Tire cure bladder composition with alkylphenoxypoly (alkyleneoxy) alkanol

• US 6,015,525 A
• Filed: 09/03/1998
• Issued: 01/18/2000
• Est. Priority Date: 09/03/1998
• Status: Expired due to Fees

• Current Assignee: Goodyear Tire & Rubber Company
• Original Assignee: Goodyear Tire & Rubber Company
• Inventors: Sandstrom, Paul Harry, Patitsas, George Philemon
• Primary Examiner(s): Vargot, Mathieu D.
• Application Number:
  US09/145,931
• Time in Patent Office: 502 Days
• Field of Search: 264/130, 264/131, 264/315, 264/326, 156/401, 425/35, 425/39, 425/43, 425/52, 249/65
• US Class Current: 264/315
• CPC Class Codes: B29C 2043/3644 Vacuum bags; Details thereof, e.g. fixing or clamping
• CPC Class Codes: B29C 43/3642 Bags, bleeder sheets or cauls for isostatic pressing
• CPC Class Codes: B29D 2030/0655 Constructional or chemical features of the flexible cores
• CPC Class Codes: B29K 2019/00 Use of rubber not provided for in a single one of main groups B29K2007/00 - B29K2011/00, as moulding material
• CPC Class Codes: C08L 23/22 Copolymers of isobutene; Butyl rubber ; Homo- or copolymers of other iso-olefins
• CPC Class Codes: C08L 2666/22 Macromolecular compounds not provided for in C08L2666/16 - C08L2666/20

Abstract

Disclosed are expandable bladders for use in curing presses for rubber compositions such as pneumatic tires. The bladders are a crosslinked elastomer comprising an isobutylene rubbery polymer. The bladder composition includes alkylphenoxypoly(alkyleneoxy)-alkanol which improves the release characteristics of the cured bladder from a tire innerliner cured in contact with said bladder. The improved release characteristics allow rubber compositions such as tires to be molded with fewer defects caused during release of the bladder from the tires or caused by abraded or deformed bladders. The use of alkylphenoxypoly(alkyleneoxy)alkanol also increases the useful life time of the bladder allowing more tires to be cured without changing bladders.

Claims

1. In a curing press for a rubber composition which uses an expandable bladder to assist in shaping and curing said rubber composition, wherein the bladder is made from crosslinking a rubber formulation including

one or more crosslinkable rubbery polymers, wherein at least 50 weight percent of said rubbery polymers of said bladder are at least one isobutylene rubbery polymer having at least 80 weight percent repeating units from isobutylene;

one or more curatives for said one or more rubbery polymers;

the improvement wherein the bladder further comprises from about 2 to about 15 parts by weight of a mono or poly(alkyl)phenoxypoly(alkyleneoxy)alkanol dispersed throughout said bladder, and

wherein said parts by weight are based on 100 parts by weight of said rubbery polymers in the rubber bladder formulation.

2. In a curing press according to claim 1, wherein at least 80 weight percent of said rubbery polymers of said bladder formulation is at least one isobutylene copolymer consisting essentially of repeating units from isobutylene and repeat units from one or more conjugated dienes of 4 to 8 carbon atoms, and wherein said alkyleneoxy of said mono or poly(alkyl)phenoxypoly(alkyleneoxy)alkanol is ethyleneoxy.

3. In a curing press according to claim 2, wherein at least 90 weight percent of said rubbery polymers of said bladder formulation consists essentially of repeat units from isobutylene and repeat units from one or more conjugated dienes of from 4 to 8 carbon atoms.

4. In a curing press according to claim 2, wherein said rubbery polymers of said bladder consist essentially of at least 90 weight percent repeating units from isobutylene and from about 1 to 10 weight percent repeating units from conjugated dienes of 4 to 8 carbon atoms, and optionally up to 10 weight percent halogenated repeating units other than brominated para-methylstyrene.

5. In a curing press according to claim 2, wherein said mono or poly(alkyl)phenoxypoly(alkyleneoxy)alkanol has on average from 5 to 30 ethyleneoxy repeating units and said mono or poly (alkyl) of said mono or poly(alkyl)phenoxypoly(alkyleneoxy)alkanol is a single octyl or nonyl group.

6. In a curing press according to claim 5, wherein said curing press is designed to shape and cure rubber compositions into pneumatic tires.

7. An expandable curing bladder comprising:

one or more rubbery polymers, wherein at least 50 weight percent of said rubbery polymers are at least one isobutylene rubbery polymer having at least 80 weight percent repeating units from isobutylene;

from about 2 to about 15 PHR of a mono or poly (alkyl)phenoxypoly(alkyleneoxy)alkanol dispersed throughout said bladder, wherein said alkyl has from 6 to 12 carbon atoms and said alkylene has from 2 to 3 carbon atoms; and

one or more curatives for said rubbery polymers,

wherein PHR is parts by weight based upon 100 parts by weight of said one or more rubbery polymers in said bladder.

8. An expandable curing bladder according to claim 7, wherein said alkylene is ethylene, and said poly(ethyleneoxy) has from 5 to 30 repeat units.

9. In a method of using an expandable rubber bladder to cure an uncured rubber composition, said method including the sequential steps of:

inserting an uncured rubber composition into a curing press having an expandable rubber bladder positioned therein and having one or more molding surfaces,

expanding said expandable rubber bladder by filling the internal portion of said bladder with a fluid to expand the bladder outwardly against an inner surface of the uncured rubber composition to force said uncured rubber composition against said one or more molding surfaces,

curing the rubber composition into a cured article under conditions of heat and pressure, and

deflating said expandable rubber bladder and removing the cured article from said curing press,

the improvement wherein the expandable bladder comprises;

one or more rubbery polymers at least 50 weight percent being of at least one rubbery isobutylene polymer having at least 80 weight percent repeating units from isobutylene;

from about 2 to about 15 parts by weight of mono or poly(alkyl)phenoxypoly(alkyleneoxy)alkanol dispersed throughout said bladder, wherein said alkyl has from 6 to 12 carbon atoms and said alkylene has from 2 to 3 carbon atoms,

wherein said parts by weight are based upon 100 parts by weight of said one or more rubbery polymers in said bladder.

10. A method according to claim 9, wherein said rubber composition being cured is a pneumatic tire.

11. In a curing press for a rubber composition which uses an expandable bladder to assist in shaping and curing said rubber compositions, wherein the bladder is a crosslinked rubber bladder formulation which includes:

one or more rubbery polymers, wherein at least 50 weight percent of said rubbery polymers of said bladder are at least one isobutylene rubbery polymer having at least 80 weight percent repeating units from isobutylene;

the improvement wherein the bladder formulation comprises about 2 to about 15 parts by weight of mono or poly(alkyl)phenoxypoly(alkyleneoxy)alkanol, wherein said alkyl has from 6 to 12 carbon atoms and said alkylene has from 2 to 3 carbon atoms.