Communication cable having reduced jacket shrinkage

• US 6,324,324 B1
• Filed: 01/12/2000
• Issued: 11/27/2001
• Est. Priority Date: 01/12/2000
• Status: Expired due to Fees

• Current Assignee: Fitel USA Corporation
• Original Assignee: Lucent Technologies, Inc. (Nokia Corporation)
• Inventors: Weimann, Peter A., Thomas, Phillip M., Dixon, Lisa A., Small, Richard D.
• Primary Examiner(s): NGO, HUNG NHAT
• Application Number:
  US09/481,186
• Time in Patent Office: 685 Days
• Field of Search: 385/100-114
• US Class Current: 385/100
• CPC Class Codes: G02B 6/443 Protective covering

Abstract

A jacket for a communication cable is made from a resin that has high aspect ratio filler materials, and possibly coupling agents, dispersed therein. The fillers and the coupling agents reduce the post-extrusion shrinkage of the jacketing compound such that the strength members used in the communication cable need have only negligible compressive stiffness.

Claims

1. A fiber optic cable comprising:

an outer jacket for the cable, wherein the jacket comprises a resin; and

high aspect ratio fillers of an aspect ratio of at least 10;

1 occupying a predetermined volume of the jacket whereby post extrusion shrinkage of the jacket is controlled.

2. The cable of claim 1, wherein the outer jacket further comprises a coupling agent to aid adhesion between the fillers and the resin and to aid dispersion of the fillers.

3. The cable of claim 2, wherein the coupling agent is mixed with the resin.

4. The cable of claim 3, wherein the coupling agent is selected from the group consisting of:

organofunctional silanes, titanates, zirconates, epoxy coating and functionalized polyolefins.

5. The cable of claim 2, wherein the fillers are coated with the coupling agent.

6. The cable of claim 5, wherein the coupling agent is selected from the group consisting of:

organofunctional silanes, titanates, zirconates, epoxy coating and functionalized polyolefins.

7. The cable of claim 6, wherein the functionalized polyolefins are selected from the group consisting of:

halogenated paraffins, carboxyl-modified polypropylenes, and maleated polypropylene.

8. The cable of claim 1, wherein the resin is selected from the group consisting of:

polyethylenes, ethylene-vinyl acetate copolymers, impact-modified isotactic polypropylene, including copolymers of polypropylene and ethylene/propylene rubbers, and ethylene-ethyl acrylate copolymers.

9. The cable of claim 1, wherein the fillers are fibrous.

10. The cable of claim 9, wherein the fibrous fillers are selected from the group consisting of:

wollastonite, glass fiber, milled glass, chopped glass and carbon filler.

11. The cable of claim 9, wherein the aspect ratio of the fibrous fillers is at least 10:

1.

12. The cable of claim 1, wherein the fillers are platelike.

13. The cable of claim 12, wherein the platelike fillers are selected from the group consisting of:

mica, talc, glass flakes, clays and silica.

14. The cable of claim 1, wherein the fillers are organic.

15. The cable of claim 14, wherein the organic fillers are selected from the group consisting of:

cellulose, jute and pineapple fibers.

16. The cable of claim 1, wherein the fillers reduce post-extrusion shrinkage of the jacket by an order of magnitude.

17. The cable of claim 1, wherein the fillers in the jacket occupy a volume up to 25%.

18. A dielectric fiber optic cable comprising:

an outer jacket for the cable, wherein the jacket comprises

a resin selected from the group consisting of;

polyethylenes, ethylene-vinyl acetate copolymers, ethylene/propylene rubbers, ethylene-ethyl acrylate copolymers or impact-modified isotactic polypropylene, including copolymers of polypropylene and ethylene/propylene rubbers;

fibrous fillers with an aspect ratio of at least 10;

1; and

a coupling agent to aid adhesion between the fillers and the resin and to aid dispersion of the fillers.