Method for the preparation of hollow polymer particle latex

• US 6,235,810 B1
• Filed: 11/22/1999
• Issued: 05/22/2001
• Est. Priority Date: 03/05/1997
• Status: Expired due to Fees

• Current Assignee: Neste Chemicals Oy (Fortum Oyj)
• Original Assignee: Neste Chemicals Oy (Fortum Oyj)
• Inventors: Skrifvars, Mikael, Ivanchev, Sergey, Halme, Erkki, Byrdina, Nina, Laamanen, Hanna, Pavlyuchenko, Valery, Koskinen, Jukka
• Primary Examiner(s): Wu, David W.
• Assistant Examiner(s): EGWIM, KELECHI CHIDI
• Application Number:
  US09/380,543
• Time in Patent Office: 547 Days
• Field of Search: 523/201, 524/460, 525/244, 525/267, 525/902, 526/75, 526/203
• US Class Current: 523/201
• CPC Class Codes: C08F 285/00 Macromolecular compounds obtained by polymerising monomers on to preformed graft polymers
• CPC Class Codes: Y10S 525/902 Core-shell

Abstract

A method for the preparation of latexes with hollow polymer particles useful as opacifying agents. The process comprises the preparation of hollow polymer particle latex by emulsion copolymerization with water soluble initiator and anionic surfactant as follows: a) preparation of seed latex of copolymer containing methyl methacrylate and methacrylic acid; b) preparation of latex of highly carboxylated copolymer containing methyl methacrylate and a cross-linking agent and optionally a vinyl aromatic compound; c) using highly carboxylated latex synthesized at stage b) in the preparation of the intermediate shell comprising a copolymer of methyl methacrylate, acrylic acid ester, a cross-linking agent and optionally vinyl aromatic compound, said intermediate shell copolymer having a glass transition temperature below 80° C.; d) swelling the particles prepared at stage c) by addition of volatile basic compound; e) preparation of a hard shell on the swollen expanded particles comprising a copolymer of vinyl aromatic compound, acrylonitrile and/or methyl methacrylate, and cross-linking agent, said hard shell having a glass transition temperature above 80° C.; and f) optional preparation of an external shell.

Claims

1. A process for preparation of hollow polymer particle latexes by emulsion copolymerization with water soluble initiator and anionic surfactant, characterized in the following stages:

a) preparation by emulsion polymerization of a seed latex of a copolymer containing methyl methacrylate and methacrylic acid monomer units;

b) preparation by emulsion polymerization of a latex of a highly carboxylated copolymer containing methyl methacrylate monomer units, monoethylenically unsaturated carboxylic acid monomer units and a cross-linking agent and optionally containing vinyl aromatic monomer units, in the presence of the seed latex prepared in stage(a);

c) in the presence of the preparation by emulsion polymerization of an intermediate shell comprising a copolymer of methyl methacrylate, an acrylic acid ester, a monoethylenically unsaturated carboxylic acid and a cross-linking agent, and optionally containing vinyl aromatic monomer units, wherein said intermediate shell copolymer is prepared in the presence of the highly carboxylated latex synthesized at stage (b), and has a glass transition temperature below 80°

C.;

d) swelling the particles prepared at stage (c) by the addition of a volatile basic compound;

e) preparation by emulsion polymerization of a hard shell in the presence of the swollen expanded particles prepared in stage (d), said hard shell comprising a copolymer of a vinyl aromatic compound, acrylonitrile and/or methyl methacrylate, and a cross-linking agent, said hard shell having a glass transition temperature above 80°

C.; and

f) optional preparation of an external shell.

2. Process according to claim 1, characterized in that the monoethylenically unsaturated carboxylic acid in both stages (b) and (c) is methacrylic acid.

3. Process according to claim 1, characterized in that the seed latex prepared at stage (a) has particle size of from 70 to 180 nm.

4. Process according to claim 1, characterized in that stage (b) comprises charging the water soluble initiator as two equal portions in the beginning of the reaction and in the middle of the process.

5. Process according to claim 1, characterized in that stage (c) comprises charging the anionic surfactant as equal portions in equal periods of time.

6. Process according to claim 1, characterized in that the ratio of weight concentrations of the sum of methyl methacrylate and vinyl aromatic compound to acrylic acid ester at stage (c) is within the range of 3.3-4.3.

7. Process according to claim 1, characterized in that the concentration of volatile basic compound at stage (d) is calculated in accordance with the following equation:

8. Process according to claim 1, characterized in that additionally after stage (e), stage (f) is performed, comprising preparation by emulsion polymerization of an external shell consisting of a copolymer of a vinyl aromatic compound, an acrylic acid ester, methacrylic acid and a cross-linking agent in the presence of the latex particles prepared in stage (e), said external shell having a glass transition temperature below 15°

C.

9. Process according to claim 8, characterized in that the volatile base concentration at stage (f) is equal to 20-80 meq per 1 g of methacrylic acid charged at stage (f).

10. Process according to claim 8, characterized in that the weight ratio of the copolymer prepared at stage (f) to the copolymer prepared at stage (e) is 0.1-1.0.

11. Process according to claim 1, characterized in that the temperature for the preparations is 60-95°

C.

12. Process according to claim 1, characterized in that the process is performed in one reactor without isolation of intermediate products or it is performed stagewise with the isolation of intermediate products, in more than one reactor.

13. Process according to claim 1, characterized in that stage a) comprises the preparation of a seed latex of a copolymer containing methyl methacrylate and methacrylic acid mononumeric units;

wherein the weight ratio of monomers/initiator/water during polymerization is equal to 1/(0.1-0.3)/50-150).

14. A coating formulation, characterized in that it comprises a latex prepared according to claim 1.