Hydrophobic coating including DLC and/or FAS on substrate
First Claim
1. A coated article comprising:
- a glass substrate;
a hydrophobic coating system provided on said glass substrate, said hydrophobic coating system including at least one diamond-like carbon (DLC) inclusive layer and at least one fluoro-alkyl silane (FAS) compound inclusive layer; and
wherein said hydrophobic coating system is heat treated so as to have an initial contact angle θ
of at least about 80 degrees, and an average hardness of at least about 10 GPa.
2 Assignments
0 Petitions
Accused Products
Abstract
A substrate is coated with a hydrophobic coating system including diamond-like carbon (DLC) and at least one fluoro-alkyl silane (FAS) compound. In certain embodiments, the coating system includes an FAS inclusive layer provided over at least one DLC inclusive layer in order to increase the initial contact angle of the coated article. At least the FAS inclusive layer may be heated (i.e., thermally cured) to an extent sufficient to at least one of: (a) improve the initial contact angle θ of the resulting coated article, (b) render the hydrophobic nature of the resulting coated article more stable when exposed to solution(s)/material(s) such as hexane and/or isopropyl alcohol, and/or (c) improve bonding characteristics of the FAS inclusive layer within itself and/or between the FAS inclusive layer and a layer immediately beneath it.
-
Citations
12 Claims
-
1. A coated article comprising:
-
a glass substrate;
a hydrophobic coating system provided on said glass substrate, said hydrophobic coating system including at least one diamond-like carbon (DLC) inclusive layer and at least one fluoro-alkyl silane (FAS) compound inclusive layer; and
wherein said hydrophobic coating system is heat treated so as to have an initial contact angle θ
of at least about 80 degrees, and an average hardness of at least about 10 GPa.- View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12)
SiO2 from about 60-80%, Na2O from about 10-20%, CaO from about 0-16%, K2O from about 0-10%, MgO from about 0-10%, Al2O3 from about 0-5%; and
wherein said DLC inclusive layer includes sp3 carbon-carbon bonds.
-
-
3. The coated article of claim 1, wherein said hydrophobic coating system includes first and second DLC inclusive layers, said first DLC inclusive layer including silicon (Si) and being provided between said DLC inclusive second layer and said substrate;
- and
wherein said second DLC inclusive layer is deposited in a manner so that at least a portion of said second DLC inclusive layer has a greater hardness and higher density than said first DLC inclusive layer.
- and
-
4. The coated article of claim 3, wherein said hydrophobic coating system further includes said FAS inclusive layer provided on said second DLC inclusive layer, so that said second DLC inclusive layer is located between said first DLC inclusive layer and said FAS inclusive layer.
-
5. The coated article of claim 1, wherein said initial contact angle is at least about 100 degrees.
-
6. The coated article of claim 5, wherein said initial contact angle is at least about 110 degrees.
-
7. The coated article of claim 1, wherein said coating system has a surface energy γ
- C of less than or equal to about 20.2 mN/m.
-
8. The coated article of claim 1, wherein said FAS compound includes at least one of:
- CF3(CH2)2Si(OCH3)3;
CF3(CF2)5(CH2)2Si(OCH2CH3)3;
CF3(CH2)2SiCl3;
CF3(CF2)5(CH2)2SiCl3;
CF3(CF2)7(CH2)2Si(OCH3)3;
CF3(CF2)5(CH2)2Si(OCH3)3;
CF3(CF2)7(CH2)2SiCl3;
CF3(CF2)7(CH2)2SiCH3Cl2; and
CF3(CF2)7(CH2)2SiCH3(OCH3)2.
- CF3(CH2)2Si(OCH3)3;
-
9. The coated article of claim 1, wherein said hydrophobic coating system has an average hardness of at least about 20 GPa.
-
10. The coated article of claim 1, wherein said DLC inclusive layer includes sp3 carbon-carbon bonds.
-
11. The coated article of claim 1, wherein at least about 50% of carbon-carbon bonds in said DLC inclusive layer are sp3 carbon-carbon bonds.
-
12. The coated article of claim 1, wherein said glass substrate comprises soda-lime-silica glass.
Specification