Method of producing piezoelectric/electrostrictive film-type element

• US 6,263,552 B1
• Filed: 05/08/2000
• Issued: 07/24/2001
• Est. Priority Date: 12/28/1995
• Status: Expired due to Term

• Current Assignee: NGK Insulators Limited
• Original Assignee: NGK Insulators Limited
• Inventors: Kimura, Koji, Takeuchi, Yukihisa, Nanataki, Tsutomu, Takahashi, Nobuo
• Primary Examiner(s): ROSENBAUM, IRENE CUDA
• Application Number:
  US09/567,067
• Time in Patent Office: 442 Days
• Field of Search: 29/253.5, 310/328, 310/330, 310/332, 310/357, 310/359, 310/365, 310/366
• US Class Current: 29/25.35
• CPC Class Codes: H04R 17/08 signals being recorded or played back by vibration of a stylus in two orthogonal directions simultaneously
• CPC Class Codes: H10N 30/074 by depositing piezoelectric or electrostrictive layers, e.g. aerosol or screen printing
• CPC Class Codes: H10N 30/2047 Membrane type
• CPC Class Codes: H10N 30/8548 Lead-based oxides
• CPC Class Codes: Y10T 29/42 Piezoelectric device making

Abstract

A piezoelectric and/or electrostrictive film-type element comprises a zirconia substrate with a thin-walled diaphragm section provided integrally to cover and close a window to serve as a hollow space, and a film-shaped piezoelectric and/or electrostrictive operating section composed of a lower electrode, a piezoelectric and/or electrostrictive layer, and an upper electrode which are successively provided in a layered configuration on an outer surface of the diaphragm section in accordance with a film-forming method, wherein at least a part of a peripheral edge portion of the piezoelectric and/or electrostrictive layer extends laterally beyond a corresponding peripheral edge portion of the lower electrode to construct an overhang section located opposingly over the diaphragm section, and the overhang section is in a state of incomplete connection with respect to a partial region of the diaphragm section located just under by the aid of particles of an alumina-magnesia compound such as spinel particles allowed to intervene therebetween.

Claims

1. A method for producing a piezoelectric and/or electrostrictive film-type element having at least one hollow space and comprising a zirconia substrate with a thin-walled diaphragm section provided integrally to cover and close said hollow space, and a film-shaped piezoelectric and/or electrostrictive operating section composed of a lower electrode, a piezoelectric and/or electrostrictive layer, and an upper electrode which are successively provided in a layered configuration on an outer surface of said diaphragm section in accordance with a film-forming method, said method for producing said piezoelectric and/or electrostrictive film-type element comprising the steps of:

preparing said zirconia substrate having been fired, forming a separation layer containing alumina or a component to give alumina at least around a region on which said lower electrode is formed, on said outer surface of said diaphragm section of said zirconia substrate, forming said lower electrode on said outer surface of said diaphragm section before or after said formation of said separation layer, subsequently forming said piezoelectric and/or electrostrictive layer on said lower electrode in accordance with a film-forming method by-using a piezoelectric and/or electrostrictive material containing magnesia or a component to give magnesia independently or in a form of a compound so that at least a part of a peripheral edge portion of said piezoelectric and/or electrostrictive layer extends laterally beyond a corresponding peripheral edge portion of said lower electrode to construct an overhang section located opposingly over said diaphragm section, and firing said piezoelectric and/or electrostrictive layer so that particles principally comprising a compound of alumina and magnesia are allowed to deposit at least at a boundary between said overhang section and a partial region of said diaphragm section located just thereunder, and thus an incomplete connection state is established between said overhang section and said partial region of said diaphragm section located just thereunder.

2. The method for producing said piezoelectric and/or electrostrictive film-type element according to claim 1, wherein said particles to be deposited are spinel particles.

3. The method for producing said piezoelectric and/or electrostrictive film-type element according to claim 1, wherein said piezoelectric and/or electrostrictive material contains magnesia as a component of a composition to exhibit piezoelectric and/or electrostrictive characteristics.

4. The method for producing said piezoelectric and/or electrostrictive film-type element according to claim 1, wherein said separation layer has a thickness of 0.1 to 10 μ

m.

5. A method for producing a piezoelectric and/or electrostrictive film-type element having at least one hollow space and comprising a zirconia substrate with a thin-walled diaphragm section provided integrally to cover and close said hollow space, and a film-shaped piezoelectric and/or electrostrictive operating section composed of a lower electrode, a piezoelectric and/or electrostrictive layer, and an upper electrode which are successively provided in a layered configuration on an outer surface of said diaphragm section in accordance with a film-forming method, said method for producing said piezoelectric and/or electrostrictive film-type element comprising the steps of:

preparing said zirconia substrate having been fired, forming a separation layer containing alumina or a component to give alumina and magnesia or a component to give magnesia, or containing particles principally comprising a compound of alumina and magnesia, at least around a region on which said lower electrode is formed, on said outer surface of said diaphragm section of said zirconia substrate, forming said lower electrode on said outer surface of said diaphragm section before or after said formation of said separation layer, subsequently forming said piezoelectric and/or electrostrictive layer on said lower electrode in accordance with a film-forming method so that at least a part of a peripheral edge portion of said piezoelectric and/or electrostrictive layer extends laterally beyond a corresponding peripheral edge portion of said lower electrode to construct an overhang section located opposingly over said diaphragm section, and firing said piezoelectric and/or electrostrictive layer so that particles principally comprising a compound of alumina and magnesia are allowed to deposit or intervene at least at a boundary between said overhang section and a partial region of said diaphragm section located just thereunder, and thus an incomplete connection state is established between said overhang section and said partial region of said diaphragm section located just thereunder.

6. The method for producing said piezoelectric and/or electrostrictive film-type element according to claim 5, wherein said particles to be deposited intervened are spinel particles.

7. The method for producing said piezoelectric and/or electrostrictive film-type element according to claim 5, wherein said piezoelectric and/or electrostrictive layer is formed by using a piezoelectric and/or electrostrictive material containing magnesia or a component to give magnesia independently or in a form of a compound.

8. The method for producing said piezoelectric and/or electrostrictive film-type element according to claim 7, wherein said piezoelectric and/or electrostrictive material contains magnesia as a component of a composition to exhibit piezoelectric and/or electrostrictive characteristics.

9. The method for producing said piezoelectric and/or electrostrictive film-type element according to claim 5, wherein said separation layer has a thickness of 0.1 to 10 μ

m.