Ceramic member resistant to halogen-plasma corrosion

• US 6,383,964 B1
• Filed: 11/29/1999
• Issued: 05/07/2002
• Est. Priority Date: 11/27/1998
• Status: Expired due to Fees

• Current Assignee: Kyocera Corporation
• Original Assignee: Kyocera Corporation
• Inventors: Itoh, Yumiko, Nakahara, Masahiro
• Primary Examiner(s): GROUP, KARL E
• Application Number:
  US09/450,162
• Time in Patent Office: 890 Days
• Field of Search: 501/105, 501/127, 501/152
• US Class Current: 501/152
• CPC Class Codes: C04B 35/117 Composites
• CPC Class Codes: C04B 35/18 rich in aluminium oxide

Abstract

The present invention is to provide ceramic members for being used as members constituting a processing chamber for etching or cleaning semiconductor substrates or wafers by halogen plasma. A ceramic member includes at least 10% by volume of a compound of yttrium-aluminum-garnet (YAG) phase and not more than 90% by volume of at least an oxide phase selected from aluminum oxide, yttrium oxide and aluminum nitride. Particularly, the ceramic member contains yttrium within a range of 35 to 80 mole % in terms of yttrium oxide Y₂O₃ and aluminum within a range of 20 to 65 mole % in terms of aluminum oxide Al₂O₃ to form a mixture of YAG phase with yttria phase, producing ceramic material having high corrosion resistance to halogenous gas and its plasma. Such ceramic material may be well applicable to members to be exposed by the halogen plasma, for example, a chamber wall, a wafer stage, a clamp ring, a shower head, which are used in systems for etching and cleaning semiconductor wafers. A ceramic member of the invention can also be composed of YAG and alumina or aluminum nitride, showing high thermal conductivity enough to prevent a deposit of the reaction products of halide over the whole members in the chamber by external heating.

Claims

1. A ceramic member having a resistance to halogen plasma, comprising not less than 10% by volume of a phase of yttrium-aluminum-garnet and not more than 90% by volume of at least a phase of aluminum oxide, which is formed of a sintered material containing as a main component any one of a combination of both crystalline phases of yttrium oxide and yttrium-aluminum-garnet, a combination of both crystalline phases of aluminum oxide and yttrium-aluminum-garnet, wherein the sintered material contains zirconium oxide as a secondary component;

and wherein the content of zirconium oxide is within a range of 0.05 to 5.0% by weight in the sintered material.

2. The ceramic member according to claim 1, wherein the sintered material includes cerium oxide in an amount sufficient to stabilize said zirconium oxide.

3. The ceramic member according to claim 1, wherein the ceramic member shows a thermal-shock resistance temperature Δ

T of not less than 100°

C.

4. The ceramic member according to claim 1, wherein a mean grain size of yttrium-aluminum-garnet is not more than 10 μ

m.

5. The ceramic member according to claim 1, wherein a porosity of the sintered material is not more than 0.2%.

6. A ceramic member having a resistance to halogen plasma, comprising not less than 10% by volume of a phase of yttrium-aluminum-garnet and not more than 90% by volume of at least a phase of aluminum oxide, which is formed of a sintered material containing as a main component any one of a combination of both crystalline phases of yttrium oxide and yttrium-aluminum-garnet, a combination of both crystalline phases of aluminum oxide and yttrium-aluminum-garnet, wherein the sintered material contains cerium oxide as a secondary component;

and wherein the content of cerium oxide is within a range of 0.0003 to 1.0% by weight in the sintered material.