Substrate for photosensitive member, photosensitive member, production method thereof and image forming apparatus using the photosensitive member

• US 6,120,955 A
• Filed: 06/26/1998
• Issued: 09/19/2000
• Est. Priority Date: 06/27/1997
• Status: Expired due to Term

• Current Assignee: Minolta Co., Ltd. (Konica Minolta Inc.)
• Original Assignee: Minolta Co., Ltd. (Konica Minolta Inc.)
• Inventors: Yamaguchi, Teiko, Tokutake, Shigeaki, Inagaki, Keiichi, Sakamoto, Mitsutoshi
• Primary Examiner(s): Dote, Janis L.
• Application Number:
  US09/105,214
• Time in Patent Office: 816 Days
• Field of Search: 430/64, 430/65, 430/56, 430/60, 430/69, 430/131, 430/127, 430/57.1, 430/67, 205/203, 205/204, 148/275, 148/276, 148/283, 428/472.2, 399/159, 399/116
• US Class Current: 430/65
• CPC Class Codes: G03G 5/102 consisting of or comprising metals
• CPC Class Codes: G03G 5/104 comprising inorganic material other than metals, e.g. salts, oxides, carbon

Abstract

An electrophotographic photosensitive member is provided which does not involve any image noise occurrence, such as black spot or white spot under any environment. The electrophotographic photosensitive member comprises a photoreceptor substrate including an anodized layer formed on the surface of an aluminum or aluminum alloy base, the anodized layer having been sealed by a low temperature sealing treatment and a high temperature sealing treatment, and at least one photosensitive layer formed on the photoreceptor substrate.

Claims

1. A photosensitive member comprising:

a substrate in which an anodized layer is formed on the surface of the substrate formed of aluminum or aluminum alloy, the anodized layer being sealed by a low temperature sealing treatment and a high temperature sealing treatment; and

a photosensitive layer;

wherein the low temperature sealing treatment is carried out by immersing the anodized layer in a treating liquid having a temperature of not higher than 40°

C. and containing a low-temperature sealing agent and the high temperature sealing treatment is carried out by immersing the anodized layer in a treating liquid having a temperature of not lower than 65°

C. and containing a high-temperature sealing agent, the low-temperature sealing agent being nickel fluoride or red prussiate, and the high-temperature sealing agent being nickel acetate.

2. A photosensitive member as defined in claim 1, wherein the anodized layer has a thickness of 1 to 15 μ

m.

3. A photosensitive member as defined in claim 1, wherein the treating liquid containing the nickel fluoride has the temperature of 20 to 40°

C.

4. A photosensitive member as defined in claim 1, wherein the treating liquid containing the nickel acetate has the temperature of 65 to 100°

C.

5. A photosensitive member as defined in claim 1, wherein the photosensitive layer is a monolayer containing a charge transporting material and a charge generating material.

6. A photosensitive member as defined in claim 1, wherein the photosensitive layer includes a charge generating layer and a charge transporting layer.

7. A photosensitive member as defined in claim 1, further comprising a surface protective layer containing a resin material and an inorganic filler, said resin material selected from group consisting of an acrylic resin, a polyarylate resin, a polycarbonate resin and an urethane resin.

8. A photosensitive member as defined in claim 1, further comprising a surface protective layer containing a resin material and organic fine particles having a mean particle size of 0.05 to 2 μ

m, said resin material selected from the group consisting of an acrylic resin, a polyarylate resin, a polycarbonate resin and an urethane resin.

9. A photosensitive member as defined in claim 1, wherein the treating liquid containing the red prussiate has the temperature of 25 to 40°

C.

10. A photosensitive member comprising:

a substrate in which an anodized layer is formed on the surface of the substrate formed of aluminum or aluminum alloy, the anodized layer being sealed by a low temperature sealing treatment and a high temperature sealing treatment; and

a photosensitive layer;

wherein the low temperature sealing treatment is carried out by immersing the anodized layer in a treating liquid having a temperature of not higher than 40°

C. and containing a low-temperature sealing agent and the high temperature sealing treatment is carried out by immersing the anodized layer in a treating liquid having a temperature of not lower than 65°

C. and containing a high-temperature sealing agent, the low-temperature sealing agent being nickel fluoride or red prussiate, and the high-temperature sealing agent being metal acetate.

11. A photosensitive member as defined in claim 10, wherein the metal acetate is selected from the group consisting of nickel acetate, cobalt acetate, lead acetate, nickel-cobalt acetate and barium acetate.

12. A photosensitive member as defined in claim 10, wherein the treating liquid containing the nickel fluoride has the temperature of 20 to 40°

C.

13. A photosensitive member as defined in claim 12, wherein the treating liquid has a pH of 5.0 to 6.0.

14. A photosensitive member as defined in claim 10, wherein the treating liquid containing the red prussiate has the temperature of 25 to 40°

C.

15. A photosensitive member as defined in claim 14, wherein the treating liquid has a pH of 5.5 to 6.0.

16. A photosensitive member as defined in claim 10, wherein the treating liquid containing the metal acetate has the temperature of 65 to 100°

C.

17. A photosensitive member as defined in claim 16, wherein the treating liquid has a pH of 5.5 to 6.0.

18. An image forming apparatus comprising:

a photosensitive member comprising a substrate including an anodized layer formed on the surface of the substrate formed of aluminum or aluminum alloy, the anodized layer being sealed by a low temperature sealing treatment and a high temperature sealing treatment, and a photosensitive layer;

wherein the low temperature sealing treatment is carried out by immersing the anodized layer in a treating liquid having a temperature of not higher than 40°

C. and containing a low-temperature sealing agent and the high temperature sealing treatment is carried out by immersing the anodized layer in a treating liquid having a temperature of not lower than 65°

C. and containing a high-temperature sealing agent, the low-temperature sealing agent being nickel fluoride or red prussiate, and the high-temperature sealing agent being nickel acetate;

a contact charging device operative to contact the surface of the photosensitive member to charge the photosensitive member;

a developing device for developing with toner an electrostatic latent image supported on the surface of the photosensitive member; and

a transfer device for transferring to a transfer medium a toner image supported on the surface of the photosensitive member.

19. A substrate for photosensitive member, comprising:

an anodized layer is formed on the surface of the substrate formed of aluminum or aluminum alloy, the anodized layer being sealed by a low temperature sealing treatment and a high temperature sealing treatment;

wherein the low temperature sealing treatment is carried out by immersing the anodized layer in a treating liquid having a temperature of not higher than 40°

C. and containing a low-temperature sealing agent and the high temperature sealing treatment is carried out by immersing the anodized layer in a treating liquid having a temperature of not lower than 65°

C. and containing a high-temperature sealing agent, the low-temperature sealing agent being nickel fluoride or red prussiate, and the high-temperature sealing agent being nickel acetate.

20. A substrate for photosensitive member as defined in claim 19, wherein the treating liquid containing the nickel fluoride has the temperature of 20 to 40°

C.

21. A substrate for photosensitive member as defined in claim 19, wherein the treating liquid containing the nickel acetate has the temperature of 65 to 100°

C.

22. A substrate for photosensitive member as defined in claim 19, wherein the treating liquid containing the red prussiate has the temperature of 25 to 40°

C.

23. A substrate for photosensitive member comprising:

a base member formed of aluminum or aluminum alloy; and

an anodized layer formed on the surface of the base member and sealed by a low temperature sealing treatment and a high temperature sealing treatment;

wherein the low temperature sealing treatment is carried out by immersing the anodized layer in a treating liquid having a temperature of not higher than 40°

C. and containing a low-temperature sealing agent and the high temperature sealing treatment is carried out by immersing the anodized layer in a treating liquid having a temperature of not lower than 65°

C. and containing a high-temperature sealing agent, the low-temperature sealing agent being nickel fluoride or red prussiate, and the high-temperature sealing agent being metal acetate.

24. A substrate for photosensitive member as defined in claim 23, wherein the metal acetate is selected from the group consisting of nickel acetate, cobalt acetate, lead acetate, nickel-cobalt acetate and barium acetate.

25. A substrate for photosensitive member as defined in claim 23, wherein the treating liquid containing the nickel fluoride has the temperature of 20 to 40°

C.

26. A substrate for photosensitive member as defined in claim 23, wherein the treating liquid containing the red prussiate has the temperature of 25 to 40°

C.

27. A substrate for photosensitive member as defined in claim 23, wherein the treating liquid containing the metal acetate has the temperature of 65 to 100°

C.