Method of manufacture of semi-compliant catheter balloons

• US 6,495,090 B1
• Filed: 06/22/1999
• Issued: 12/17/2002
• Est. Priority Date: 06/11/1998
• Status: Expired due to Fees

• Current Assignee: Infinity Extrusion & Engineering
• Original Assignee: Infinity Extrusion & Engineering
• Inventors: Wilkins, Douglas
• Primary Examiner(s): McDowell, Suzanne E.
• Application Number:
  US09/338,349
• Time in Patent Office: 1,274 Days
• Field of Search: 264/540, 264/573
• US Class Current: 264/540
• CPC Class Codes: A61L 29/041 obtained by reactions only involving carbon-to-carbon unsaturated bonds
• CPC Class Codes: A61L 29/049 Mixtures of macromolecular compounds
• CPC Class Codes: A61M 25/1029 Production methods of the balloon members, e.g. blow-moulding, extruding, deposition or by wrapping a plurality of layers of balloon material around a mandril
• CPC Class Codes: C08L 35/04 Homopolymers or copolymers of nitriles C08L35/06, C08L35/08 take precedence
• CPC Class Codes: Y10T 428/1334 Nonself-supporting tubular film or bag [e.g., pouch, envelope, packet, etc.]

Abstract

The present invention relates to catheter balloons for medical devices. In particular, the present invention provides biaxially oriented semi-compliant catheter balloons comprising acrylonitrile polymers, acrylonitrile copolymers, and acrylonitrile blends, and methods of making same. The catheter balloons provided herein exhibit relatively high tensile strength, controlled compliance, reduced tendency for pinholing, ease of coating with and of bonding to other compounds, as well as resistance to moisture.

Claims

1. A method for making a biaxially oriented catheter balloon, comprising:

a) providing a material selected from the group consisting of acrylonitrile homopolymer, acrylonitrile copolymer, and acrylonitrile blend;

b) extruding said material to form an extruded tube;

c) heat setting said extruded tube to form a heat set tube;

d) longitudinally drawing said heat set tube to form a drawn tube;

e) radially expanding said drawn tube to form a balloon member; and

f) heat setting said balloon member to form a heat set balloon member.

2. The method of claim 1, wherein said extruding is performed in a die comprising a barrel zone, and wherein said die is at a temperature of from approximately 500°

F. to approximately 560°

F. and said barrel zone is at a temperature of from approximately 400°

F. to approximately 470°

F.

3. The method of claim 2, further comprising after step b) quenching said extruded tube in a water bath at approximately 22°

C.

4. The method of claim 3, wherein the distance between said water bath and said die is from approximately 0.2 inches to approximately 1.0 inches.

5. The method of claim 1, wherein said tube is extruded at a drawdown ratio of less than 3:

1.

6. The method of claim 5, wherein said drawdown ratio is approximately 2:

1.

7. The method of claim 1, wherein said heat setting is at a temperature of from approximately 60°

C. to approximately 80°

C.

8. The method of claim 1, wherein said heat setting is for a period of at least approximately two hours.

9. The method of claim 1, wherein the time between said heat setting and said extruding is less than approximately eight hours.

10. The method of claim 1, wherein said drawing is at a tube draw temperature between the first order glass transition temperature and the second order glass transition temperature of said material.

11. The method of claim 10, wherein said tube draw temperature is from approximately 300°

C. to approximately 450°

C.

12. The method of claim 10, wherein the length of said drawn tube is from approximately 2 times to approximately 5 times the length of said extruded tube.

13. The method of claim 1, wherein said radially expanding is at a blow up ratio of from approximately 5.25:

1 to approximately 7.25;

1.

14. The method of claim 1, wherein the ratio of mean wall thickness of said heat set tube to said heat set balloon is from approximately 15:

1 to approximately 20;

1.

15. The method of claim 1, wherein said heat setting of said balloon member comprises raising the temperature of said balloon member to a heat setting temperature greater than the glass transition temperature of said material to form a heated balloon member, followed by cooling said heated balloon member to a temperature below the glass transition temperature of said material.

16. The method of claims 15, wherein said heat setting temperature is from approximately 90°

C. to approximately 180°

C.

17. The method of claim 15, wherein said glass transition temperature is from approximately 180°

C. to approximately 240°

C.

18. The method of claim 15, wherein said temperature below the glass transition temperature is from approximately 20°

C. to approximately 25°

C.

19. The method of claim 1, wherein said acrylonitrile blend comprises acrylonitrile and polyethylene elastomer.

20. The method of claim 1, wherein said acrylonitrile blend comprises acrylonitrile and a block copolymer comprising crystalline polybutylene terephthalate and amorphous long chain glycols.

21. The method of claim 1, wherein said acrylonitrile blend comprises acrylonitrile and polyether block amide.

22. The method of claim 1, further comprising after step d) the step of cooling said drawn tube to room temperature.

23. The method of claim 1, further comprising after step b) the step of quenching said extruded tube in a water bath at approximately 22°

C., and after step d) the step of cooling said drawn tube to room temperature.

24. The method of claim 1, wherein said material in step (a) is acrylonitrile homopolymer.

25. The method of claim 24, further comprising after step b) the step of quenching said extruded tube in a water bath at approximately 22°

C.

26. The method of claim 24, further comprising after step d) the step of cooling said drawn tube to room temperature.

27. The method of claim 24, further comprising after step b) the step of quenching said extruded tube in a water bath at approximately 22°

C., and after step d) the step of cooling said drawn tube to room temperature.

28. The method of claim 1, wherein said material in step (a) is acrylonitrile copolymer.

29. The method of claim 28, wherein said acrylonitrile copolymer comprises acrylonitrile and methyl acrylate.

30. The method of claim 29, wherein said acrylonitrile copolymer comprises from approximately 73 to approximately 77 parts by weight of acrylonitrile and from approximately 23 to approximately 27 parts by weight of methyl acrylate.

31. The method of claim 28, further comprising after step b) the step of quenching said extruded tube in a water bath at approximately 22°

C.

32. The method of claim 28, further comprising after step d) the step of cooling said drawn tube to room temperature.

33. The method of claim 28, further comprising after step b) the step of quenching said extruded tube in a water bath at approximately 22°

C., and after step d) the step of cooling said drawn tube to room temperature.

34. The method of claim 1, wherein said material in step (a) is acrlyontirile blend.

35. The method of claim 34, wherein said acrylonitrile blend comprises acrylonitrile and polyethylene elastomer.

36. The method of claim 35, wherein said acrylonitrile blend comprises approximately 70 parts by weight of acrylonitrile and approximately 30 parts by weight of polyethylene elastomer.

37. The method of claim 34, further comprising after step b) the step of quenching said extruded tube in a water bath at approximately 22°

C.

38. The method of claim 34, further comprising after step d) the step of cooling said drawn tube to room temperature.

39. The method of claim 34, further comprising after step b) the step of quenching said extruded tube in a water bath at approximately 22°

C., and after step d) the step said drawn tube to room temperature.