High temperature insulation for ceramic matrix composites

• US 6,013,592 A
• Filed: 03/27/1998
• Issued: 01/11/2000
• Est. Priority Date: 03/27/1998
• Status: Expired due to Term

• Current Assignee: Siemens Energy Incorporated (Siemens AG)
• Original Assignee: Siemens Westinghouse Power Corporation
• Inventors: Merrill, Gary B., Morrison, Jay Alan
• Primary Examiner(s): Bell, Mark L.
• Assistant Examiner(s): SAMPLE, DAVID R
• Application Number:
  US09/049,328
• Time in Patent Office: 655 Days
• Field of Search: 501/80, 501/127, 501/128, 501/103, 501/105, 501/153, 501/154, 428/402, 428/472
• US Class Current: 501/80
• CPC Class Codes: C04B 14/30 Oxides other than silica ferrites C04B14/363
• CPC Class Codes: C04B 14/301 porous or hollow
• CPC Class Codes: C04B 14/303 Alumina
• CPC Class Codes: C04B 20/0076 characterised by the grain distribution
• CPC Class Codes: C04B 28/34 containing cold phosphate binders

Abstract

A ceramic composition is provided to insulate ceramic matrix composites under high temperature, high heat flux environments. The composite comprises a plurality of hollow oxide-based spheres of varios dimentions, a phosphate binder, and at least one oxide filler powder, whereby the phosphate binder partially fills gaps between the spheres and the filler powders. The spheres are situated in the phosphate binder and the filler powders such that each sphere is in contact with at least one other sphere. The spheres may be any combination of Mullite spheres, Alumina spheres, or stabilized Zirconia spheres. The filler powder may be any combination of Alumina, Mullite, Ceria, or Hafnia. Preferably, the phosphate binder is Aluminum Ortho-Phosphate. A method of manufacturing the ceramic insulating composition and its application to CMC substates are also provided.

Claims

1. A ceramic insulating composition comprising:

a plurality of hollow oxide-based spheres of various dimensions;

a phosphate binder; and

at least one oxide filler powder, whereby said phosphate binder partially fills gaps between said spheres and said filler powders;

whereby said spheres are situated in said phosphate binder and said filler powders such that each sphere is in contact with at least one other sphere.

2. The composition of claim 1 stable at temperatures up to approximately 1600°

C.

3. The composition of claim 1 having a coefficient of thermal expansion in the range of approximately 5.7×

10^-6 mm/mm°

C. to approximately 10×

10^-6 mm/mm°

C.

4. The composition of claim 1 having thermal conductivity less than approximately 2.5 W/km.

5. The composition of claim 1 having an erosion 20 resistance in the range of approximately 4.5 g/kg to approximately 7.5 g/kg, when measured at 1100°

C., a 15°

impingement angle, and an erodent speed of 900 ft/s.

6. The composition of claim 1, wherein spheres are selected by one or more of the following:

Mullite spheres;

Alumina spheres; and

stabilized Zirconia spheres.

7. The composition of claim 6, wherein:

each of said Mullite spheres has a diameter in the range of approximately 0.4 to approximately 1.8 mm;

each of said Alumina spheres has a diameter in the range of approximately 0.3 to approximately 1 mm; and

each of said stabilized Zirconia spheres has a diameter in the range of approximately 0.6 to approximately 1.2 mm.

8. The composition of claim 1, wherein said spheres are one of the following:

Mullite spheres, wherein said spheres have a weight percentage of 32%±

10% of the composition;

Alumina spheres, wherein said spheres have a weight percentage of 63%±

15% of the composition; and

Stabilized Zirconia spheres, wherein said spheres have a weight percentage of 58%±

15% of the composition.

9. The composition of claim 1, wherein said spheres are 20% Mullite of said spheres by volume and 80% Alumina of said spheres by volume.

10. The composition of claim 1, wherein said filler powder is one or more of the following:

Alumina;

Mullite;

Ceria; and

Hafnia.

11. The composition of claim 1, wherein said filler powder is Mullite filler powder.

12. The composition of claim 11, wherein said oxide filler powder has a weight percentage of 32%±

15% of the composition.

13. The composition of claim 1, wherein said phosphate binder is Aluminum Ortho-Phosphate.

14. The composition of claim 13, wherein said Aluminum Ortho-Phosphate has a weight percentage of 31%±

15% of the composition.

15. The composition of claim 13, wherein said filler powder is Mullite and said combination of said phosphate binder and said Mullite has a viscosity of approximately 9,000 centipoise.