Vitrified grindstone having pores partially filled with resin, and method of manufacturing the same

• US 6,450,870 B2
• Filed: 01/19/2001
• Issued: 09/17/2002
• Est. Priority Date: 01/26/2000
• Status: Active Grant

• Current Assignee: Noritake Company Limited (Noritake)
• Original Assignee: Noritake Company Limited (Noritake)
• Inventors: Ito, Kenji
• Primary Examiner(s): Rachuba, M.
• Assistant Examiner(s): MCDONALD, SHANTESE L
• Application Number:
  US09/764,095
• Publication Number:
  US 20010018324A1
• Time in Patent Office: 606 Days
• Field of Search: 451/540, 451/541, 451/542, 451/544, 451/546, 451/548, 512/95, 512/96, 512/97, 512/98, 513/07
• US Class Current: 451/542
• CPC Class Codes: B24B 5/02 involving centres or chucks for holding work
• CPC Class Codes: B24D 18/0027 by impregnation
• CPC Class Codes: B24D 3/18 for porous or cellular structure
• CPC Class Codes: B24D 3/348 utilised as impregnating agent for porous abrasive bodies

Abstract

A vitrified grindstone having a vitrified abrasive structure which has pores and which includes abrasive grains and an inorganic bonding agent that holds the abrasive grains together, wherein 10-95% of a total volume of the pores is filled with a cured resin. The vitrified abrasive structure may further include an aggregate such that the abrasive grains and the aggregate are held together by the inorganic bonding agent.

Claims

1. A vitrified grindstone having a vitrified abrasive structure which has pores and which includes abrasive grains and an inorganic bonding agent that holds said abrasive grains together, wherein 10-95% of a total volume of said pores is filled with a cured resin.

2. A vitrified grindstone according to claim 1, wherein said vitrified abrasive structure further includes an aggregate such that said abrasive grains and said aggregate are held together by said inorganic bonding agent.

3. A vitrified grindstone according to claim 1, wherein 40-90% of the total volume of said pores is filled with said cured resin.

4. A vitrified grindstone according to claim 1, wherein said cured resin consists of at least one thermosetting synthetic resin which is selected from a phenol resin and an epoxy resin.

5. A vitrified grindstone according to claim 1, wherein said abrasive grains consist of diamond abrasive grains.

6. A vitrified grindstone according to claim 1, wherein said abrasive grains consist of CBN abrasive grains.

7. A vitrified grindstone according to claim 1, wherein said abrasive grains in said vitrified abrasive structure have a concentration of 10-230.

8. A vitrified grindstone according to claim 1, wherein said abrasive grains have an average grain size of 20-220 μ

m.

9. A vitrified grindstone according to claim 1, wherein said vitrified abrasive structure has a porosity of 20-75% by volume, before said vitrified abrasive structure is impregnated with said resin.

10. A vitrified grindstone according to claim 1, wherein said inorganic bonding agent includes a crystallized glass in which willemite precipitates.

11. A vitrified grindstone according to claim 1, wherein said vitrified abrasive structure includes 15-35% by volume of said inorganic bonding agent.

12. A vitrified grindstone according to claim 1, wherein said vitrified abrasive structure further includes a pore forming agent.

13. A method of manufacturing a vitrified grindstone having a vitrified abrasive structure which includes abrasive grains and an inorganic bonding agent that holds said abrasive grains together, said method comprising:

a step of preparing a mixture of a liquid resin and a liquid diluent which is other than said liquid resin and which dilutes said liquid resin, such that said mixture includes 10-95% by volume of said liquid resin;

a step of impregnating said vitrified abrasive structure with said mixture; and

a step of curing said liquid resin contained in said mixture with which said vitrified abrasive structure is impregnated.

14. A method according to claim 13, wherein said liquid diluent consists of a volatile liquid.