Polyfunctional fluorosilicone composition, method for making, and use

• US 6,479,610 B1
• Filed: 07/27/2000
• Issued: 11/12/2002
• Est. Priority Date: 07/27/2000
• Status: Expired due to Term

• Current Assignee: General Electric Company
• Original Assignee: General Electric Company
• Inventors: Singh, Navjot, Leman, John Thomas, Whitney, John M.
• Primary Examiner(s): Moore, Margaret G.
• Application Number:
  US09/627,911
• Time in Patent Office: 838 Days
• Field of Search: 528/42, 528/18, 524/43, 524/588
• US Class Current: 528/18
• CPC Class Codes: C08G 77/045 containing less than 25 silicon atoms
• CPC Class Codes: C08G 77/24 halogen-containing groups
• CPC Class Codes: C08K 5/57 Organo-tin compounds
• CPC Class Codes: C08L 2666/44 Silicon-containing compounds
• CPC Class Codes: C08L 2666/52 Metal-containing compounds
• CPC Class Codes: C08L 83/00 Compositions of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon only; Compositions of derivatives of such polymers
• CPC Class Codes: C08L 83/08 containing silicon bound to organic groups containing atoms other than carbon, hydrogen and oxygen

Abstract

A fluorosilicone crosslinker and method for making is provided. Reaction is effected between a silanol terminated polyfluoroalkyl silicone fluid and a polyalkoxysilane in the presence of a Platinum Group Metal catalyst. The fluorosilicone crosslinker can be used in combination with a silanol terminated fluoroalkyl substituted polydiorganosiloxane to formulate a neutral, condensation curable, solvent resistant sealant.

Claims

1. A neutral, room temperature condensation curable, fluorosilicone sealant composition comprising:

(A) a silanol terminated fluoroalkyl substituted polydiorganosiloxane, wherein fluoroalkyl substituent groups are C_(3-5) polyfluoroalkyl groups;

(B) an oligomeric fluorosilicone crosslinker;

(C) a filler; and

(D) an effective amount of a condensation catalyst.

2. The sealant composition in accordance with claim 1, wherein the polydiorganosiloxane is present at about 80 parts per 100 parts by weight of the sealant composition.

3. The sealant composition in accordance with claim 1, where the polydiorganosiloxane comprises organofluorosiloxy units of the formula

8. The sealant composition in accordance with claim 1, where the condensation catalyst comprises an organometallic compound.

9. The sealant composition in accordance with claim 8, where the organometallic compound comprises dibutyltin diacetate, dimethyltin neodecanoate, dibutyltin dilaurate, stannous octoate, dimethyltin hydroxyoleate, or combinations thereof.

10. The sealant composition in accordance with claim 9, where the organometallic compound comprises dibutyltin diacetate.

11. The sealant composition in accordance with claim 1, where the condensation catalyst is present in a range between about 0.1 parts and about 5.0 parts by weight per 100 parts of the of sealant composition.

12. The sealant composition in accordance with claim 11, where the condensation catalyst is present in a range between about 0.1 parts and about 1.0 parts by weight per 100 parts of the sealant composition.

13. The sealant composition in accordance with claim 1, where the filler comprises fumed silica.

4. A neutral, room temperature condensation curable, fluorosilicone sealant composition comprising:

(A) a silanol terminated fluoroalkyl substituted polydiorganosiloxane which comprises organofluorosiloxy units of the formula

5. A neutral, room temperature condensation curable, fluorosilicone sealant composition comprising:

(A) a silanol terminated fluoroalkyl substituted polydiorganosiloxane;

(B) an oligomeric fluorosilicone crosslinker which comprises a material having a formula

6. The sealant composition in accordance with claim 5, where the crosslinker comprises a dimethoxymethylsilyl terminated methyltrifluoropropyl-siloxane fluid.

7. The sealant composition in accordance with claim 5, where the crosslinker is present in a range between about 1 part and about 20 parts by weight per 100 parts of the silanol terminated fluoroalkyl substituted polydiorganosiloxane.

14. A neutral, room temperature condensation curable, fluorosilicone sealant composition comprising:

(A) a silanol terminated C_(3-5) polyflouroalkyl substituted polydiorganosiloxane;

(B) an oligomeric fluorosilicone crosslinker;

(C) a filler; and

(D) an effective amount of a condensation catalyst;

wherein the filler is present in an amount up to about 30 parts by weight per 100 parts of the silanol terminated fluoroalkyl substituted polydiorganosiloxane.

15. The sealant in accordance with claim 14, where the filler is present in a range between about 5 parts and about 15 parts by weight per 100 parts of the silanol terminated fluoroalkyl substituted polydiorganosiloxane.

16. A neutral, room temperature condensation curable, fluorosilicone sealant composition comprising:

(A) a silano terminated fluoroalkyl substituted polyorganosiloxane, wherein fluoroalkyl substituent groups are C_(3-5) polyfluoroalkyl groups;

(B) an oligomeric fluorosilicone crosslinker;

(C) a filler;

(D) an effective amount of a condensation catalyst; and

(E) a heat stabilizer.

17. The sealant composition in accordance with claim 16, where the heat stabilizer comprises iron oxide, ceric oxide, titanium dioxide, or combinations thereof.

18. The sealant composition in accordance with claim 17, where the heat stabilizer comprises iron oxide.

19. The sealant composition in accordance with claim 16, wherein said heat stabilizer is present in a range between about 0.1 parts and about 10 parts by weight per 100 parts of the silanol terminated fluoroalkyl substituted polydiorganosiloxane.

20. A neutral, room temperature condensation curable, fluorosilicone sealant composition comprising by weight:

(A) a silanol terminated fluoroalkyl substituted polydiorganosiloxane which comprises trifluoropropyl(methyl)siloxy units present at about 80 parts per 100 parts by weight of the sealant composition,

(B) a diethoxymethylsilyl terminated methyltrifluoropropylsiloxane present in a range between about 1 part and about 20 parts by weight per 100 parts of the silanol terminated fluoroalkyl substituted polydiorganosiloxane,

(C) fumed silica filler in a range between about 5 parts and about 15 parts by weight per 100 parts of the silanol terminated fluoroalkyl substituted polydiorganosiloxane, and

(D) dibutyltin diacetate in a range between about 0.1 parts and about 1 parts by weight per 100 parts of the silanol terminated fluoroalkyl substituted polydiorganosiloxane.