Anti-corrosive pigment and compositions formulated with such pigments

• US 6,083,308 A
• Filed: 02/24/1998
• Issued: 07/04/2000
• Est. Priority Date: 08/25/1995
• Status: Expired due to Term

• Current Assignee: Grace GmbH & Co. KG
• Original Assignee: Grace GmbH & Co. KG
• Inventors: Fletcher, Tim
• Primary Examiner(s): GREEN, ANTHONY J
• Application Number:
  US09/029,478
• Time in Patent Office: 861 Days
• Field of Search: 106/14.12, 106/14.13, 106/14.14, 106/14.41, 106/14.44, 106/419, 106/447, 106/450, 106/460, 106/462, 106/480, 106/493, 106/494, 106/499, 106/505, 106/404
• US Class Current: 106/14.12
• CPC Class Codes: C01P 2004/80 Particles consisting of a mixture of two or more inorganic phases
• CPC Class Codes: C08L 43/02 Homopolymers or copolymers of monomers containing phosphorus
• CPC Class Codes: C09B 57/10 Metal complexes of organic compounds not being dyes in uncomplexed form
• CPC Class Codes: C09C 1/0081 Composite particulate pigments or fillers, i.e. containing at least two solid phases, except those consisting of coated particles of one compound C09C1/0015, C09C1/0078 take precedence
• CPC Class Codes: C09D 143/02 Homopolymers or copolymers of monomers containing phosphorus
• CPC Class Codes: C09D 5/086 Organic or non-macromolecular compounds
• CPC Class Codes: C09J 11/06 organic

Abstract

Effective anti-corrosive pigments are obtained using basic or neutral to basic polyvalent metal organophosphonates. The anti-corrosive organophosphonate pigments may optionally contain a co-acidic substance such as silica. The organophosphonate pigments provide ant-corrosive protection comparable to traditional pigments while enabling the avoidance of heavy metals.

Claims

1. An anti-corrosive pigment comprising a polyvalent metal organophosphonate wherein the organophosphonate corresponds to phosphono carboxylic acid containing one or more acid groups and the ratio of polyvalent metal in said organophosphonate to acid group or groups in the corresponding phosphono carboxylic acid is greater than one on an equivalents basis.

2. An anti-corrosive pigment according to claim 1 wherein the phosphono carboxylic acid contains one acid group.

3. The anti-corrosive pigment according to claim 1 wherein said polyvalent metal is selected from the group consisting of magnesium, calcium, strontium, barium, zinc, cobalt, nickel, iron, titanium, zirconium, aluminum and mixtures thereof.

4. The anti-corrosive pigment according to claim 1 wherein said polyvalent metal comprises a combination of at least two metals selected from the group consisting of zinc, calcium, magnesium and aluminum.

5. The anti-corrosive pigment according to claim 1 wherein said pigment is free of transition metal.

6. The anti-corrosive pigment according to claim 1 wherein said pigment is free of zinc.

7. The anti-corrosive pigment according to claim 1 wherein said ratio of polyvalent metal in said organophosphonate to acid group or groups in the corresponding phosphono carboxylic acid is 1.25:

1-5;

1 on an equivalents basis.

8. The anti-corrosive pigment according to claim 3 wherein the organophosphonate corresponds to hydroxyphosphonoacetic acid.

9. An anti-corrosive pigment according to claim 1 further comprising a member of a group consisting of an essentially water insoluble co-acid, a polyvalent metal salt of an essentially water insoluble co-acid and mixtures of said co-acid and polyvalent metal salt of said co-acid.

10. The anti-corrosive pigment according to claim 9 wherein said polyvalent metal is selected from the group consisting of magnesium, calcium, strontium, barium, zinc, cobalt, nickel, iron, titanium, zirconium, aluminum and mixtures thereof.

11. The anti-corrosive pigment according to claim 9 wherein said polyvalent metal comprises a combination of at least two metals selected from the group consisting of zinc, calcium, magnesium and aluminum.

12. The anti-corrosive pigment according to claim 9 wherein said pigment is free of transition metals.

13. The anti-corrosive pigment according to claim 9 wherein said pigment is free of zinc.

14. The anti-corrosive pigment according to claim 9 wherein said ratio of polyvalent metal in said organophosphonate to acid groups on the corresponding phosphono carboxylic acid is 1.25:

1-5;

1 on an equivalents basis.

15. The anti-corrosive pigment according to claim 9 wherein said co-acid comprises silica and/or silica alumina.

16. The anti-corrosive pigment according to claim 9 wherein at least a portion of said polyvalent organophosphonate corresponds to phosphono carboxylic acid selected from the group consisting of hydroxyphosphonoacetic acid, 2-phosphonobutanetricarboxylic acid, phosphonated oligomers of maleic acid or acrylic acid, phosphonated maleic acid/acrylic acid co-oligomers and mixtures thereof.

17. The anti-corrosive pigment according to claim 15 wherein said pigment contains 5 to 95 wt. % of said co-acid.

18. An anti-corrosive primer or coating composition comprising a polyvalent metal organophosphioniate wherein the organophosphonate corresponds to phosphono carboxylic acid containing one or more acid groups and the ratio of polyvalent metal in said organophosphonate to acid group or groups in the corresponding phosphono carboxylic acid is greater than one on an equivalents basis.

19. The primer or coating of claim 18 wherein said polyvalent metal is selected from the group consisting of magnesium, calcium, strontium, barium, zinc, cobalt, nickel, iron, titanium, zirconium, aluminum and mixtures thereof.

20. The primer or coating of claim 18 wherein the organophosphonate corresponds to hydroxyphosphonoacetic acid.

21. An anti-corrosive primer or coating composition comprising, (a) polyvalent metal organophosphonate wherein the organophosphonate corresponds to phosphono carboxylic acid containing one or more acid groups and the ratio of polyvalent metal in said organophosphonate to acid groups in the corresponding phosphono carboxylic acid is greater than or equal to one on an equivalents basis, and (b) a member of a group consisting of an essentially water insoluble co-acid, a polyvalent metal salt of an essentially water insoluble co-acid or mixtures of said co-acid and polyvalent metal salt of said co-acid.

22. A primer or coating composition of claim 21 wherein the co-acid comprises silica and/or silica/alumina.

23. A primer or coating composition of claim 22 wherein at least a portion of said polyvalent organophosphonate corresponds to organophosphonic acid selected from the group consisting of hydroxyphosphonoacetic acid, 2-phosphonobutanetricarboxylici acid, aminotrimethylenephosphonic acid, hydroxyethanediphosphonic acid, phosphonated oligomers of maleic acid or acrylic acid, phosphonated maleic acid/acrylic acid co-oligomers and mixtures thereof.

24. A process for preparing anti-corrosive pigments comprising (a) mixing an organophosphonic component selected from the group consisting phosphono carboxylic acid, phosphono carboxylic acid salt,and mixtures thereof, with water and at least one polyvalent metal compound to form a reaction mixture and (b) reacting said organophosphonic component and said polyvalent metal compound to form polyvalent metal organophosphonate.

25. The process according to claim 24 wherein solid co-acid is combined with the polyvalent compound prior to mixing with organophosphonic component.

26. A process according to claim 24 wherein water-insoluble co-acid is added to the reaction mixture.

27. The process according to claim 24 wherein all excess of sparingly soluble polyvalent metal oxide or hydroxide is added to the reaction mixture in addition to said polyvalent metal compound whereby an organophosphonate having a ratio polyvalent metal to acid groups in the corresponding phosphono carboxylic acid of 1.25:

1-5;

1 on an equivalent basis is formed.

28. The process according to claim 24 wherein the reaction mixture in step (a) is adjusted to a pH in the range of about 4 to about 9 by addition of a base to said reaction mixture.

29. The process according to claim 24 wherein the reaction mixture is heated to between 40°

C. and 95°

C. during step (b).

30. The process according to claim 24 wherein a slurry containing said polyvalent metal organophosphonate is formed in step (b) which slurry is subsequently treated to recover pigment particles containing said polyvalent metal organophosphonate.

31. The process according to claim 30 wherein said subsequent treatment comprises wet-milling, spray drying and/or dry milling.