Surgical implant system for restoration and repair of body function

• US 6,299,448 B1
• Filed: 02/17/2000
• Issued: 10/09/2001
• Est. Priority Date: 02/17/1999
• Status: Expired due to Fees

• Current Assignee: Dermagenesis, LLC
• Original Assignee: Ivanka J. Zdrahala, Richard J. Zdrahala
• Inventors: Zdrahala, Richard J., Zdrahala, Ivanka J.
• Primary Examiner(s): Manahan, Todd E.
• Application Number:
  US09/505,567
• Time in Patent Office: 600 Days
• Field of Search: 433/173, 433/215, 433/218, 433/175, 623/16.11, 623/17.18, 623/23.98, 623/23.52, 623/1.18, 623/1.19, 623/1.22
• US Class Current: 433/173
• CPC Class Codes: A61C 2201/007 using shape memory effect
• CPC Class Codes: A61C 8/0006 Periodontal tissue or bone regeneration support means for endoprosthetic bone substitute or bone graft implants A61F2/2846
• CPC Class Codes: A61C 8/0036 Tooth replica

Abstract

The present invention relates generally to surgical implants intended for the augmentation, repair, and restoration of soft tissue (e.g. gingiva or cartilage), hard tissue (e.g. bone), and the like. More particularly, the present invention relates to the in vivo anchoring of cast implants by stent-like anchors made of a shape memory alloy and/or polymers which are desirably covered with a textile sleeve of a specific porosity.

Claims

1. A method for restoration of dental tissue, and providing an implant device for attaching artificial teeth comprising the steps of:

(i) preserving and dressing the cavity created by the extraction of a tooth;

(ii) estimating or measuring the parameters of the cavity or lesion formed within the bone and gum tissues;

(iii) providing a stent assembly comprising an expandable stent made from a shape-memory material, said stent having a sleeve of porous fabric at least partially covering said stent, said stent assembly generally conforming to the parameters of said cavity or lesion;

(iv) positioning the said stent assembly within the cavity or lesion; and

(v) delivering an in situ polymerizable, exothermic polymer system to the inner space of the said assembly to provide internal structure to the assembly.

2. The method of claim 1, wherein said expandable stent is formed from a shape-memory metal alloy.

3. The method of claim 1, wherein said expandable stent is formed from nitinol.

4. The method of claim 1, wherein the expandable stent is radially expandable.

5. The method of claim 1, wherein said expandable stent is in the shape of a helical coil.

6. The method of claim 1, wherein said expandable stent is in the shape of a tube having openings in its wall.

7. The method of claim 1, wherein said expandable stent is formed from a shape-memory polymer.

8. The method of claim 7, wherein said expandable stent is formed from a biodurable polymer.

9. The method of claim 7, wherein said expandable stent is formed from a biodegradable polymer.

10. The method of claim 1, wherein said sleeve is a knitted, woven, braided or non-woven fabric.

11. The method of claim 1, wherein said sleeve has a water porosity of about 50 to about 1,000 ml/min/cm².

12. The method of claim 1, wherein said sleeve has a thickness of about 0.1 to about 1.0 mm.

13. The method of claim 1, wherein said sleeve is formed of a combination of biodurable and biodegradable fibers.

14. The method of claim 1, wherein said sleeve is expanded PTFE.

15. The method of claim 14, wherein said sleeve has a fibril length of about 30 to about 300 microns.

16. The method of claim 14, wherein said sleeve has a thickness of about 0.1 to about 1.0.

17. The method of claim 1, wherein said sleeve is coated or impregnated with a bioactive material.

18. The method of claim 17, wherein said bioactive material is released from a hydrogel matrix.

19. The method of claim 1, wherein said delivering of said in situ polymerizable exothermic polymer system is by reaction injection molding.

20. The method of claim 1, wherein said in situ polymerizable exothermic polymer system includes a polyurethane or polyurethane-containing polymer.

21. The method of claim 1, wherein the in situ polymerizable exothermic polymer system includes a polymethylmethacrylate-based bone cement.

22. The method of claim 1, wherein the in situ polymerizable exothermic polymer system provides sufficient heat during polymerization to cause expansion of said expandable stent.

23. The method of claim 1, wherein said expansion of said expandable stent is sufficient to initially anchor said stent assembly.

24. The method of claim 1, further including the step of positioning within said in situ polymerizable exothermic polymer system a post for attaching a crown.

25. The method of claim 24, further including the step of attaching a crown to the exposed surface of the stent assembly.

26. A dental implant device comprising a generally elongate expandable stent member at least partially covered by a porous sleeve formed from a porous polymeric fabric or film, said stent member being formed from a shape memory material capable of expanding in the cavity of the implant site, said sleeve being adapted to receive a polymerizable material therein for providing internal structure and support to said implant device upon in situ cure.

27. The dental implant of claim 26, wherein the stent member is in the shape of a helical coil, porous tube or mesh-walled tube.

28. The dental implant of claim 26, wherein the sleeve is a material selected from biodurable materials, biodegradable materials and combinations thereof.

29. The dental implant of claim 26, further including a post for attachment of a crown.

30. The dental implant of claim 29, further including a crown for attachment to said post and implant device.

31. A dental implant kit comprising (i) a stent member;

(ii) a sleeve member for covering said stent member and for receiving in situ polymerizable polymer and (iii) polymer components which when mixed can be delivered in vivo for in situ polymerization.

32. The dental implant kit of claim 31 further including a post and dental crown.