Anionic waterborne polyurethane dispersions containing polyfluorooxetanes
First Claim
Patent Images
1. A waterborne polyurethane, comprising:
- polyurethane particles dispersed in an aqueous medium, said polyurethane comprising;
at least one polyfluorooxetane repeat unit derived from a polyfluorooxetane oligomer, polymer, or copolymer;
at least one repeat unit derived from a polyol intermediate; and
at least one repeat unit derived from a hydroxyl containing carboxylic acid dispersaint;
said repeat units connected by a urethane linkage derived from at least one polyisocyanate;
wherein said polyurethane is free of a silyl group, optionally wherein said polyurethane is chain extended; and
optionally wherein said polyurethane is crosslinked.
3 Assignments
0 Petitions
Accused Products
Abstract
Anionic waterborne polyurethane dispersions are formed in the presence of polyfluorooxetane oligomers, polymers, or copolymers so that the polyfluorooxetanes are incorporated in the polyurethane. Coatings made from such polyurethanes have good low temperature flexibility, good chemical resistance and abrasion resistance, as well as a low coefficient of friction. Alternatively, the anionic water borne polyurethane dispersion can be blended with vinyl ester monomers such as various acrylates and subsequently polymerized by radiation, for example ultraviolet light, to form a comingled blend of at least two different types of polymers.
53 Citations
58 Claims
-
1. A waterborne polyurethane, comprising:
-
polyurethane particles dispersed in an aqueous medium, said polyurethane comprising;
at least one polyfluorooxetane repeat unit derived from a polyfluorooxetane oligomer, polymer, or copolymer;
at least one repeat unit derived from a polyol intermediate; and
at least one repeat unit derived from a hydroxyl containing carboxylic acid dispersaint;
said repeat units connected by a urethane linkage derived from at least one polyisocyanate;
wherein said polyurethane is free of a silyl group, optionally wherein said polyurethane is chain extended; and
optionally wherein said polyurethane is crosslinked. - View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 22, 23, 24, 25, 26, 27, 28, 29, 30, 31, 32, 33)
or combinations thereof, where n is the same or different and independently each repeat group is an integer of from 1 to about 5, R is hydrogen or an alkyl of from 1 to about 6 carbon atoms, and each Rf is the same or different and, independently, on each repeat unit is a linear or branched fluorinated alkyl of from 1 to about 20 carbon atoms, a minimum of 50 percent of the non-carbon atoms being fluorine atoms and the remaining atoms being H, I, Cl, or Br; - or each Rf is the same or different and, independently, is an oxyperfluorinated polyether having from 4 to about 60 carbon atoms; and
wherein said Dp is from about 2 to about 250.
-
3. A waterborne polyurethane according to claim 2, wherein said carboxylic acid dispersant is neutralized, wherein said polyol intermediate comprises one or more polyether polyols, one or more polythioether polyols, one or more polycarbonate polyols, one or more polyacetal polyols, one or more polyolefin polyols, one or more organic polyols, or one or more polyester polyols, or combinations thereof, and optionally wherein said polyfluorooxetane is a copolymer having at least one repeat unit derived from a monomer containing an epoxy (oxirane) functionality, a monomer having a 4-membered cyclic ether group, a monomer having a 5-membered cyclic ether group, 1,4-dioxane, 1,3-dioxane, trioxane, or caprolactone, or combinations thereof.
-
4. A waterborne polyurethane according to claim according to claim 3, wherein said hydroxyl terminated carboxylic acid dispersant contains one or more carboxyl groups and two or more hydroxyl groups;
- wherein the equivalent weight ratio of said at least one polyisocyanate to said at least one polyfluorooxetane oligomer, polymer, or copolymer, said at least one polyol intermediate, and said at least one hydroxyl containing carboxylic acid dispersant, is from about 0.8 to about 5.0;
wherein the equivalent weight ratio of said at least one polyol intermediate to said at least one polyfluorooxetane oligomer, polymer, or copolymer is from about 2.0 to about 200; and
wherein the weight ratio of said hydroxyl terminated carboxylic acid dispersant is from about 1 to about 15 percent based upon the total weight of said at least one polyfluorooxetane oligomer, polymer, or copolymer, said polyol intermediate, and said hydroxyl terminate carboxylic acid dispersant.
- wherein the equivalent weight ratio of said at least one polyisocyanate to said at least one polyfluorooxetane oligomer, polymer, or copolymer, said at least one polyol intermediate, and said at least one hydroxyl containing carboxylic acid dispersant, is from about 0.8 to about 5.0;
-
5. A waterborne polyurethane according to claim 4, wherein said polyurethane is chain extended;
- wherein said polyol intermediate is derived from one or more polyester polyols or one or more polycarbonate polyols;
wherein said polyfluorooxetane oligomer, polymer, or copolymer is said copolymer, wherein said hydroxyl terminated carboxylic acid dispersant iswherein R is hydrogen or an alkyl containing from 1 to about 16 carbon atoms; and
wherein said polyisocyanate is IPDI, MDI, hexamethylene diisocyanate, or combinations thereof.
- wherein said polyol intermediate is derived from one or more polyester polyols or one or more polycarbonate polyols;
-
6. A waterborne polyurethane according to claim 5, wherein the amount of polyurethane solids in said aqueous medium is from about 20 to about 65 percent by weight, wherein the equivalent weight ratio of said polyisocyanate to said polyfluorooxetane copolymer, said polyol intermediate and said hydroxyl terminated carboxylic acid dispersant is from about 0.9 to about 1.8;
- wherein the equivalent weight ratio of said polyol intermediate to said polyfluorooxetane copolymer is from about 15 to about 50; and
wherein the weight ratio of said hydroxyl terminated carboxylic acid dispersant is from about 2 to about 10 percent based upon the total weight of said polyfluorooxetane copolymer, said polyol intermediate, and said hydroxyl terminated carboxylic acid dispersant.
- wherein the equivalent weight ratio of said polyol intermediate to said polyfluorooxetane copolymer is from about 15 to about 50; and
-
7. A coating, comprising;
- the dried composition of claim 1.
-
8. A coating, comprising;
- the dried composition of claim 3.
-
9. A coating, comprising;
- the dried composition of claim 6.
-
10. A coating, comprising;
- the dried, cured composition of claim 1.
-
11. A coating, comprising;
- the dried, cured composition of claim 3.
-
12. A coating, comprising;
- the dried, cured composition of claim 6.
-
22. A laminate, comprising:
a coating on a substrate, said coating comprising the dried composition of claim 1.
-
23. A laminate, comprising:
a coating on a substrate, said coating comprising the dried composition of claim 2.
-
24. A laminate, comprising:
a coating on a substrate, said coating comprising the dried composition of claim 3.
-
25. A laminate, comprising:
a coating on a substrate, said coating comprising the dried composition of claim 4.
-
26. A laminate, comprising:
a coating on a substrate, said coating comprising the dried composition of claim 5.
-
27. A laminate, comprising:
a coating on a substrate, said coating comprising the dried composition of claim 6.
-
28. A laminate according to claim 22, wherein said substrate is plastic, paper, a wood containing article, a metal, or combinations thereof.
-
29. A laminate according to claim 25, wherein said substrate is plastic, paper, a wood containing article, a metal, or combinations thereof.
-
30. A laminate according to claim 27, wherein said substrate is plastic, paper, a wood containing article, a metal, or combinations thereof.
-
31. A laminate according to claim 23, wherein said substrate is a plastic comprising polyvinyl chloride, nylon, polyester, polyolefin, polyurethane, polystyrene, polyacrylate, polycarbonate, or combinations thereof.
-
32. A laminate according to claim 25, wherein said substrate is a fiber comprising polyester, polyolefin, nylon, or combinations thereof.
-
33. A laminate according to claim 27, wherein said substrate is a carpet fiber comprising polyester, polyolefin, nylon, or combinations thereof.
-
-
13. A polyurethane-polyester composition, comprising a polyurethane and a polyvinyl ester polymer;
-
said polyurethane comprising at least one polyfluorooxetane repeat unit derived from a polyfluorooxetane oligomer, polymer, or copolymer;
at least one repeat unit derived from a polyol intermediate; and
at least one repeat unit derived from a hydroxyl containing carboxylic acid dispersant;
said repeat units connected by a urethane linkage derived from at least one polyisocyanate;
wherein said polyurethane is free of a silyl group;
optionally wherein said polyurethane is chain extended;
optionally wherein said polyurethane is crosslinked; and
said polyvinyl ester polymer derived from at least one radiation initiable free radical polymerizable vinyl ester monomer, or oligomer, or combinations thereof. - View Dependent Claims (14, 15, 16, 17, 18, 19, 20, 21, 34, 35, 36, 37, 38, 39, 40, 41)
or combinations thereof, where n is the same or different and independently each repeat group is an integer of from 1 to about 5, R is hydrogen or an alkyl of from 1 to about 6 carbon atoms, and each Rf is the same or different and, independently, on each repeat unit is a linear or branched fluorinated alkyl of from 1 to about 20 carbon atoms, a minimum of 50 percent of the non-carbon atoms being fluorine atoms and the remaining atoms being H, I, Cl, r Br; - or each Rf is the same or different and, independently, is an oxyperfluorinated polyether having from 4 to about 60 carbon atoms; and
wherein said Dp is from about 2 to about 250, and
wherein said vinyl ester monomer or oligomer is an ester of an ethylenically unsaturated carboxylic acid.
-
-
15. A polyurethane-polyvinyl ester composition according to claim 14, wherein said carboxylic acid dispersant is neutralized, wherein said polyol intermediate comprises one or more polyether polyols, one or more polythioether polyols, one or more polycarbonate polyols, one or more polyacetal polyols, one or more polyolefin polyols, one or more organic polyols, or one or more polyester polyols, or combinations thereof, and optionally wherein said polyfluorooxetane is a copolymer having at least one repeat unit derived from a monomer containing an epoxy (oxirane) functionality, a monomer having a 4-membered cyclic ether group, a monomer having a 5-membered cyclic ether group, 1,4-dioxane, 1,3-dioxane, trioxane, or caprolactone, or combinations thereof, and
wherein said vinyl ester is an acrylate, or a methacrylate, or an alkoxylated (meth)acrylate comprising at least 2 (meth)acrylate groups wherein said (meth) group may or may not exist and from 3 to about 50 alkoxy groups, or combinations thereof. -
16. A polyurethane-polyvinyl ester composition according to claim 15, wherein said hydroxyl terminated carboxylic acid dispersant contains one or more carboxyl groups and two or more hydroxyl groups;
- wherein the equivalent weight ratio of said at least one polyisocyanate to said at least one polyfluorooxetane oligomer, polymer, or copolymer, said at least one polyol intermediate, and said at least one hydroxyl containing carboxylic acid dispersant, is from about 0.8 to about 5.0;
wherein the equivalent weight ratio of said at least one polyol intermediate to said at least one polyfluorooxetane oligomer, polymer, or copolymer is from about 2.0 to about 200; and
wherein the weight ratio of said hydroxyl terminated carboxylic acid dispersant is from about 1 to about 15 percent based upon the total weight of said at least one polyfluorooxetane oligomer, polymer, or copolymer, said polyol intermediate, and said hydroxyl terminate carboxylic acid dispersant.
- wherein the equivalent weight ratio of said at least one polyisocyanate to said at least one polyfluorooxetane oligomer, polymer, or copolymer, said at least one polyol intermediate, and said at least one hydroxyl containing carboxylic acid dispersant, is from about 0.8 to about 5.0;
-
17. A polyurethane-polyvinyl ester composition according to claim 16, wherein said polyurethane is chain extended;
- wherein said polyol intermediate is derived from one or more polyester polyols or one or more polycarbonate polyols;
wherein said polyfluorooxetane oligomer, polymer, or copolymer is said copolymer, wherein said hydroxyl terminated carboxylic acid dispersant iswherein R is hydrogen or an alkyl containing from 1 to about 16 carbon atoms; and
wherein said polyisocyanate is IPDI, MDI, hexamethylene diisocyanate, or combinations thereof, andwherein said vinyl ester oligomer comprises said alkoxylated (meth)acrylate, wherein the number of said (meth)acrylate groups is from about 2 to about 4, wherein the ester portion of said (meth)acrylate is an alkyl having from 1 to 10 carbon atoms, and wherein the amount of said alkoxy groups is from about 3 to about 20, wherein said alkoxylated (meth)acrylate is UV polymerizable, and wherein the amount of said alkoxylated (meth)acrylated is from about 5 to about 75 parts by weight for every 100 parts by weight of said polyurethane.
- wherein said polyol intermediate is derived from one or more polyester polyols or one or more polycarbonate polyols;
-
18. A polyurethane-polyvinyl ester composition according to claim 17, wherein the equivalent weight ratio of said polyisocyanate to said polyfluorooxetane copolymer, said polyol intermediate and said hydroxyl terminated carboxylic acid dispersant is from about 0.9 to about 1.8;
- wherein the equivalent weight ratio of said polyol intermediate to said polyfluorooxetane copolymer is from about 15 to about 50; and
wherein the weight ratio of said hydroxyl terminated carboxylic acid dispersant is from about 2 to about 10 percent based upon the total weight of said polyfluorooxetane copolymer, said polyol intermediate, and said hydroxyl terminated carboxylic acid dispersant.
- wherein the equivalent weight ratio of said polyol intermediate to said polyfluorooxetane copolymer is from about 15 to about 50; and
-
19. A polyurethane-polyvinyl ester composition according to claim 13, wherein said polyurethane is crosslinked.
-
20. A polyurethane-polyvinyl ester composition according to claim 16, wherein said polyurethane is crosslinked.
-
21. A polyurethane-polyvinyl ester composition according to claim 18, wherein said polyurethane is crosslinked.
-
34. A laminate, comprising:
a substrate, and a substrate coating comprising the composition of claim 13.
-
35. A laminate, comprising:
a substrate, and a substrate coating comprising the composition of claim 15.
-
36. A laminate, comprising:
a substrate, and a substrate coating comprising the composition of claim 18.
-
37. A laminate, comprising:
a substrate, and a substrate coating comprising the composition of claim 19.
-
38. A laminate, comprising:
a substrate, and a substrate coating comprising the composition of claim 21.
-
39. A coating comprising the composition of claim 13.
-
40. A coating comprising the composition of claim 15.
-
41. A coating comprising the composition of claim 18.
-
42. A process for making a waterborne polyurethane dispersion, comprising the steps of:
-
reacting at least one polyisocyanate with at least one polyol intermediate, at least one hydroxyl terminated carboxylic acid dispersant, and at least one polyfluorooxetane oligomer, polymer, or copolymer to form a polyurethane;
neutralizing said polyurethane;
dispersing said neutralized polyurethane in water;
optionally chain-extending said polyurethane, optionally crosslinking said polyurethane, and wherein said polyurethane is free of a silyl group. - View Dependent Claims (43, 44, 45, 46)
or combinations thereof, where n is the same or different and, independently, each repeat group is an integer of from 1 to about 5, R is hydrogen or an alkyl of from 1 to about 6 carbon atoms, and each Rf is the same or different and, independently, on each repeat unit is a linear or branched fluorinated alkyl of 1 to about 20 carbon atoms, a minimum of 50 percent of the non-carbon atoms being fluorine atoms and the remaining atoms being H, I, Cl, or Br; - or each Rf is the same or different and, independently, is an oxyperfluorinated polyether having from 4 to about 60 carbon atoms, and wherein said Dp is from about 2 to about 250;
wherein said polyol intermediate comprises one or more polyether polyols, one or more polythioether polyols, one or more polycarbonate polyols, one or more polyacetal polyols, one or more polyolefin polyols, one or more organic polyols, or one or more polyester polyols, or combinations thereof, and optionally wherein said polyfluorooxetane is a copolymer having at least one repeat unit derived from a monomer containing an epoxy (oxirane) functionality, a monomer having a 4-membered cyclic ether group, a monomer having a 5-membered cyclic ether group, 1,4-dioxane, 1,3-dioxane, trioxane, or caprolactone, or combinations thereof; and
wherein said hydroxyl terminated carboxylic acid dispersant contains one or more carboxyl groups and two or more hydroxyl groups.
-
44. A process according to claim 43, including chain extending said polyurethane and drying said polyurethane, wherein the equivalent weight ratio of said at least one polyisocyanate to said at least one polyfluorooxetane oligomer, polymer, or copolymer, said at least one polyol intermediate, and said at least one hydroxyl containing carboxylic acid dispersant, is from about 0.8 to about 5.0;
- wherein the equivalent weight ratio of said at least one polyol intermediate to said at least one polyfluorooxetane oligomer, polymer, or copolymer is from about 2.0 to about 200; and
wherein the equivalent weight ratio of said hydroxyl terminated carboxylic acid dispersant is from about 1 to about 15 percent based upon the total equivalent weight of said at least one polyfluorooxetane oligomer, polymer, or copolymer, said polyol intermediate, and said hydroxyl terminate carboxylic acid dispersant.
- wherein the equivalent weight ratio of said at least one polyol intermediate to said at least one polyfluorooxetane oligomer, polymer, or copolymer is from about 2.0 to about 200; and
-
45. A process according to claim 44, wherein said polyol intermediate is derived from one or more polyester polyols or one or more polycarbonate polyols;
- wherein said polyfluorooxetane oligomer, polymer, or copolymer is said copolymer; and
wherein said polyisocyanate is IPDI, MDI, hexamethylene diisocyanate, or combinations thereof.
- wherein said polyfluorooxetane oligomer, polymer, or copolymer is said copolymer; and
-
46. A process according to claim 45, including crosslinking said polyurethane.
-
-
47. A process comprising:
-
mixing one or more radiation initiable free radical polymerizable vinyl ester monomers with a neutralized waterborne polyurethane dispersion to form a mixture thereof;
said polyurethane formed by reacting at least one polyisocyanate with at least one polyol intermediate, at least one hydroxyl terminated carboxylic acid dispersant, and at least one polyfluorooxetane oligomer, polymer, or copolymer;
neutralizing said polyurethane;
dispersing said neutralized polyurethane in water;
optionally chain-extending said polyurethane, optionally crosslinking said polyurethane, and wherein said polyurethane is free of a silyl group. - View Dependent Claims (48, 49, 50, 51, 52)
drying said polyurethane-free radical polymerizable vinyl ester monomer or oligomer mixture; - and
polymerizing said free radical polymerizable monomers or oligomers in the presence of radiation and forming a co-mingled polyurethane-polyvinyl ester composition;
wherein said polyfluorooxetane oligomer or polymer has repeat groups of the formula or combinations thereof, where n is the same or different and, independently, each repeat group is an integer of from 1 to about 5, R is hydrogen or an alkyl of from 1 to about 6 carbon atoms, and each Rf is the same or different and, independently, on each repeat unit is a linear or branched fluorinated alkyl of 1 to about 20 carbon atoms, a minimum of 50 percent of the non-carbon atoms being fluorine atoms and the remaining atoms being H, I, Cl, or Br;
or each Rf is the same or different and, independently, is an oxyperfluorinated polyether having from 4 to about 60 carbon atoms, and wherein said Dp is from about 2 to about 250;
wherein said polyol intermediate comprises one or more polyether polyols, one or more polythioether polyols, one or more polycarbonate polyols, one or more polyacetal polyols, one or more polyolefin polyols, one or more organic polyols, or one or more polyester polyols, or combinations thereof, and optionally wherein said polyfluorooxetane is a copolymer having at least one repeat unit derived from a monomer containing an epoxy (oxirane) functionality, a monomer having a 4-membered cyclic ether group, a monomer having a 5-membered cyclic ether group, 1,4-dioxane, 1,3-dioxane, trioxane, or caprolactone, or combinations thereof; and
wherein said hydroxyl terminated carboxylic acid dispersant contains one or more carboxyl groups and two or more hydroxyl groups.
-
-
49. A process according to claim 48, including chain extending said polyurethane, wherein the equivalent weight ratio of said at least one polyisocyanate to said at least one polyfluorooxetane oligomer, polymer, or copolymer, said at least one polyol intermediate, and said at least one hydroxyl containing carboxylic acid dispersant, is from about 0.8 to about 5.0;
- wherein the equivalent weight ratio of said at least one polyol intermediate to said at least one polyfluorooxetane oligomer, polymer, or copolymer is from about 2.0 to about 200; and
wherein the equivalent weight ratio of said hydroxyl terminated carboxylic acid dispersant is from about 1 to about 15 percent based upon the total equivalent weight of said at least one polyfluorooxetane oligomer, polymer, or copolymer, said polyol intermediate, and said hydroxyl terminate carboxylic acid dispersant, andwherein said vinyl ester is an acrylate, or a methacrylate, or an alkoxylated (meth)acrylate comprising at least 2 (meth)acrylate groups wherein said (meth) group may or may not exist and from 3 to about 50 alkoxy groups, or combinations thereof.
- wherein the equivalent weight ratio of said at least one polyol intermediate to said at least one polyfluorooxetane oligomer, polymer, or copolymer is from about 2.0 to about 200; and
-
50. A process according to claim 49, wherein said polyol intermediate is derived from one or more polyester polyols or one or more polycarbonate polyols;
- wherein said polyfluorooxetane oligomer, polymer, or copolymer is said copolymer; and
wherein said polyisocyanate is IPDI, MDI, hexamethylene diisocyanate, or combinations thereof, andwherein said vinyl ester oligomer comprises said alkoxylated (meth)acrylate, wherein the number of said (meth)acrylate groups is from about 2 to about 4, wherein the ester portion of said (meth)acrylate is an alkyl having from 1 to 10 carbon atoms, and wherein the amount of said alkoxy groups is from about 3 to about 20, wherein said alkoxylated (meth)acrylate is UV polymerizable, and wherein the amount of said alkoxylated (meth)acrylated is from about 5 to about 75 parts by weight for every 100 parts by weight of said polyurethane.
- wherein said polyfluorooxetane oligomer, polymer, or copolymer is said copolymer; and
-
51. A process according to claim 47, including crosslinking said polyurethane.
-
52. A process according to claim 50, including crosslinking said polyurethane.
-
53. A polyurethane composition, comprising:
-
the reaction product of at least one polyfluorooxetane oligomer, polymer, or copolymer;
at least one polyol intermediate;
at least one hydroxyl containing carboxylic acid dispersant; and
at least one polyisocyanate;
wherein said polyurethane is free of a silyl group, optionally wherein said polyurethane is chain extended; and
optionally wherein said polyurethane is crosslinked. - View Dependent Claims (54, 55, 56, 57, 58)
or combinations thereof, where n is the same or different and independently each repeat group is an integer of from 1 to about 5, R is hydrogen or an alkyl of from 1 to about 6 carbon atoms, and each Rf is the same or different and, independently, on each repeat unit is a linear or branched fluorinated alkyl of from 1 to about 20 carbon atoms, a minimum of 50 percent of the non-carbon atoms being fluorine atoms and the remaining atoms being H, I, Cl, or Br; - or each Rf is the same or different and, independently, is an oxyperfluorinated polyether having from 4 to about 60 carbon atoms; and
wherein said Dp is from about 2 to about 250.
-
55. A polyurethane composition according to claim 54, wherein said carboxylic acid dispersant is neutralized, wherein said polyol intermediate comprises one or more polyether polyols, one or more polythioether polyols, one or more polycarbonate polyols, one or more polyacetal polyols, one or more polyolefin polyols, one or more organic polyols, or one or more polyester polyols, or combinations thereof, and optionally wherein said polyfluorooxetane is a copolymer having at least one repeat unit derived from a monomer containing an epoxy (oxirane) functionality, a monomer having a 4-membered cyclic ether group, a monomer having a 5-membered cyclic ether group, 1,4-dioxane, 1,3-dioxane, trioxane, or caprolactone, or combinations thereof.
-
56. A polyurethane composition according to claim 55, wherein said hydroxyl terminated carboxylic acid dispersant contains one or more carboxyl groups and two or more hydroxyl groups;
- wherein the equivalent weight ratio of said at least one polyisocyanate to said at least one polyfluorooxetane oligomer, polymer, or copolymer, said at least one polyol intermediate, and said at least one hydroxyl containing carboxylic acid dispersant, is from about 0.8 to about 5.0;
wherein the equivalent weight ratio of said at least one polyol intermediate to said at least one polyfluorooxetane oligomer, polymer, or copolymer is from about 2.0 to about 200; and
wherein the weight ratio of said hydroxyl terminated carboxylic acid dispersant is from about 1 to about 15 percent based upon the total weight of said at least one polyfluorooxetane oligomer, polymer, or copolymer, said polyol intermediate, and said hydroxyl terminate carboxylic acid dispersant.
- wherein the equivalent weight ratio of said at least one polyisocyanate to said at least one polyfluorooxetane oligomer, polymer, or copolymer, said at least one polyol intermediate, and said at least one hydroxyl containing carboxylic acid dispersant, is from about 0.8 to about 5.0;
-
57. A polyurethane composition according to claim 56, wherein said polyurethane is chain extended;
- wherein said polyol intermediate is derived from one or more polyester polyols or one or more polycarbonate polyols;
wherein said polyfluorooxetane oligomer, polymer, or copolymer is said copolymer, wherein said hydroxyl terminated carboxylic acid dispersant iswherein R is hydrogen or an alkyl containing from 1 to about 16 carbon atoms; and
wherein said polyisocyanate is IPDI, MDI, hexamethylene diisocyanate, or combinations thereof.
- wherein said polyol intermediate is derived from one or more polyester polyols or one or more polycarbonate polyols;
-
58. A polyurethane composition according to claim 57, wherein the amount of polyurethane solids in said aqueous medium is from about 20 to about 60 percent by weight, wherein the equivalent weight ratio of said polyisocyanate to said polyfluorooxetane copolymer, said polyol intermediate and said hydroxyl terminated carboxylic acid dispersant is from about 0.9 to about 1.8;
- wherein the equivalent weight ratio of said polyol intermediate to said polyfluorooxetane copolymer is from about 15 to about 50; and
wherein the weight ratio of said hydroxyl terminated carboxylic acid dispersant is from about 2 to about 10 percent based upon the total weight of said polyfluorooxetane copolymer, said polyol intermediate, and said hydroxyl terminated carboxylic acid dispersant.
- wherein the equivalent weight ratio of said polyol intermediate to said polyfluorooxetane copolymer is from about 15 to about 50; and
-
Specification