Electrical cable having a semiconductive water-blocking expanded layer

• US 6,455,769 B1
• Filed: 06/20/2000
• Issued: 09/24/2002
• Est. Priority Date: 12/22/1997
• Status: Expired due to Term

• Current Assignee: Prysmian Cavi E Sistemi Italia Srl (Prysmian SPA)
• Original Assignee: Pirelli Cavi e Sistemi S.P.A. (Prysmian SPA)
• Inventors: Belli, Sergio, Balconi, Luca, Bareggi, Alberto, Caimi, Luigi
• Primary Examiner(s): Nguyen, Chau N.
• Application Number:
  US09/597,267
• Time in Patent Office: 826 Days
• Field of Search: 174/23.C, 174/23.R, 174/102.SC, 174/105.SC, 174/120.SC, 174/102.R, 174/106.R, 174/110.F
• US Class Current: 174/23.00C
• CPC Class Codes: H01B 7/288 using hygroscopic material or material swelling in the presence of liquid
• CPC Class Codes: H01B 9/027 composed of semi-conducting layers
• CPC Class Codes: Y02A 30/14 Extreme weather resilient electric power supply systems, e.g. strengthening power lines or underground power cables

Abstract

Electrical cable, in particular for medium- or high-voltage power transmission or distribution, having a metal shield and a semiconductive water-blocking expanded layer. This layer exerts three main functions, the first one is to elastically and uniformly absorb radial forces of expansion and contraction of the cable coating layers due to thermal cycles of the cable during use, thus preventing deformations or breakages in the metal shield, the second one is to ensure electrical continuity between the cable core and the metal shield, the third one is to effectively avoid penetration and propagation of moisture and/or water along the cable core due, e.g., to possible ruptures in the metal shield. The third function is obtained by including in the expanded layer a water-swellable material.

Claims

1. Electrical cable comprising a conductor, at least one insulating layer, an outer metal shield and a layer of an expanded polymer material placed under the metal shield, characterized in that the layer of the expanded polymer material is semiconductive and includes a water-swellable material, and wherein the layer of the expanded polymer material has a degree of expansion between 5% and 500%.

2. Cable according to claim 1, wherein the expanded layer has a predtermined degree of expansion so as to ensure elastic absorption of the radial forces of thermal expansion and contraction of the cable and to maintain the semiconductive properties.

3. Cable according to claim 2, wherein the degree of expansion of the expanded layer is between 10% and 200%.

4. Cable according to claim 1, wherein the thickness of the expanded layer is at least 0.1 mm.

5. Cable according to claim 4, wherein the thickness of the expanded layer is between 0.2 and 2 mm .

6. Cable according to claim 1, further comprising a compact semiconductive layer placed between the insulating layer and the expanded layer.

7. Cable according to claim 6, wherein the compact semiconductive layer has a thickness of from 0.1 to 1 mm.

8. Cable according to claim 7, wherein the compact semiconductive layer has a thickness of from 0.2 to 0.5 mm.

9. Cable according to claim 1, wherein the water-swellable material is in the form of powder.

10. Cable according to claim 9, wherein the water-swellable material is in the form of powder having a particle diameter not greater than 250 μ

m and an average particle diameter of from 10 to 100 μ

m.

11. Cable according to claim 10, wherein in the water-swellable material the amount of particles having a diameter of from 10 to 50 μ

m are at least 50% by weight with respect the total weight of the powder.

12. Cable according to claim 1, wherein the water swellable material is a homopolymer or copolymer having hydrophilic groups along the polymer chain.

13. Cable according to claim 1, wherein the water-swellable material is present in an amount of from 5 to 120 phr.

14. Cable according to claim 13, wherein the water-swellable material is present in an amount of from 15 to 80 phr.

15. Cable according to claim 1, wherein the polymer material which constitutes the expanded layer is an expandable polymer comprising:

polyolefins, copolymers of different olefins, copolymers of an olefin with an ethylenically unsaturated ester, polyesters, polycarbonates, polysulfones, phenolic resins, or urea resins, or mixtures thereof.

16. Cable according to claim 15, wherein the polymer material is an olefin polymer comprising ethylene or propylene.

17. Cable according to claim 16, wherein the polymer material comprises:

(a) copolymers of ethylene with an ethylenically unsaturated ester, wherein the amount of unsaturated ester is between 5 and 80% by weight;

(b) elastomeric copolymers of ethylene with at least one C₃-C₁₂ alpha-olefin, and optionally a diene, having the following composition;

35-90% mole of ethylene, 10-65% mole of alpha-olefin, 0-10% mole of diene;

(c) copolymers of ethylene with at least one C₄-C₁₂ alpha-olefin, and optionally a diene, having a density of between 0.86 and 0.90 g/cm³;

or

(d) polypropylene modified with ethylene/C₃-C₁₂ alpha-olefin copolymers, wherein the weight ratio between polypropylene and ethylene/C₃-C₁₂ alpha-olefin copolymer is between 90/10 and 10/90.

18. Cable according to claim 17, wherein the polymer material is a thermoplastic elastomer comprising a continuous matrix of a thermoplastic polymer and fine particles of a cured elastomeric polymer dispersed in the thermoplastic polymer.

19. Cable according to claim 15, wherein the polymer material is an olefin copolymer comprising ethylene and propylene.

20. Cable according to claim 1, wherein the expanded layer has a volumetric resistivity value for the expanded material at room temperature of less than 500 Ω

·

m.

21. Cable according to claim 1, wherein the expanded layer further comprises a predetermined amount of electroconductive carbon black.

22. Cable according to claim 21, wherein the electroconductive carbon black has a surface area of at least 20 m²/g.

23. Cable according to claim 22, wherein the carbon black has a surface area of at least 900 m²/g.

24. Cable according to claim 21, wherein the carbon black is present in amounts of between 5 and 80% by weight.

25. Cable according to claim 24, wherein the carbon black is present in amounts of between 10 and 70% by weight.

26. Cable according to claim 1, wherein the expanded layer is obtained by extrusion.

27. Cable according to claim 26, wherein the expansion of the layer is obtained during the extrusion by addition of an expanding agent.

28. Cable according to claim 26, wherein the expansion of the layer is obtained during extrusion by high-pressure injection of a gas.

29. Cable according to claim 1, wherein the diameter of the expanded layer, in the absence of applied forces, is greater than the inside diameter of the metal shield, so as to obtain a predetermined degree of precompression of the expanded layer after the metal shield has been applied.