Aqueous paint compositions comprising polyether amides

• US 6,114,430 A
• Filed: 08/25/1999
• Issued: 09/05/2000
• Est. Priority Date: 08/25/1999
• Status: Expired due to Fees

• Current Assignee: H.B. Fuller Licensing & Financing, Inc.
• Original Assignee: H.B. Fuller Licensing & Financing, Inc.
• Inventors: Dochniak, Michael J., Wiitala, Keith W., Paulson, Virginia A.
• Primary Examiner(s): WOODWARD, ANA LUCRECIA
• Application Number:
  US09/382,813
• Time in Patent Office: 377 Days
• Field of Search: 524/514, 524/413, 524/451, 524/449, 524/432, 524/444, 524/492, 524/493, 427/136, 427/372.2, 427/427, 427/428
• US Class Current: 524/432
• CPC Class Codes: C08L 77/06 Polyamides derived from polyamines and polycarboxylic acids C08L77/10 takes precedence
• CPC Class Codes: C09D 177/06 Polyamides derived from polyamines and polycarboxylic acids C09D177/10 takes precedence

Abstract

The present invention discloses aqueous paint compositions having enhanced adhesion characteristics. The compositions contain at least one water-soluble and/or water-dispersible polyether amide comprising the reaction product of polyoxyalkylene diamines and polycarboxylic acids. The dried compositions have improved adhesion characteristics making them particularly useful protective and/or decorative coatings on substrates including wood, metal, concrete, and plastic.

Claims

1. An aqueous paint composition, useful as a protective coating and decorative coating, comprising:

a) at least one aqueous polymer dispersion comprising the reaction product of at least one ethylenically-unsaturated monomer;

b) at least one inorganic pigment;

c) at least one polyether amide comprising the condensation product of;

i) at least one polycarboxylic acid; and

ii) at least one polyoxyalkylene amine; and

d) optionally at least one water dispersible crosslinking agent selected from the group consisting of polyisocyanates, polyaziridines, melamine-formaldehyde resins, polyepoxies and polycarbodiimides.

2. The composition as described in claim 1, wherein said dispersion is formed from at least one ethylenically unsaturated monomer selected from the group consisting of acrylic, vinyl, allylic and acrylamide.

3. The composition as described in claim 1, wherein said dispersion further comprises at least one polyether amide comprising the condensation product of:

a) at least one polycarboxylic acid; and

b) at least one polyoxyalkylene amine.

4. The composition as described in claim 1, wherein said pigment is selected from the group consisting of titanium dioxide, talc, mica, silicates, zinc oxide clay, iron oxide, and mixtures thereof.

5. The composition as described in claim 1, wherein said polycarboxylic acid is adipic acid.

6. The composition as described in claim 1, wherein said amine is 4,7,10, trioxatridecane-1,13-diamine.

7. The composition as described in claim 1, wherein said amide is present in a range of from about 1.0% by weight to about 10.0% by weight, based on total solids.

8. The composition as described in claim 1, wherein said amide is amine-terminated.

9. The composition as described in claim 1, wherein said amide is acid-terminated.

10. The composition as described in claim 1, further comprising at least one water dispersible crosslinking agent selected from the group consisting of polyisocyanates, polyaziridines, melamine-formaldehyde resins, polyepoxies and polycarbodiimides.

11. A method for the preparation of aqueous paint compositions, useful as a protective coating and decorative coating, comprising the steps of:

a) providing at least one aqueous-suspension comprising;

i) at least one aqueous polymer dispersion comprising the reaction product of at least one ethylenically-unsaturated monomer;

ii) at least one inorganic pigment; and

b) providing at least one polyether amide comprising the condensation product of;

i) at least one polyoxyalkylene diamine; and

ii) at least one polycarboxylic acid;

then combining a) and b) to form said composition.

12. The method as described in claim 11, wherein said dispersion is a polyacrylic dispersion.

13. The composition as described in claim 11, wherein said dispersion comprises the reaction product of:

a) at least one ethylenically unsaturated monomer; and

b) at least one polyether amide comprising the condensation product of;

i) at least one polycarboxylic acid; and

ii) at least one polyoxyalkylene amine;

wherein said amide is used as a protective colloid.

14. The method as described in claim 11, wherein said pigment is selected from the group consisting of titanium dioxide, talc, mica, silicates, zinc oxide clay, iron oxide, and mixtures thereof.

15. The method as described in claim 11, wherein said diamine is 4,7,10, trioxatridecane 1,13-diamine.

16. The method as described in claim 11, wherein said acid is adipic acid.

17. The method as described in claim 11, wherein said amide is present in a range of from about 1.0% by weight to about 10% by weight, based on total solids.

18. The method as described in claim 11, wherein said composition has a viscosity of about 100 krebs.

19. A method for the preparation of a coated substrate, the method comprising the steps of:

a) applying an aqueous paint composition on a substrate to form a wet-coated substrate, said composition comprising;

i) at least one aqueous polymer dispersion comprising the reaction product of at least one ethylenically-unsaturated monomer;

ii) at least one inorganic pigment; and

iii) at least one polyether amide comprising the condensation product of;

1) at least one polycarboxylic acid; and

2) at least one polyoxyalkylene diamine;

then

2) at least one polyoxyalkylene diamine;

then

b) drying the wet-coated substrate.

20. The composition as described in claim 19, wherein the substrate is selected from the group consisting of asphalt, concrete, glass, wood, leather, metal, ceramics, cloth, natural rubber, and plastic.