Method for preparing electrodes for Ni/Metal hydride secondary cells using Cu

• US 6,372,383 B1
• Filed: 01/31/2000
• Issued: 04/16/2002
• Est. Priority Date: 01/31/2000
• Status: Expired due to Fees

• Current Assignee: Korea Advanced Institute of Science and Technology
• Original Assignee: Korea Advanced Institute of Science and Technology
• Inventors: Lee, Ho, Lee, Sang Min, Kim, Dong Myung, Yu, Ji Sang, Lee, Jai Young, Jang, Kuk Jin
• Primary Examiner(s): Chaney, Carol
• Assistant Examiner(s): DOVE, TRACY MAE
• Application Number:
  US09/494,596
• Time in Patent Office: 806 Days
• Field of Search: 429/218.2, 429/217, 429/245
• US Class Current: 429/218.2
• CPC Class Codes: H01M 4/383 Hydrogen absorbing alloys
• CPC Class Codes: H01M 4/621 Binders
• CPC Class Codes: H01M 4/661 Metal or alloys, e.g. alloy coatings H01M4/669 take precedence
• CPC Class Codes: H01M 4/663 containing carbon or carbonaceous materials as conductive part, e.g. graphite, carbon fibres
• CPC Class Codes: Y02E 60/10 Energy storage using batteries

Abstract

Disclosed is a method for preparing a high performance, negative electrode for Ni/metal hydride cells. A Zr-based hydrogen storage alloy, a binder comprising a mixture of polytetrafluoroethylene and 50th and a thickening agent (hydroxypropylmethyl cellulose), and a current collector comprising carbon black and copper are slurried and molded into a paste-type electrode. In a closed type cell, the copper repetitively undergoes melting and deposition on the electrode during charging and discharging cycles, allowing the electrode to show a similar change in surface morphology and electrochemical properties to that of a conventionally electroless plated electrode. Giving a contribution to the improvement in cell properties, including inner cell pressure, high rate dischargeability and energy density per volume, the method can substitute conventional alloy surface modifying methods, such as electroless plating methods and other pre-treatment processes necessary for the preparation of electrodes, which are difficult to practice owing to the production of pollution of the environment and to requirement of additional procedures.

Claims

1. A negative electrode for a Ni/metal hydride secondary cell comprising:

a hydrogen storage alloy;

a binder; and

a current collector comprising a mixture of from 10;

90 to 50;

50 wt. % carbon black;

copper.

2. A negative electrode according to claim 1, wherein the hydrogen storage alloy is a powder with a size of −

400 mesh (<

38 μ

m).

3. A negative electrode according to claim 1, wherein the binder comprises a mixture of polytetrafluoroethylene and acrylic polymer in water.

4. A negative electrode according to claim 1, wherein the binder comprises a 1:

1 to 2;

1 mixture of polytetrafluoroethylene;

acrylic polymer in water.

5. A negative electrode according to claim 1, wherein the binder is present at a concentration of about 2 to 4 wt. % of the hydrogen storage alloy.

6. A negative electrode according to claim 1, further comprising a thickener.

7. A negative electrode according to claim 6, wherein the thickener is hydroxypropyl methyl cellulose.

8. A negative electrode according to claim 6, wherein the thickener has a concentration of from 0.3 to 0.8 wt. % of the hydrogen storage alloy.

9. A negative electrode according to claim 1, wherein the current collector is present in an amount of from 1 to 2.5 wt. % based upon the amount of hydrogen storage alloy present in the electrode.

10. A negative electrode according to claim 1, wherein the hydrogen storage alloy is Zr_0.9Ti_0.1(Mn_0.7V_0.5Ni_1.2)_0.92.

11. A negative electrode for a Ni/metal hydride secondary cell comprising:

a powder hydrogen storage alloy having a size of −

400 mesh (<

38 μ

m);

a binder;

a thickener; and

a current collector comprising a mixture of carbon black and copper.

12. A negative electrode according to claim 11, wherein the binder comprises a mixture of polytetrafluoroethylene, acrylic polymer in water.

13. A negative electrode according to claim 12, wherein the binder comprises a 1:

1 to 2;

1 mixture of polytetrafluoroethylene;

acrylic polymer in water.

14. A negative electrode according to claim 12, wherein the binder is present at a concentration of about 3.6 wt. % of the hydrogen storage alloy.

15. A negative electrode according to claim 14, wherein the thickener is hydroxypropyl methyl cellulose.

16. A negative electrode according to claim 15, wherein the thickener has a concentration of about 0.3 to 0.8 wt. % of the hydrogen storage alloy.

17. A negative electrode according to claim 16, wherein the current collector is present in an amount of from 1 to 2.5 wt. % based upon the amount of hydrogen storage alloy present in the electrode.

18. A negative electrode according to claim 17, wherein the current collector comprises a mixture of from 10:

90 to 50;

50 wt. % carbon black;

copper.

19. A negative electrode according to claim 18, wherein the hydrogen storage alloy is Zr_0.9Ti_0.1(Mn_0.7V_0.5Ni_1.2)_0.92.