Briquette binder composition

• US 6,013,116 A
• Filed: 08/11/1998
• Issued: 01/11/2000
• Est. Priority Date: 02/02/1998
• Status: Expired due to Fees

• Current Assignee: Billy Joseph Major, George Radu
• Original Assignee: Billy Joseph Major, George Radu
• Inventors: Radu, George, Major, Billy Joseph
• Primary Examiner(s): Howard, Jacqueline V.
• Application Number:
  US09/132,506
• Time in Patent Office: 518 Days
• Field of Search: 44/551, 44/578
• US Class Current: 44/551
• CPC Class Codes: C10L 5/10 with the aid of binders, e.g. pretreated binders
• CPC Class Codes: C10L 5/40 essentially based on materials of non-mineral origin
• CPC Class Codes: C22B 1/242 with binders
• CPC Class Codes: Y02E 50/30 Fuel from waste, e.g. synthetic alcohol or diesel

Abstract

A binder composition for use in forming briquettes is disclosed. The composition comprises from about 5 to about 95% asphalt base and about 5 to about 95% sodium carbonate pulping liquor by weight. The binder composition may contain up to about 3% by weight of a surfactant, such as nonyl phenol ethoxylate, to increase homogeneity of briquette formation. Strength increasing additives such as latex, vinyl derivatives, cellulose, cellulose derivatives, peat moss, starch, starch derivatives, pulp from the pulp and paper industry, paper, cardboad, acrylic copolymers and combinations thereof, may be added to the binder composition in a total amount of up to about 10% by weight. Lignosulfonate may be added to the composition in an amount of up to about 30% by weight. An inorganic component such as cement or bentonite clay may be added in an amount of up to about 70% by weight, and up to about 30% by weight of a plasticizer such as rubber or plastic may be added. The binder composition may be used to agglomerate a briquette filler such as metal fines, coal fines, miniers, fly ash or other suitable briquette components.

Claims

1. A binder composition comprising up from about 1% to about 99% sodium carbonate pulping liquor by weight and from about 1% to about 99% asphalt base by weight.

2. The binder composition according to claim 1, additionally comprising lignosulfonate in an amount of up to about 30% by weight.

3. The binder composition according to claim 2, wherein the lignosulfonate is selected from the group comprising sodium lignosulfonate, ammonium lignosulfonate, calcium lignosulfonate and combinations thereof.

4. The binder composition according to claim 1, additionally comprising a surfactant.

5. The binder composition according to claim 4, wherein the surfactant is nonyl phenol ethoxylate.

6. The binder composition according to claim 1, additionally comprising a strength increasing additive selected from the group comprising latex, vinyl derivatives, cellulose, cellulose derivatives, peat moss, starch, starch derivatives, pulp from the pulp and paper industry, paper, cardboard, acrylic copolymers, and combinations thereof, in an amount of up to about 10% by weight.

7. The binder composition according to claim 6, wherein the vinyl derivatives are selected from the group consisting of polyvinyl acetate and polyvinyl alcohol.

8. The binder composition according to claim 6, wherein the cellulose derivatives are selected from the group consisting of carboxymethyl cellulose and hydroxy ethyl cellulosed.

9. A binder composition according to claim 1, comprising up to about 30% by weight of a plasticizer selected from the group comprising plastic and rubber.

10. A binder composition according to claim 1, comprising up to about 70% by weight of an inorganic component selected from the group comprising bentonite and cement.

11. A binder composition according to claim 1, comprising about 50% asphalt base and about 50% sodium carbonate pulping liquor by weight.

12. A binder composition according to claim 1, comprising about 35% asphalt base and about 65% sodium carbonate pulping liquor by weight.

13. A binder composition according to claim 1, wherein the solids content of the pulping liquor is from about 25 to about 100% by weight.

15. A briquette comprising briquette filler and the binder composition according to claim 1.

16. The briquette according to claim 15, wherein the binder composition is present in an amount of from about 1 to about 30% by weight of the briquette.

17. The briquette according to claim 15, wherein the binder composition is present in an amount of from about 2 to about 20% by weight of the briquette.

18. The briquette according to claim 15, wherein said binder composition comprises sodium carbonate pulping liquor having a solids content of from about 25% to about 100% by weight.

19. The briquette according to claim 15, additionally comprising up to about 3% of an acidifying agent by weight.

20. The briquette according to claim 15, additionally comprising a homopolymer.

22. A process for preparing a briquette comprising the steps of:

(i) combining briquette filler with about 1 to about 30% by weight of the binder composition of claim 1, and

(ii) compressing the product of step (i) into a briquette.

23. The process as defined in claim 22 further comprising a step of heat curing the briquette.

24. A briquette prepared by the process of claim 23.

25. A binder composition according to claim 1, comprising from about 20% to about 60% asphalt and from about 40% to about 80% sodium carbonate pulping liquor.

26. A briquette comprising briquette filler and from about 4% to about 10% of the binder composition according to claim 25.

14. A binder composition comprising from about 1 to about 99% pulping liquor by weight, from about 1 to about 99% asphalt base by weight, up to about 30% lignosulfonate by weight, up to about 3% surfactant by weight, up to about 10% of a strength increasing additive by weight, up to about 30% of a plasticizer by weight, and up to about 70% of an inorganic component by weight.

21. A briquette comprising about 1% to about 30% by weight of a binder composition according to claim 14, up to about 3% by weight of an acidifying agent, up to about 15% by weight of a homopolymer, and the balance being briquette filler.