Bonding method of dual phase stainless steel

• US 6,156,134 A
• Filed: 08/27/1998
• Issued: 12/05/2000
• Est. Priority Date: 08/29/1997
• Status: Expired due to Term

• Current Assignee: Daido Tokushuko Kabushiki Kaisha
• Original Assignee: Daido Tokushuko Kabushiki Kaisha
• Inventors: Horio, Hirotsugu, Shimizu, Takao, Tsuchiya, Masaki, Yamamoto, Noboru, Suzuki, Hiroaki, Inagaki, Shigeyuki
• Primary Examiner(s): Wyszomierski, George
• Application Number:
  US09/140,887
• Time in Patent Office: 831 Days
• Field of Search: 148/526, 148/528, 148/529, 148/530, 228/231, 228/233.2, 228/246, 228/262.42, 219/615
• US Class Current: 148/526
• CPC Class Codes: B23K 20/023 Thermo-compression bonding
• CPC Class Codes: B23K 20/16 with interposition of special material to facilitate connection of the parts, e.g. material for absorbing or producing gas
• CPC Class Codes: B23K 2103/05 Stainless steel
• CPC Class Codes: F28F 21/083 from stainless steel

Abstract

In a method of bonding ferric and austenitic dual stainless steels, an insert material made of a Ni base alloy having a melting point below 1290° C. is put between the bonding cross section faces of mother material steels comprising a dual phase stainless steel. A pressure force in the range of 3 MPa to 5 MPa is applied to a bonding area. The bonding area is heated at a temperature in the range of 1290° C. to a melting point of the mother material steel. The temperature is kept for in the range of 30 second to 180 second.

Claims

1. A method of bonding ferritic and austenitic dual stainless steels, comprising the steps of:

putting an insert material comprising a Ni base alloy having a melting point below 1290°

C. between the bonding cross section faces of two dual phase ferritic-austenitic stainless steels

applying pressure force in the range of 3 MPa to 5 MPa to a bonding area; and

heating the bonding area at a temperature in the range of 1290°

C. to a melting point of the dual phase ferritic and austenitic stainless steel in which the temperature is kept in said range for a time of 30 seconds to 180 seconds.

2. The bonding method according to claim 1, wherein the Ni base alloy has a shape of thin foil, fish scale or powder, and the insert material is applied between the bonding cross section faces of said steels to a thickness of 20 μ

m to 100 μ

m.

3. The bonding method according to claim 1, wherein the Ni base alloy has a composition of 3 wt %≦

Si≦

6 wt %, 5 wt %≦

Cr≦

10 wt %, 2 wt %≦

Fe≦

6 wt %, 2 wt %≦

B≦

4 wt %, the balance being nickel.

4. The bonding method according to claim 1, wherein a surface roughness of the bonding cross section face of the steel is Rmax≦

50 μ

m.

5. The bonding method according to claim 1, wherein the bonding of the steels is performed in an atmosphere of inert gas.

6. The bonding method according to claim 1, wherein the bonding of the steels is performed by a high frequency induction heating wherein said frequency is equal to or less than 100 kHz.

7. The bonding method according to claim 1, further comprising the step of rapidly cooling a heat zone which is heated above 300°

C. during boding immediately after the heating step.

8. The bonding method according to claim 7, wherein the rapid cooling speed is equal to or faster than 5°

C./sec.

9. The bonding method according to claim 8, the rapid cooling speed is in the range of 10 to 30°

C./sec.

10. The bonding method according to claim 1, further comprising the steps of:

after once cooling down the bonding area, reheating the bonding area above the solution temperature; and

then rapidly cooling down the bonding area.

11. The bonding method according to claim 10, wherein the rapid cooling speed is equal to or faster than 5°

C./sec.

12. The bonding method according to claim 11, the rapid cooling speed is in the range of 10 to 30°

C./sec.