Stent manufacturing method thereof and indwelling method thereof

• US 6,416,544 B2
• Filed: 11/10/1999
• Issued: 07/09/2002
• Est. Priority Date: 11/11/1998
• Status: Expired due to Fees

• Current Assignee: Ogawa Spring Co., Ltd.
• Original Assignee: Actment Co., Ltd.
• Inventors: Ogawa, Akira, Sugita, Yoichi, Kyo, Kenji
• Primary Examiner(s): Milano, Michael J.
• Assistant Examiner(s): Bui, Vy Q.
• Application Number:
  US09/437,606
• Publication Number:
  US 20010056296A1
• Time in Patent Office: 972 Days
• Field of Search: 623/1.15, 623/900, 623/1, 623/1.11, 623/1.12, 623/1.13, 623/1.18, 623/1.19, 623/1.2, 623/1.22, 606/191, 606/108, 606/198, 606/194, 148/402
• US Class Current: 623/1.19
• CPC Class Codes: A61F 2/90 characterised by a net-like or mesh-like structure
• CPC Class Codes: A61F 2210/0042 using a fluid, e.g. circulating

Abstract

A stent is reversibly deformable between a lower-temperature shape and a higher-temperature shape in accordance with temperature changes in a patient'"'"'s body. The stent has a hollow cylindrical body formed by a plurality of braided filament bodies made of a Ti—Ni alloy of excessive Ni. A lower-temperature shape memorizing process and a higher-temperature shape memorizing process are conducted to the hollow cylindrical body to memorize the lower-temperature and higher-temperature shapes, respectively. The crossing filament bodies are fixed only at the ends of the stent.

Claims

1. A stent comprising a hollow body made of a plurality of braided filament bodies of an iron-free Ti—

Ni alloy having excessive Ni, the hollow body memorize a first shape during a lower-temperature shape memorizing process and a second shape during a higher-temperature shape memorizing process and being reversibly deformable between the fist shape and the second shape in accordance with temperature change;

wherein the lower-temperature shape memorizing process is a solution thermal treatment and the higher-temperature shape memorizing process is a constraint aging thermal treatment; and

the solution thermal treatment is conducted at a temperature higher than about 800°

C. and lower than or equal to about 1000°

C.

2. The stent according to claim 1, wherein the first shape has a diameter smaller than that of the second shape.

3. The stent according to claim 2, wherein the braided filament bodies are fixed only at both ends of the hollow body.

4. The stent according to claim 2, wherein the diameter of the second shape is larger at both opening ends than in an intermediate portion thereof.

5. The stent according to claim 1, wherein one or more than one of the plurality of filament bodies is/are made of gold or tantalum.

6. The stent according to claim 1, wherein the Ti—

Ni alloy further contains Co or Cu.

7. The stent of claim 1, wherein said hollow body is a hollow cylindrical body.

8. A method of manufacturing a stent, comprising the steps of:

braiding a plurality of filament bodies of an iron-free Ti—

Ni alloy of excessive Ni to form a hollow body deformable into mutually different first and second shapes;

conducting a lower-temperature shape memorizing process for causing the hollow body to memorize the first shape as a lower-temperature shape; and

conducting a higher-temperature shape memorizing process for causing the hollow body to memorize the second shape as a higher-temperature shape;

wherein a solution thermal treatment is conducted during the lower-temperature shape memorizing process and a constraint aging thermal treatment is conducted during the higher-temperature shape memorizing process; and

the solution thermal treatment is conducted at a temperature higher than about 800°

C. and lower than or equal to about 1000°

C.

9. The method according to claim 8, wherein the solution thermal treatment is conducted while keeping the hollow body in the fist shape, and the constraint aging thermal treatment is conducted while binding the hollow body in the second shape.

10. The method of claim 8, wherein said hollow body is a hollow cylindrical body.