Method for producing a monolithic multilayer piezo actuator

• US 6,260,248 B1
• Filed: 10/19/1998
• Issued: 07/17/2001
• Est. Priority Date: 04/19/1996
• Status: Expired due to Term

• Current Assignee: Siemens AG
• Original Assignee: Siemens AG
• Inventors: Lubitz, Karl, Cramer, Dieter, Hellebrand, Hans
• Primary Examiner(s): Young, Lee
• Assistant Examiner(s): TUGBANG, ANTHONY D
• Application Number:
  US09/171,474
• Time in Patent Office: 1,002 Days
• Field of Search: 29/253.5, 29/254.1, 295/94, 298/51, 310/311, 310/323, 310/331, 310/323.06, 310/323.01, 310/323.03, 361/301.4, 361/321.1, 361/321.2, 361/321.4
• US Class Current: 29/25.35
• CPC Class Codes: H10N 30/053 by integrally sintering piezoelectric or electrostrictive bodies and electrodes
• CPC Class Codes: H10N 30/50 having a stacked or multilayer structure
• CPC Class Codes: Y10T 29/42 Piezoelectric device making
• CPC Class Codes: Y10T 29/49163 with sintering of base

Abstract

A method for manufacturing a monolithic piezoelectric actuator of multilayer design and having a high aspect ratio of more than two built up from a plurality of smaller stacks in a multilayer design, includes alternately layering green piezoceramic films and electrode material, compressing the layers while elevating the temperature to remove the binder and thereby form a composite, stacking several of the composites on one another, and sintering the stack so as to form the monolithic piezoelectric actuator which exhibits an improved mechanical strength with good piezoelectric properties.

Claims

1. A method for producing a piezoelectric actuator of monolithic multilayer design, comprising the steps of:

providing a plurality of piezoceramic green films, each green film containing a binder and having a thickness of 20 to 200 μ

m;

printing a layer of electrode material on one side of each of the green films;

layering the green films loosely on one another to form a plurality of first stacks, each first stack having a 3 mm maximum height and having an alternating layered sequence of green films and electrode material;

laminating the first stacks using uniaxial compression to form a corresponding plurality of first composites;

removing the binder from the first composites at an elevated temperature;

stacking the first composites from which the binder has been removed on one another to form a plurality of first composite stacks, each first composite stack having a height of more than 5 mm;

sintering a first composite stack under uniaxial pressure to form a piezoelectric actuator having a desired number of individual layers, said sintering step taking place while applying pressure to said first composite stack with a press die;

selectively providing piezoceramic green films of n times a desired base area as part of the step of providing a plurality of piezoceramic green films, n being a positive whole number greater than one; and

dividing up, by at least one of cutting and stamping, a first composite into said n composites of a desired base area before the step of removing the binder.

2. A method as claimed in claim 1, wherein the step of stacking takes place in said press die.

3. A method as claimed in claim 1, wherein the green films include lead zirconate titanate (PZT) and the step of sintering takes place in an oxidizing atmosphere.

4. A method as claimed in claim 1, wherein the step of sintering takes place under constant pressure of 10 to 100 kPa.

5. A method as claimed in claim 1, wherein the piezoelectric actuator is formed from one of said first composite stacks which is, in turn, formed of differing composites which include a top composite, a middle composite and a bottom composite.

6. A method as claimed in claim 1, wherein the piezoelectric actuator is formed from a composite stack which is, in turn, formed from a plurality of composites, at least one of said composites having an electrode structure which is different from an electrode structure of other ones of said composites.

7. A method as claimed in claim 1, wherein the electrode material is a paste which contains silver and palladium.