Acid etch resistant film-forming compositions and composite coating compositions

• US 6,306,505 B1
• Filed: 08/18/2000
• Issued: 10/23/2001
• Est. Priority Date: 07/11/1997
• Status: Expired due to Fees

• Current Assignee: PPG Industries Ohio Incorporated (Nouryon BV)
• Original Assignee: PPG Industries Ohio Incorporated (Nouryon BV)
• Inventors: Kish, Daniel D., Rush-Batista, Melissa S., Mauer, George W.
• Primary Examiner(s): Thibodeau, Paul
• Assistant Examiner(s): TARAZANO, DONALD LAWRENCE
• Application Number:
  US09/641,592
• Time in Patent Office: 431 Days
• Field of Search: 428/413, 428/418, 428/423.1, 428/423.3, 428/424.2, 428/520, 428/522, 428/450, 428/459, 525/450, 525/459
• US Class Current: 428/413
• CPC Class Codes: C08L 2666/14 Macromolecular compounds according to C08L59/00 - C08L87/00; Derivatives thereof
• CPC Class Codes: C08L 61/32 Modified amine-aldehyde condensates
• CPC Class Codes: C09D 133/066 containing -OH groups
• CPC Class Codes: Y10T 428/31511 Of epoxy ether
• CPC Class Codes: Y10T 428/31529 Next to metal
• CPC Class Codes: Y10T 428/31551 Of polyamidoester [polyurethane, polyisocyanate, polycarbamate, etc.]
• CPC Class Codes: Y10T 428/31554 Next to second layer of polyamidoester
• CPC Class Codes: Y10T 428/31573 Next to addition polymer of ethylenically unsaturated monomer
• CPC Class Codes: Y10T 428/31928 Ester, halide or nitrile of addition polymer
• CPC Class Codes: Y10T 428/31935 Ester, halide or nitrile of addition polymer

Abstract

A curable film-forming composition which is resistant to acid etching is provided. The curable film-forming composition comprises:

A) a polymer prepared from the following ingredients:

1) an ethylenically unsaturated, beta-hydroxy ester functional monomer;

2) an ethylenically unsaturated, hydroxyalkyl functional monomer;

3) a vinyl aromatic compound; and

4) an alkyl ester of acrylic or methacrylic acid having 1 to 30 carbon atoms in the alkyl group; and

B) an etherified aminoplast crosslinking agent. A multi-component composite coating composition is also provided, comprising a base coat deposited from a pigmented film-forming composition and a transparent top coat applied over the base coat in which the transparent coat, or clear coat, is deposited from the curable film-forming composition described above.

Claims

1. A curable film-forming composition which when cured yields a resultant coating resistant to acid etching, comprising:

A) a polymer having a weight average molecular weight of about 5000 to about 25,000 as determined by gel permeation chromatography using a polystyrene standard, and having a glass transition temperature of at least about 20°

C., said polymer prepared from the following ingredients;

1) about 10 to about 80 percent by weight, based on the total solid weight of monomers Used to prepare the polymer, of a reaction product of an ethylenically unsaturated acid functional monomer and an epoxy compound containing at least 5 carbon atoms which is not polymerizable with the ethylenically unsaturated acid functional monomer;

2) about 5 to about 50 percent by weight, based on the total solid weight of monomers used to prepare the polymer, of an ethylenically unsaturated, hydroxyalkyl functional monomer;

3) about 15 to about 40 percent by weight, based on the total solid weight of monomers used to prepare the polymer, of a vinyl aromatic monomer; and

4) about 10 to about 60 percent by weight, based on the total solid weight of monomers used to prepare the polymer, of an alkyl ester of acrylic or methacrylic acid containing from 1 to 30 carbon atoms in the alkyl group;

B) an etherified aminoplast crosslinking agent; and

C) an adjuvant curing agent in an amount of up to about 20 percent by weight based on the total weight of resin solids in the film-forming composition.

2. The film-forming composition of claim 1, wherein the polymer is present in the film-forming composition in an amount of about 55 to about 85 percent by weight based on the total weight of resin solids in the film-forming composition.

3. The film-forming composition of claim 1, wherein the aminoplast is present in the film-forming composition in an amount of about 15 to about 45 percent by weight based on the total weight of resin solids in the film-forming composition.

4. The film-forming composition of claim 1, wherein the ethylenically unsaturated, acid functional monomer is selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, and mixtures thereof.

5. The film-forming composition of claim 1, wherein the epoxy compound has the following structure:

wherein R is a hydrocarbon radical containing from about 4 to about 26 carbon atoms.

6. The film-forming composition of claim 1, wherein the ethylenically unsaturated, hydroxyalkyl functional monomer is selected from the group consisting of hydroxyethyl acrylate, hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, 4-hydroxybutyl methacrylate, and mixtures thereof.

7. The film-forming composition of claim 1 in which the vinyl aromatic monomer is styrene.

8. The film-forming composition of claim 1, wherein the aminoplast is etherified at least in part with isobutyl alcohol.

9. The film-forming composition of claim 1, wherein the alkyl ester of acrylic or methacrylic acid is 2-ethylhexyl methacrylate.

10. The film-forming composition of claim 9, wherein styrene is present in an amount of about 30 to about 40 percent, and the 2-ethylhexyl methacrylate is present in an amount of about 10 to about 20 percent, based on the total solid weight of monomers used to prepare the polymer.

11. The film-forming composition of claim 1, wherein the polymer contains carbamate functionality.

12. The film-forming composition of claim 1, wherein said adjuvant curing agent comprises a tricarbamoyl triazine compound having the formula C₃N₃(NHCOXR)₃, wherein X is nitrogen, oxygen, sulfur, phosphorus, or carbon, and R is a lower alkyl group having one to twelve carbon atoms or mixtures of lower alkyl groups.

13. A multi-component composite coating composition comprising a base coat deposited from a pigmented film-forming composition and a transparent top coat applied over the base coat in which the transparent top coat is deposited from a clear film-forming composition comprising:

A) a polymer having a weight average molecular weight of about 5000 to about 15,000 as determined by gel permeation chromatography using a polystyrene standard, and having a glass transition temperature of at least about 20°

C., said polymer prepared from the following ingredients;

1) about 10 to about 70 percent by weight, based on the total solid weight of monomers used to prepare the polymer, of a reaction product of an ethylenically unsaturated acid functional monomer and an epoxy compound containing at least 5 carbon atoms which is not polymerizable with the ethylenically unsaturated acid functional monomer;

2) about 5 to about 50 percent by weight, based on the total solid weight of monomers used to prepare the polymer, of an ethylenically unsaturated, hydroxyalkyl functional monomer;

3) about 15 to about 40 percent by weight, based on the total solid weight of monomers used to prepare the polymer, of a vinyl aromatic monomer; and

4) about 10 to about 60 percent by weight, based on the total solid weight of monomers used to prepare the polymer, of an alkyl ester of acrylic or methacrylic acid containing from 1 to 30 carbon atoms in the alkyl group;

B) an etherified aminoplast crosslinking agent, which is etherified with one or more alcohols selected from the group consisting of methanol, n-butyl alcohol, and isobutyl alcohol; and

C) an adjuvant curing agent in an amount up to about 20 percent by weight based on the total weight of resin solids in the clear film-forming composition.

14. The multi-component composite coating composition of claim 13, wherein the polymer is present in the clear film-forming composition in an amount of about 55 to about 85 percent by weight based on the total weight of resin solids in the clear film-forming composition.

15. The multi-component composite coating composition of claim 13, wherein the aminoplast is present in the clear film-forming composition in an amount of about 15 to about 45 percent by weight based on the weight of resin solids in the clear film-forming composition.

16. The multi-component composite coating composition of claim 13, wherein the ethylenically unsaturated, acid functional monomer is selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, an mixtures thereof.

17. The multi-component composite coating composition of claim 13, wherein the epoxy compound has the following structure:

wherein R is a hydrocarbon radical contining from about 4 to about 26 carbon atoms.

18. The multi-component composite coating composition of claim 13, wherein the ethylenically unsaturated, hydroxyalkyl functional monomer is selected from the group consisting of hydroxyethyl acrylate, hydroxyethyl methacrylate, hydroxypropyl acrylate, hydroxypropyl methacrylate, 4-hydroxybutyl acrylate, 4-hydroxybutyl methacrylate, and mixtures thereof.

19. The multi-component composite coating composition of claim 13, in which the vinyl aromatic monomer is styrene.

20. The multi-component composite coating composition of claim 13, wherein the aminoplast is etherified at least in part with isobutyl alcohol.

21. The multi-component composite coating composition of claim 13, wherein the alkyl ester of acrylic or methacrylic is 2-ethylhexyl methacrylate.

22. The multi-component composite coating composition of claim 21, wherein the styrene is present in an amount of about 30 to about 40 percent, and the 2-ethylhexyl methacrylate is present in an amount of about 10 to about 20 percent, based on the total solid weight of monomers used to prepare the polymer.

23. The multi-component composite coating composition of claim 13, wherein the polymer contains carbamate functionality.

24. The multi-component composite coating composition of claim 13, wherein said adjuvant curing agent comprises a tricarbamoyl triazine compound having the formula C₃N₃(NHCOXR)₃, wherein X is nitrogen, oxygen, sulfur, phosphorus, or carbon, and R is a lower alkyl group having one to twelve carbon atoms or mixtures of lower alkyl groups.