Oil resistant silicone sealants containing a metal acetate

• US 5,985,991 A
• Filed: 06/10/1997
• Issued: 11/16/1999
• Est. Priority Date: 06/10/1997
• Status: Expired due to Fees

• Current Assignee: Dow, Inc.
• Original Assignee: Dow, Inc.
• Inventors: Houck, Peter James, Lower, Loren Dale, Beljanski, Philip David
• Primary Examiner(s): Marquis, Melvyn I.
• Assistant Examiner(s): Milstead, Mark W.
• Application Number:
  US08/872,618
• Time in Patent Office: 889 Days
• Field of Search: 528/15, 528/21, 528/16, 528/17, 528/19, 528/14, 528/18, 524/779, 524/781, 524/789, 524/860
• US Class Current: 524/779
• CPC Class Codes: C08K 5/0025 Crosslinking or vulcanising agents; including accelerators
• CPC Class Codes: C08K 5/0091 Complexes with metal-heteroatom-bonds
• CPC Class Codes: C08K 5/098 Metal salts of carboxylic acids
• CPC Class Codes: C08L 83/04 Polysiloxanes

Abstract

The invention relates to a RTV silicone composition having increased hot oil resistance upon curing. The RTV silicone composition comprises a polydiorganosiloxane, an acyloxy-functional crosslinker, a metal salt of a carboxylic acid catalyst, a filler, and a metal acetate. In a preferred embodiment a metal acetylacetonate is also added.

Claims

1. A RTV silicone composition which is curable in the presence of moisture, comprising:

(A) 100 parts by weight of a polydiorganosiloxane in which the terminal groups are selected from the group consisting of silanol and triorganosilyl groups, provided at least 60 mole percent of the terminal groups are silanol groups;

(B) 1 to 15 parts by weight of an acyloxy-functional crosslinking agent described by the formula

space="preserve" listing-type="equation">R.sub.m Si(OCOR'"'"').sub.4-m

where R is a monovalent hydrocarbon radical comprising from 1 to about 12 carbon atoms, each R'"'"' is an independently selected monovalent hydrocarbon radical comprising from 1 to about 12 carbon atoms, and m is 0 or 1;

(C) 0.001 to 1 part by weight of a metal salt of a carboxylic acid catalyst, provided the metal salt of a carboxylic acid catalyst does not include calcium acetate, zinc acetate, magnesium acetate, aluminum acetate, zirconium acetate, barium acetate, titanium acetate, strontium acetate, and copper acetate;

(D) 5 to 150 parts by weight of a filler;

(E) an amount of a metal acetate effective for providing increased hot oil resistance to the RTV silicone composition upon curing, where the metal portion of the metal acetate is selected from the group consisting of calcium, zinc, magnesium, aluminum, zirconium, barium, titanium, strontium, and copper; and

(F) optionally, an amount of a metal acetylacetonate effective for providing increased hot oil resistance to the RTV silicone composition upon curing.

2. The RTV silicone composition of claim 1, where Component (E) comprises about 0.01 to 10 parts by weight of the metal acetate, based on 100 parts by weight of the polydiorganosiloxane.

3. The RTV silicone composition of claim 1, where Component (E) comprises about 0.01 to 1.5 parts by weight of the metal acetate, based on 100 parts by weight of the polydiorganosiloxane.

4. The RTV silicone composition of claim 1, where Component (E) comprises about 0.01 to 1 part by weight of strontium acetate or calcium acetate, based on 100 parts by weight of the polydiorganosiloxane.

5. The RTV silicone composition of claim 3, where the polydiorganosiloxane is a polydimethylsiloxane in which 80 to 100 mole percent of the terminal groups are silanol groups;

R and R'"'"' of the acyloxy-functional crosslinking agent are independently selected from the group consisting of methyl and ethyl, and m is 1;

the catalyst is a tin salt of a carboxylic acid; and

the filler is a silica filler.

6. The RTV silicone composition of claim 4, comprising:

(A) 100 parts by weight of a polydimethylsiloxane in which 80 to 100 mole percent of the terminal groups are silanol groups;

(B) 2 to 10 parts by weight of the acyloxy-functional crosslinking agent where R and R'"'"' are independently selected from the group consisting of methyl and ethyl, and m is 1;

(C) 0.01 to 0.3 part by weight of a tin salt of a carboxylic acid catalyst; and

(D) 5 to 30 parts by weight of a fumed silica.

7. The RTV silicone composition of claim 2, where Component (F) comprises about 0.01 to 5 parts by weight of the metal acetylacetonate based on 100 parts by weight of the polydiorganosiloxane.

8. The RTV silicone composition of claim 3, where Component (F) comprises about 0.05 to 1.5 parts by weight of the metal acetylacetonate based on 100 parts by weight of the polydiorganosiloxane, where the metal portion of the metal acetylacetonate is selected from the group consisting of copper, chromium, iron, aluminum, zinc, titanium and zirconium.

9. The RTV silicone composition of claim 4, where Component (F) comprises about 0.1 to 0.6 parts by weight copper acetylacetonate based on 100 parts by weight of the polydiorganosiloxane.

10. The RTV silicone composition of claim 8, where the polydiorganosiloxane is a polydimethylsiloxane in which 80 to 100 mole percent of the terminal groups are silanol groups;

R and R'"'"' of the acyloxy-functional crosslinking agent are independently selected from the group consisting of methyl and ethyl, and m is 1;

the catalyst is a tin salt of a carboxylic acid; and

the filler is a silica filler.

11. The RTV silicone composition of claim 9, comprising:

(A) 100 parts by weight of a polydimethylsiloxane in which 80 to 100 mole percent of the terminal groups are silanol groups;

(B) 2 to 10 parts by weight of the acyloxy-functional crosslinking agent where R and R'"'"' are independently selected from the group consisting of methyl and ethyl, and m is 1;

(C) 0.01 to 0.3 part by weight of a tin salt of a carboxylic acid catalyst; and

(D) 5 to 30 parts by weight of a fumed silica.