Method of producing press-forming punch and die

• US 6,474,196 B2
• Filed: 02/14/2001
• Issued: 11/05/2002
• Est. Priority Date: 02/15/2000
• Status: Expired due to Fees

• Current Assignee: Honda Giken Kogyo Kabushiki Kaisha (Honda Motor Company)
• Original Assignee: Honda Giken Kogyo Kabushiki Kaisha (Honda Motor Company)
• Inventors: Nakamura, Yoshikazu, Nakamura, Masafumi, Watanabe, Teiji
• Primary Examiner(s): PAYER, HWEI SIU CHOU
• Application Number:
  US09/783,357
• Publication Number:
  US 20010013265A1
• Time in Patent Office: 629 Days
• Field of Search: 761/011, 761/071, 724/62, 724/668
• US Class Current: 76/107.1
• CPC Class Codes: B21D 37/20 Making tools by operations not covered by a single other subclass
• CPC Class Codes: B23P 15/24 dies B21C3/18, B21C25/10, B21D37/20 take precedence

Abstract

An economical method of producing a press-forming die is disclosed wherein a master die and a master punch are relatively reciprocated to produce a press-formed panel. A working surface of the master die is cut down by a predetermined cutting depth, and the press-formed panel is fitted over the master punch. While a second blank sheet having a thickness equal to the cutting depth of the master die working surface is placed between the master die and the press-formed panel fitted over the master punch, the master die and punch are relatively reciprocated whereby the second blank sheet is press-formed into a die panel. A back-up material such as high-strength cement is then applied to the rear surface of the die panel whereby a press-forming die is produced. A method of producing a press-forming punch is also disclosed.

Claims

1. A method of producing a press-forming die, comprising the steps of:

preparing a master die and a master punch relatively movable toward and away from each other so as to define therebetween a die cavity, the master die having a working surface partially defining to die cavity;

while a first blank sheet is disposed between the master die and the master punch, relatively reciprocating the master die and the master punch together, thereby press-forming the first blank sheet into a press-formed panel complementary in contour to the shape of the die cavity;

cutting down the working surface of the master die by a predetermined depth of cut;

fitting the press-formed panel over the master punch;

while a second blank sheet having a thickness equal to the predetermined depth of cut of the working surface is disposed between the master die and the press-formed panel fitted over the master punch, relatively reciprocating the master die and the master punch together, thereby press-forming the second blank sheet into a die panel complementary in contour to the shape of the press-formed panel; and

applying a back-up material to the rear surface of the die panel to thereby produce a press-forming die.

2. The method according to claim 1, between the second-mentioned reciprocating step and the applying step, comprising the additional step-of applying a backing material to the rear surface of the die panel.

3. The method according to claim 2, wherein the backing material comprises a water-soluble epoxy resin.

4. The method according to claim 2, wherein the backing material comprises a fibre-reinforced water-soluble epoxy resin.

5. The method according to claim 1, wherein the die panel is made of steel and has been subjected to a work-hardening process when the second blank sheet is press-formed into the die panel.

6. The method according to claim 1, wherein the back-up material comprises a high-strength cement.

7. The method according to claim 1, wherein the back-up material comprises a synthetic resin.

8. The method according to claim 1, wherein the applying step includes placing a slurry of high-strength cement on the rear surface of the die panel while removing bubbles from the slurry by the action of a vacuum.

9. The method according to claim 8, wherein the applying step further includes applying vibrations to the slurry to promote separation of the bubbles from the slurry.

10. A method of producing a press-forming punch, comprising the steps of:

preparing a master die and a master punch relatively movable toward and away from each other so as to define therebetween a die cavity, the master punch having a working surface partially defining the die cavity;

while a first blank sheet is disposed between the master die and the master punch, relatively reciprocating the master die and the master punch together, thereby press-forming the first blank sheet into a press-formed panel complementary in contour to the shape of the die cavity;

cutting down the working surface of the master punch by a predetermined depth of cut;

fitting the press-formed panel in the master die;

while a second blank sheet having a thickness equal to the predetermined depth of cut of the working surface is disposed between the master punch and the press-formed panel fitted in the master die, relatively reciprocating the master die and the master punch together, thereby press-forming the second blank sheet into a punch panel complementary in contour to the shape of the press-formed panel; and

applying a back-up material to the rear surface of the punch panel to thereby produce a press-forming punch.

11. The method according to claim 10, between the second-mentioned reciprocating step and the applying step, comprising the additional step of applying a backing material to the rear surface of the punch panel.

12. The method according to claim 11, wherein the backing material comprises a water-soluble epoxy resin.

13. The method according to claim 11, wherein the backing material comprises a fibre-reinforced water-soluble epoxy resin.

14. The method according to claim 10, wherein the punch panel is made of steel and has been subjected to a work-hardening process when the second blank sheet is press-formed into the punch panel.

15. The method according to claim 10, wherein the back-up material comprises a high-strength cement.

16. The method according to claim 10, wherein the back-up material comprises a synthetic resin.

17. The method according to claim 10, wherein the applying step includes placing a slurry of high-strength cement on the rear surface of the punch panel while removing bubbles from the slurry by the action of a vacuum.

18. The method according to claim 17, wherein the applying step farther includes applying vibrations to the slurry to promote separation of the bubbles from the slurry.

19. A method of producing a press-forming punch and a press-forming die in succession, comprising the steps of:

preparing a master die and a master punch relatively movable toward and away from each other so as to define therebetween a die cavity, the master die and master punch having respective working surfaces jointly defining the die cavity;

while a first blank sheet is disposed between the master die and the master punch, relatively reciprocating the master die and the master punch together, thereby press-forming the first blank sheet into a press-formed panel complementary in contour to the shape of the die cavity;

cutting down the working surface of the master punch by at predetermined depth of cut;

fitting the press-formed panel in the master die;

while a second blank sheet having a thickness equal to the predetermined depth of cut of the working surface is disposed between the master punch and the press-formed panel fitted in the master die, relatively reciprocating the master die and the master punch together, thereby press-forming the second blank sheet into a first punch panel complementary in contour to the shape of the press-formed panel;

repeating the second-named reciprocating step to thereby produce a second punch panel;

applying a back-up material to the rear surface of the first punch panel to thereby produce a press-forming punch;

cutting down the working surface of the master die by a second predetermined depth of cut;

fitting the second punch panel over the master punch;

fitting the press-formed panel over the second punch panel;

while a third blank sheet having a thickness equal to the second predetermined depth of cut of the working surface of the master die is disposed between the master die and the second punch panel fitted over the master punch, relatively reciprocating the master die and the master punch together, thereby press-forming the third blank sheet into a die panel complementary in contour to the shape of the press-formed panel; and

applying a back-up material to the rear surface of the die panel to thereby produce a press-forming die.

20. The method according to claim 19, comprising the additional steps of applying a backing material to the rear surface of the first punch panel, and applying a backing material to the rear surface of the die panel.

21. The method according to claim 20, wherein the backing materials comprise a water-soluble epoxy resin.

22. The method according to claim 20, wherein the backing materials comprise a fibre-reinforced water-soluble epoxy resin.

23. The method according to claim 19, wherein the die panel is made of steel and has been subjected to a work-hardening process when the third blank sheet is press-formed into the die panel, and the first punch panel is made of steel and has been subjected to a work-hardening process when the second blank sheet is press-formed into the first punch panel.

24. The method according to claim 19, wherein the back-up materials comprise a high-strength cement.

25. The method according to claim 19, wherein the back-up up materials comprise a synthetic resin.

26. The method according to claim 19, wherein the first mentioned applying step includes placing a slurry of high-strength cement on the rear surface of the first punch panel while removing bubbles from the slurry by the action of a vacuum, and the second-mentioned applying step includes placing a slurry of high-strength cement on the rear surface of the die panel while removing bubbles from the slurry by the action of a vacuum.

27. The method according to claim 26, wherein the first-mentioned applying step further includes applying vibrations to the slurry to promote separation of the bubbles from the slurry, and the second-mentioned applying step further includes applying vibrations to the slurry to promote separation of the bubbles from the slurry.