Acrylate composite barrier coating

• US 6,231,939 B1
• Filed: 08/30/1996
• Issued: 05/15/2001
• Est. Priority Date: 10/04/1993
• Status: Expired due to Term

• Current Assignee: Presstek Incorporated (MAI Holdings, Inc.)
• Original Assignee: Presstek Incorporated (MAI Holdings, Inc.)
• Inventors: Langlois, Marc, Shaw, David G., Dawson, Eric, Cline, Daniel
• Primary Examiner(s): NAKARANI, DHIRAJLAL S
• Application Number:
  US08/706,180
• Time in Patent Office: 1,719 Days
• Field of Search: 428/35.3, 428/35.8, 428/35.9, 428/213, 428/215, 428/216, 428/336, 428/451, 428/463, 428/475.8, 428/476.3, 428/483, 428/520
• US Class Current: 428/35.9
• CPC Class Codes: B05D 1/60 Deposition of organic layers from vapour phase vapour phase deposition in general C23C14/00, C23C16/00
• CPC Class Codes: B05D 3/144 of polymeric substrates
• CPC Class Codes: B65D 1/0215 multilayered B65D81/3837 takes precedence
• CPC Class Codes: H01G 2/12 Protection against corrosion H01G2/10 takes precedence
• CPC Class Codes: H01G 4/20 using combinations of dielectrics from more than one of groups H01G4/02 - H01G4/06 H01G4/12 takes precedence
• CPC Class Codes: H01G 4/206 inorganic and synthetic material
• CPC Class Codes: H01G 4/32 Wound capacitors
• CPC Class Codes: Y10T 428/1334 Nonself-supporting tubular film or bag [e.g., pouch, envelope, packet, etc.]
• CPC Class Codes: Y10T 428/1338 Elemental metal containing
• CPC Class Codes: Y10T 428/1352 Polymer or resin containing [i.e., natural or synthetic]
• CPC Class Codes: Y10T 428/1355 Elemental metal containing [e.g., substrate, foil, film, coating, etc.]
• CPC Class Codes: Y10T 428/1359 Three or more layers [continuous layer]
• CPC Class Codes: Y10T 428/2495 Thickness [relative or absolute]
• CPC Class Codes: Y10T 428/24967 Absolute thicknesses specified
• CPC Class Codes: Y10T 428/24975 No layer or component greater than 5 mils thick
• CPC Class Codes: Y10T 428/265 1 mil or less
• CPC Class Codes: Y10T 428/31667 Next to addition polymer from unsaturated monomers, or aldehyde or ketone condensation product
• CPC Class Codes: Y10T 428/31699 Ester, halide or nitrile of addition polymer
• CPC Class Codes: Y10T 428/31743 Next to addition polymer from unsaturated monomer[s]
• CPC Class Codes: Y10T 428/3175 Next to addition polymer from unsaturated monomer[s]
• CPC Class Codes: Y10T 428/31797 : Next to addition polymer from unsaturated monomers
• CPC Class Codes: Y10T 428/31928 : Ester, halide or nitrile of addition polymer
• CPC Class Codes: Y10T 428/31935 : Ester, halide or nitrile of addition polymer

Abstract

A thermoplastic container or packaging material is given low oxygen permeability by coating with a cross-linked acrylate layer and a layer of oxygen barrier material deposited over the acrylate layer. Another acrylate layer may be deposited over the oxygen barrier. The oxygen barrier is selected from the group consisting of silicon oxide, aluminum oxide and metal. The acrylate layer may be formed from a photopolymerizable polyfunctional acrylate that is sufficiently low viscosity to be sprayed on the substrate or applied by dipping. Alternatively, the acrylate layer is a polymerization product of an acrylate monomer which is evaporated in a vacuum, condensed on the substrate and polymerized by irradiation by ultraviolet or an electron beam. The surface of the thermoplastic substrate is prepared for deposition of the acrylate by either flame treating the surface of the substrate to heat it above its melting point without deforming the substrate to thereby smooth the surface, or by plasma treating the surface for enhancing adhesion of the acrylate. Chilling the substrate enhances deposition efficiency.

Claims

1. A barrier sheet comprising:

a thermoplastic substrate;

a first vapor deposited, crosslinked acrylate layer on one face of the substrate, the acrylate layer being a polymerization product of a blend of acrylate monomers comprising at least one monomer having a molecular weight in the range of from 150 to 400 and another acrylate having a molecular weight of more than 600;

a substantially continuous layer of gas barrier material vacuum deposited over the acrylate layer; and

a second vapor deposited acrylate layer over the gas barrier material which was crosslinked before the gas barrier material contacted any solid surface.

2. A barrier as recited in claim 1 wherein the substrate is selected from the group consisting of polypropylene, polyethylene, polyester and nylon.

3. A barrier as recited in claim 1 wherein the gas barrier material is selected from the group consisting of silicon oxide, aluminum oxide and metal.

4. A barrier as recited in claim 1 wherein each crosslinked acrylate layer has a thickness of more than one half micrometer.

8. A container as recited in claim 3 wherein at least one of the crosslinked acrylate layers is a polymerization product of a blend of acrylate monomers comprising at least one monomer having a molecular weight in the range of from 150 to 400 and an acrylate having a molecular weight of more than 600.

5. A container comprising:

a closable hollow container molded from a thermoplastic selected from the class consisting of polypropylene, polyethylene, polyester and nylon;

a first vapor deposited, crosslinked acrylate layer on the outside of the container, the outside surface of the container being sufficiently smooth that the acrylate layer is continuous;

a substantially continuous layer of gas barrier material vacuum deposited over the acrylate layer; and

a second vapor deposited acrylate layer over the gas barrier layer which was crosslinked before the gas barrier material contacted any solid surface.

6. A container as recited in claim 5 wherein the gas barrier material is selected from the group consisting of silicon oxide and aluminum oxide.

7. A container as recited in claim 5 wherein the second crosslinked acrylate layer is a polymerization product of acrylate monomer having a molecular weight in the range of from 150 to 600.

9. The container as recited in claim 5 wherein the gas barrier material is at least one of metal oxide, metal, and inorganic material.

10. The container of claim 5 further comprising:

a second substantially continuous layer of gas barrier material vacuum deposited over the second acrylate layer; and

a third vapor deposited acrylate layer over the second layer of gas barrier material which was crosslinked before the second layer of gas barrier material contacted any solid surface.

11. A gas barrier sheet comprising:

a thermoplastic sheet substrate;

a substantially continuous layer of gas barrier material vacuum deposited on one face of the sheet substrate; and

an evaporated acrylate layer deposited over the gas barrier layer and crosslinked before the gas barrier material contacts any solid surface.

12. A barrier sheet comprising:

a thermoplastic substrate;

a first vapor deposited, crosslinked acrylate layer on one face of the substrate;

a substantially continuous layer of gas barrier material vacuum deposited over the acrylate layer; and

a second vapor deposited acrylate layer over the gas barrier material which was crosslinked before the gas barrier material contacted any solid surface.

13. A barrier as recited in claim 12 wherein the gas barrier material is at least one of metal oxide, metal, and inorganic material.

14. The barrier sheet of claim 12 further comprising:

a second substantially continuous layer of gas barrier material vacuum deposited over the second acrylate layer; and

a third vapor deposited acrylate layer over the second layer of gas barrier material which was crosslinked before the second layer of gas barrier material contacted any solid surface.

15. A barrier sheet comprising:

a thermoplastic substrate;

a first vapor deposited, crosslinked acrylate layer on one face of the substrate;

a substantially continuous layer of gas barrier material vacuum deposited over the acrylate layer, wherein the gas barrier material layer is transparent; and

a second vapor deposited acrylate layer over the gas barrier material which was crosslinked before the gas barrier material contacted any solid surface.

16. A barrier sheet made in a continuous in-line process comprising:

a thermoplastic substrate;

a first vapor deposited, crosslinked acrylate layer on one face of the substrate;

a substantially continuous layer of gas barrier material vacuum deposited in the in-line process over the acrylate layer; and

a second vapor deposited acrylate layer over the gas barrier material which was crosslinked before the gas barrier material contacted any solid surface.

17. A barrier as recited in claim 16 wherein the substrate is selected from the group consisting of polypropylene, polyethylene, polyester and nylon.

18. A barrier as recited in claim 16 wherein the gas barrier material is selected from the group consisting of silicon oxide, aluminum oxide and metal.

19. A barrier as recited in claim 16 wherein each crosslinked acrylate layer has a thickness of more than one half micrometer.

20. A barrier as recited in claim 16 wherein the gas barrier material is at least one of metal oxide, metal, and inorganic material.

21. The barrier sheet of claim 16 further comprising:

a second substantially continuous layer of gas barrier material vacuum deposited over the second acrylate layer; and

a third vapor deposited acrylate layer over the second layer of gas barrier material which was crosslinked before the second layer of gas barrier material contacted any solid surface.

22. A barrier sheet made in a moving web process comprising:

a thermoplastic moving web substrate;

a first vapor deposited, crosslinked acrylate layer on one face of the substrate;

a substantially continuous layer of gas barrier material vacuum deposited in the moving web process over the acrylate layer; and

a second vapor deposited acrylate layer over the gas barrier material which was crosslinked before the gas barrier material contacted any solid surface.

23. A barrier as recited in claim 22 wherein the substrate is selected from the group consisting of polypropylene, polyethylene, polyester and nylon.

24. A barrier as recited in claim 22 wherein the gas barrier material is selected from the group consisting of silicon oxide, aluminum oxide and metal.

25. A barrier as recited in claim 22 wherein each crosslinked acrylate layer has a thickness of more than one half micrometer.

26. A barrier as recited in claim 22 wherein the gas barrier material is at least one of metal oxide, metal, and inorganic material.

27. The barrier sheet of claim 22 further comprising:

a second substantially continuous layer of gas barrier material vacuum deposited over the second acrylate layer; and

a third vapor deposited acrylate layer over the second layer of gas barrier material which was crosslinked before the second layer of gas barrier material contacted any solid surface.