Fully martensitic steel alloy

• US 6,030,469 A
• Filed: 03/20/1998
• Issued: 02/29/2000
• Est. Priority Date: 03/21/1997
• Status: Expired due to Term

• Current Assignee: General Electric Technology GmbH (GE Aerospace)
• Original Assignee: ABB Research Ltd. (ABB Ltd.)
• Inventors: Gocmen, Alkan, Uggowitzer, Peter, Ernst, Peter, Speidel, Markus
• Primary Examiner(s): Yee, Deborah
• Application Number:
  US09/044,784
• Time in Patent Office: 711 Days
• Field of Search: 148/325, 148/333, 148/663, 148/654, 420/36-38, 420/70, 420/109, 420/107
• US Class Current: 148/325
• CPC Class Codes: C21D 1/18 Hardening C21D1/02 takes precedence; Quenching with or without subsequent tempering quenching devices C21D1/62
• CPC Class Codes: C21D 6/002 containing Cr C21D6/004 takes precedence
• CPC Class Codes: C22C 33/0285 with Cr, Co, or Ni having a minimum content higher than 5%
• CPC Class Codes: C22C 38/001 containing N
• CPC Class Codes: C22C 38/30 with cobalt

Abstract

A fully martensitic quenching and tempering steel (AP) essentially consists of (measured in % by weight): 8 to 15% of Cr, up to 15% of Co, up to 4% of Mn, up to 4% of Ni, up to 8% of Mo, up to 6% of W, 0.5 to 1.5% of V, up to 0.15% of Nb, up to 0.04% of Ti, up to 0.4% of Ta, up to 0.02% of Zr, up to 0.02% of Hf, at most 50 ppm of B, up to 0.1% of C and 0.12-0.25% of N, the content of Mn+Ni being less than 4% and the content of Mo+W being less than 8%, the remainder being iron and usual impurities resulting from smelting.

Claims

1. A fully martensitic quenching and tempering steel, essentially consisting of (measured in % by weight):

8 to 15% of Cr, 5 to 15% of Co, up to 4% of Mn, up to 4% of Ni, up to 8% of Mo, up to 6% of W, 0.5 to 1.5% of V, up to 0.15% of Nb, up to 0.04% of Ti, up to 0.4% of Ta, up to 0.02% of Zr, up to 0.02% of Hf, at most 50 ppm of B, up to 0.1% of C and 0.12-0.25% of N, the content of Mn+Ni being less than 4% and the content of Mo+W being less than 8%, the remainder being iron and usual impurities resulting from smelting.

2. A fully martensitic quenching and tempering steel as claimed in claim 1, wherein 0.5 to 1% of V and 0.12-0.2% of N, not more than 0.1% of Nb and/or 0.001 to 0.04% of Ti, and/or 0.001 to 0.4% of Ta, and/or 0.001 to 0.02% of Zr, and/or 0.001 to 0.02% of Hf are present.

3. A fully martensitic quenching and tempering steel as claimed in claim 1, wherein 0.5 to 0.8% of V and 0.12-0.18% of N are present, the niobium content is between 0.02 and 0.1%, and 0.001 to 0.04% of Ti, and/or 0.001 to 0.4% of Ta, and/or 0.001 to 0.02% of Zr, and/or 0.001 to 0.02% of Hf are present.

4. A fully martensitic quenching and tempering steel as claimed in claim 1 wherein 7 to 15% of Co is present.

5. A fully martensitic quenching and tempering steel as claimed in claim 2, wherein 10-14% of Cr, not more than 2.5% of Mn and not more than 2.5% of Ni are present, the sum of Ni+Mn not exceeding 2.5%, not more than 5% of Mo and not more than 4% of W being present and the sum of Mo+W being between 3 and 6%.

6. A fully martensitic quenching and tempering steel as claimed in claim 3, wherein 11-13% of Cr, not more than 1.5% of Mn and not more than 1.5% of Ni are present, the sum Ni+Mn not exceeding 2% and the sum of Mo+W being between 3 and 5%.

7. A fully martensitic quenching and tempering steel as claimed in claim 1, wherein 5 to 10% of Co is present.

8. A fully martensitic quenching and tempering steel as claimed in claim 2, wherein 10-14% of Cr and 5 to 8% of Co, not more than 2% of Mn and not more than 2% of Ni are present, the sum Ni+Mn being not more than 2.5%, not more than 3% of Mo and not more than 3% of W being present and the sum of Mo+W being not more than 3%.

9. A fully martensitic quenching and tempering steel as claimed in claim 3, wherein 11-13% of Cr, not more than 1.5% of Mn and not more than 1.5% of Ni are present, the sum Ni+Mn being not more than 2%.

10. A fully martensitic quenching and tempering steel as claimed in claim 1, wherein 6 to 15% of Co is present.

11. A fully martensitic quenching and tempering steel as claimed in claim 2, wherein 10-14% Cr and 5 to 10% of Co, not more than 2.5% of Mn and not more than 2.5% of Ni are present, the sum Ni+Mn being not more than 3%, not more than 4% of Mo and not more than 4% of W being present and the sum of Mo+W being not more than 4%.

12. A fully martensitic quenching and tempering steel as claimed in claim 3, wherein 11-13% of Cr and 5 to 7% of Co, not more than 3% of Mo and not more than 3% of W are present and the sum of Mo+W is not more than 3%.

13. A load bearing article made of the steel alloy as claimed in claim 1, the steel alloy having a fully martensitic quenched and tempered microstructure.

14. A heat treatment process for the steel alloy as claimed in claim 1, which comprises solution-annealing the alloy at temperatures between 1150°

C. and 1250°

C. with holding times of between 0.5 and 15 hours, cooling the alloy to room temperature and then tempering it for 0.5 to 25 hours at temperatures between 600°

C. and 820°

C.

15. The heat treatment process as claimed in claim 14, wherein the alloy, after the solution-annealing, is cooled below a temperature of 900°

C. at cooling rates of less than 120°

C./hour.

16. The heat treatment process as claimed in claim 14, wherein the alloy, directly after the solution-annealing treatment, is subjected at a temperature below 900°

C. for between 5 and 500 hours to one or more isothermal annealing steps at one temperature or at different temperatures.

17. The heat treatment process as claimed in claim 14, wherein the heat treatment after the solution annealing is combined with a forming step.

18. A fully martensitic quenching and tempering steel as claimed in claim 1, wherein 0.6 to 1.5% of V is present.

19. A fully martensitic quenching and tempering steel as claimed in claim 1, wherein the steel contains nitride particles having sizes of 3 to 50 nm and spacing therebetween of 5 to 100 nm.

20. A fully martensitic quenching and tempering steel as claimed in claim 1, wherein the steel has a grain size of less than 50 μ

m.