Increased throughput in the manufacture of anionic polymers by reduction in polymers by reduction in polymer cement viscosity through the addition of metal alkyls
First Claim
1. A method for anionically polymerizing monomers, comprising:
- a) forming a reaction mixture by contacting monomers with a mono- or multi-functional anionic polymerization initiator, wherein the polymerization initiator is an organo-substituted alkali metal compound in a suitable solvent;
b) adding to (a) before, or at the beginning of polymerization, at least 0.01 equivalents of a metal alkyl compound per equivalent of alkali metal to reduce the viscosity of the reaction mixture, wherein the alkyl groups of the metal alkyl compound are chosen so that they will not exchange with the alkali metal.
12 Assignments
0 Petitions
Accused Products
Abstract
The present invention is an improvement upon the known method of anionically polymerizing monomers by contacting the monomers with an anionic polymerization initiator which is an organo-substituted alkali metal compound. The improvement comprises decreasing the viscosity of the polymer cement by adding at least 0.01 equivalent of a metal alkyl compound per equivalent of alkali metal initiator if the metal alkyl is added before or at the beginning of polymerization. If the metal alkyl is added during the polymerization or after but before the living polymer is terminated, then at least 0.01 equivalent of the metal alkyl compound per equivalent of living polymer chain ends is should be used. The alkyl groups of the metal alkyl are chosen such that they do not exchange with the organo substituents of the alkali metal, which can be the living polymer chain ends or the organo substituents of the initiator. To avoid this undesired exchange reaction, the alkyl groups of the metal alkyl compound are selected to be more basic and/or less bulky or both than the organo substituents of the alkali metal compound.
-
Citations
10 Claims
-
1. A method for anionically polymerizing monomers, comprising:
-
a) forming a reaction mixture by contacting monomers with a mono- or multi-functional anionic polymerization initiator, wherein the polymerization initiator is an organo-substituted alkali metal compound in a suitable solvent;
b) adding to (a) before, or at the beginning of polymerization, at least 0.01 equivalents of a metal alkyl compound per equivalent of alkali metal to reduce the viscosity of the reaction mixture, wherein the alkyl groups of the metal alkyl compound are chosen so that they will not exchange with the alkali metal. - View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10)
-
Specification