Friction material for a synchronizer ring

• US 5,969,001 A
• Filed: 09/09/1996
• Issued: 10/19/1999
• Est. Priority Date: 02/16/1996
• Status: Expired due to Fees

• Current Assignee: Dynax Corporation (Exedy Corporation)
• Original Assignee: Dynax Corporation (Exedy Corporation)
• Inventors: Kawai, Satoshi
• Primary Examiner(s): McCamish, Marion
• Assistant Examiner(s): Guarriello, John J.
• Application Number:
  US08/711,136
• Time in Patent Office: 1,135 Days
• Field of Search: 523/149, 523/158, 524/413, 524/423, 524/437, 524/440, 524/493, 524/494, 524/495, 524/593, 524/594, 524/15, 192/107 M
• US Class Current: 523/158
• CPC Class Codes: F16D 2200/0069 being characterised by their size
• CPC Class Codes: F16D 23/025 Synchro rings
• CPC Class Codes: F16D 69/026 containing fibres

Abstract

A friction material for a synchronizer ring which exhibits good heat resistance, wear resistance and scorching resistance properties has 30 to 70% by weight of a carbon material, 10 to 40% by weight of a thermosetting resin, 5 to 30% by weight of metal fibers or metal particles and 5 to 40% by weight of inorganic fibers or inorganic particles, and having a porosity of 10 to 50%. The carbon is porous graphite particles of a size distribution in which not less than 50% of the entire number of said graphite particles have a particle diameter from 44 to 250 μm. The thermosetting resin is a novolac type phenol resin, epoxy modified phenol resin, melamine modified phenol resin, cashew modified phenol resin, hydrocarbon resin modified phenol resin or cresol modified phenol resin. The metal fibers or metal particles are an alloy containing aluminum, copper, iron, nickel, zinc or lead as the main ingredient, the inorganic fibers or particles are barium sulfate, wollastonite, silicon, potassium titanate, glass or alumina and organic fibers and cashew dust are each contained in an amount of not more than 10% by weight.

Claims

1. A synchronizer ring for a gear change transmission, comprising:

a friction material for frictionally engaging a mating member of said gear change transmission so as to synchronously rotate said ring and member, said friction material comprising;

30 to 70% by weight of a carbon material;

10 to 40% by weight of a thermosetting resin;

5 to 30% by weight of metal fibers or metal particles; and

5 to 40% by weight of inorganic fibers or inorganic particles;

wherein said friction material has a porosity of 10 to 50% .

2. A synchronizer ring as defined in claim 1, wherein said carbon material is porous graphite particles and not less than 50% of the entire number of said graphite particles have a particle diameter from 44 to 250 μ

m.

3. A synchronizer ring as defined in claim 1, wherein said thermosetting resin is a phenol resin.

4. A synchronizer ring as defined in claim 1, wherein said metal fibers or metal particles are made of a metal alloy which contains as a main ingredient a metal selected from the group consisting of aluminum, copper, iron, nickel, zinc and lead.

5. A synchronizer ring as defined in claim 1, wherein said inorganic fibers or inorganic particles are made of a material selected from the group consisting of barium sulfate, wollastonite, silicon, potassium titanate, glass and alumina.

6. A synchronizer ring as defined in claim 1, further comprising organic fibers and cashew dust each of not more than 10% by weight.

7. A synchronizer ring as defined in claim 1, wherein said friction material defines a conical surface.

8. A synchronizer ring as defined in claim 1, further comprising a ring shaped structural body with which said friction material is integrally molded.

9. A synchronizer ring as defined in claim 8, wherein an inner circumferential surface of said synchronizer ring is defined by said friction material.

10. A synchronizer ring as defined in claim 9, wherein said inner circumferential surface of said synchronizer ring tapers in diameter.

11. A synchronizer ring as defined in claim 10, wherein said structural body defines a radially outer surface of said synchronizer ring.

12. A synchronizer ring as defined in claim 11, wherein said structural body is made of brass.