-formaldehyde condensation products
• CPC Class Codes: C04B 28/04 Portland cements

Abstract

An ultrafine cementitious grout in three particle grades containing Portland cement, pumice as a pozzolanic material and superplasticizer in the amounts of about 30 wt. % to about 70 wt. % Portland cement; from about 30 wt. % to about 70 wt. % pumice containing at least 70% amorphous silicon dioxide; and from 1.2 wt. % to about 5.0 wt. % superplasticizer. The superplasticizer is dispersed in the mixing water prior to the addition of dry grout and the W/CM ratio is about 0.4 to 1/1. The grout has very high strength and very low permeability with good workability. The ultrafine particle sizes allow for sealing of microfractures below 10 μm in width.

Claims

1. An ultrafine cementitious grout composition consisting essentially of:

from about 30 wt. % to about 70 wt. % Portland cement;

from about 30 wt. % to about 70 wt. % pumice; and

from 1.2 wt. % to about 5 wt. % superplasticizer;

wherein the Portland cement, the pumice and superplasticizer all having particle sizes such that approximately 90% of the particles are less than 17 μ

m in diameter and the average particle size is less than 8 μ

m in diameter.

2. The composition of claim 1 wherein the pumice contains at least 70% SiO₂.

3. The composition of claim 1 wherein the superplasticizer is a sulfonated salt of napthalyene formaldehyde.

4. The composition of claim 1 wherein the Portland Cement is a Type 3, Portland cement.

5. The composition of claim 1 further consisting essentially of water in an amount sufficient to provide the composition with a water/(Portland cement+pumice+superplasticizer) ratio of about 0.40 to 1.00.

6. An ultrafine cementitious grout composition consisting essentially of:

from about 30 wt. % to about 70 wt. % Portland cement;

from about 30 wt. % to about 70 wt. % pumice; and

from 1.2 wt. % to about 5 wt. % superplasticizer;

wherein the Portland cement, the pumice and superplasticizer all having particle sizes such that approximately 90% of the particles are less than 8 μ

m in diameter and the average particle size is less than 4 μ

m in diameter.

7. The composition of claim 6 wherein the pumice contains at least 70% SiO₂.

8. The composition of claim 6 wherein the superplasticizer is a sulfonated salt of napthalyene formaldehyde.

9. The composition of claim 6 wherein the Portland Cement is a Type 3, Portland cement.

10. The composition of claim 6, further consisting essentially of water in an amount sufficient to provide the composition with a water/(Portland cement+pumice+superplasticizer) ratio of about 0.40 to 1.00.

11. An ultrafine cementitious grout composition consisting essentially of:

from about 30 wt. % to about 70 wt. % Portland cement;

from about 30 wt. % to about 70 wt. % pumice; and

from 1.2 wt. % to about 5 wt. % superplasticizer;

wherein the Portland cement, the pumice and superplasticizer all having particle sizes such that approximately 90% of the particles are less than 5 μ

m in diameter and the average particle size is approximately 2.5 μ

m in diameter.

12. The composition of claim 11 wherein the pumice contains at least 70% SiO₂.

13. The composition of claim 11 wherein the superplasticizer is a sulfonated salt of napthalyene formaldehyde.

14. The composition of claim 11 wherein the Portland Cement is a Type 3 Portland cement.

15. The composition of claim 11, further consisting essentially of water in an amount sufficient to provide the composition with a water/(Portland cement+pumice+superplasticizer) ratio of about 0.40 to 1.00.

16. An ultrafine cementitious grout product made by a process comprising:

combining from about 30 wt. % to about 60 wt. % Portland cement with from about 40 wt. % to about 70 wt. % pumice containing at least 70% amorphous silicon dioxide,

placing the combined components in a high speed attritor grinding means containing zirconium silicate grinding media having a size approximately 2 mm in diameter,

grinding the combined components to form pulverized dry grout,

conveying the pulverized dry grout from the grinding means to an air classifier means having a first output which allows only particles of a size correlating to 90% of which are less than 5 μ

m in diameter and an average size of about 2.5 μ

m or less to pass and a second output for particles having a larger size than those passed by the first output,

conveying the particles from the second output back into the grinding means,

segregating the particles from the first output wherein the particles from the first output form dry ultrafine cemetitious grout product, and

upon use, combining the dry ultrafine cementitious grout product with mixing water containing superplasticizer in the amount of from about 1.2 to about 5 wt. % of the cement and pumice.