Polymerizable composition of allyl functional monomers

• US 6,506,864 B1
• Filed: 08/01/2000
• Issued: 01/14/2003
• Est. Priority Date: 04/10/2000
• Status: Expired due to Term

• Current Assignee: PPG Industries Ohio Incorporated (Nouryon BV)
• Original Assignee: PPG Industries Ohio Incorporated (Nouryon BV)
• Inventors: Herold, Robert D., Daughenbaugh, Randy E.
• Primary Examiner(s): PEZZUTO, HELEN LEE
• Application Number:
  US09/630,074
• Time in Patent Office: 896 Days
• Field of Search: 526/204, 526/217, 526/220, 526/230.5, 526/314
• US Class Current: 526/314
• CPC Class Codes: C08F 18/24 Esters of carbonic or haloformic acids
• CPC Class Codes: C08F 218/24 Esters of carbonic or haloformic acids, e.g. allyl carbonate

Abstract

Describes a polymerizable composition of (a) a first allyl functional monomer, which is selected such that a substantially completely cured polymerizate of the first allyl functional monomer has a 15 second Barcol 934 hardness of at least 40, and (b) a second allyl functional monomer selected from polyether diol bis(allyl carbonate), polylactone diol bis(allyl carbonate) and mixtures thereof. The second allyl functional monomer is present in the composition in an amount to provide a substantially completely cured polymerizate having: (i) improved organic photochromic substance incorporation relative to a substantially completely cured polymerizate of the composition free of monomer (b); and (ii) heat distortion temperature of at least 40° C.

Claims

1. A polymerizable composition comprising:

(a) a first allyl functional monomer having at least two allyl groups, said first allyl functional monomer being selected such that a substantially completely cured polymerizate of said first allyl functional monomer has a 15 second Barcol 934 hardness of at least 40; and

(b) a second allyl functional monomer, which is different from said first allyl functional monomer and is selected from,

(i) polyether diol bis(allyl carbonate);

(ii) polylactone diol bis(allyl carbonate); and

(iii) mixtures of (i) and (ii),

wherein said second allyl functional monomer (b) is present in said polymerizable composition in an amount to provide a substantially completely cured polymerizate of said composition having improved organic photochromic substance incorporation relative to a substantially completely cured polymerizate of said composition free of (b), and heat distortion temperature of at least 40°

C.

2. The polymerizable composition of claim 1 wherein said first allyl functional monomer (a) is selected from

(a)(i) an allyl functional monomer represented by the following general formula,

3. The polymerizable composition of claim 1 wherein the polyether diol of the polyether diol bis(allyl carbonate) (b)(i) is selected from homopolymeric polyether diols, random copolymeric polyether diols, block copolymeric polyether diols and mixtures thereof.

4. The polymerizable composition of claim 1 wherein the polylactone diol of the polylactone diol bis(allyl carbonate) (b)(ii) is the reaction product of a diol and a lactone.

5. The polymerizable composition of claim 4 wherein the diol of the polylactone diol is selected from linear or branched aliphatic diols having from 2 to 20 carbon atoms, poly(C₂-C₄)alkylene glycols, cycloaliphatic diols having from 5 to 8 carbon atoms in the cyclic ring, monocyclic aromatic diols, bisphenols, hydrogenated bisphenols and mixtures thereof;

and the lactone of the polylactone diol is selected from at least one lactone having from 3 to 8 carbon atoms in the cyclic lactone ring.

6. The polymerizable composition of claim 5 wherein said lactone is epsilon-caprolactone.

7. The polymerizable composition of claim 1 wherein said first allyl functional monomer (a) is present in said composition in an amount of from 40 percent by weight to 90 percent by weight, based on the total monomer weight of said composition, and said second allyl functional monomer (b) is present in said composition in an amount of from 10 percent by weight to 60 percent by weight, based on the total monomer weight of said composition.

8. The polymerizable composition of claim 2 wherein said first allyl functional monomer (a) is allyl functional monomer (a)(i) for which R is a residue of 1,2-ethane diol, and said second allyl functional-monomer (b) is polylactone diol bis(allyl carbonate).

9. The polymerizable composition of claim 8 wherein the polylactone diol of the polylactone diol bis(allyl carbonate) (b)(ii) is the reaction product of a diol and a lactone;

the diol of the polylactone diol is selected from linear or branched aliphatic diols having from 2 to 20 carbon atoms, poly(C₂-C₄)alkylene glycols, cycloaliphatic diols having from 5 to 8 carbon atoms in the cyclic ring, hydrogenated bisphenols and mixtures thereof; and

the lactone of the polylactone diol is selected from at least one lactone having from 3 to 8 carbon atoms in the cyclic lactone ring.

10. The polymerizable composition of claim 9 wherein the diol of the polylactone diol is diethylene glycol, and the lactone of the polylactone diol is epsilon-caprolactone.

11. The polymerizable composition of claim 10 wherein the polylactone diol of said polylactone diol bis(allyl carbonate) has a number average molecular weight of from 400 to 600.

12. The polymerizable composition of claim 1 wherein said first allyl functional monomer is a polyol(allyl carbonate) monomer, and said polymerizable composition is prepared by a method comprising:

(a) preparing separately a first chloroformate intermediate of said first allyl functional monomer, and a second chloroformate intermediate of said second allyl functional monomer;

(b) forming a mixture of said first and second chloroformate intermediates; and

(c) reacting the chloroformate groups of said mixture of said first and second chloroformate intermediates with allyl alcohol, thereby forming said polymerizable composition.

20. The polymerizate of claim 1.

21. The polymerizate of claim 10.

23. A photochromic article comprising:

(a) the polymerizate of claim 1; and

(b) a photochromic amount of organic photochromic substance.

24. A photochromic article comprising:

(a) the polymerizate of claim 10; and

(b) a photochromic amount of organic photochromic substance.

25. The photochromic article of claim 24 wherein the organic photochromic substance is selected from the group consisting of spiro(indoline)naphthoxazines, spiro(indoline)benzoxazines, benzopyrans, naphthopyrans, chromenes, organo-metal dithizonates, fulgides and fulgimides and mixtures of such organic photochromic substances.

13. A polymerizable composition comprising:

(a) a first allyl functional monomer having at least two allyl groups, said first allyl functional monomer being selected such that a substantially completely cured polymerizate of said first allyl functional monomer has a 15 second Barcol 934 hardness of at least 40;

(b) a second allyl functional monomer, which is different from said first allyl functional monomer and is selected from,

(i) polyether diol bis(allyl carbonate);

(ii) polylactone diol bis(allyl carbonate); and

(iii) mixtures of (i) and (ii); and

(c) a third allyl functional monomer that is different than each of said first and second allyl functional monomers;

said third allyl functional monomer being represented by the following general formula,

14. The polymerizable composition of claim 13 wherein said first allyl functional monomer is present in said composition in an amount of from 25 percent by weight to 90 percent by weight, based on the total monomer weight of said composition;

said second allyl functional monomer is present in said composition in an amount of from 10 percent by weight to 60 percent by weight, based on the total monomer weight of said composition; and

said third allyl functional monomer is present in said composition in an amount of from 1 percent by weight to 50 percent by weight, based on the total monomer weight of said composition.

15. The polymerizable composition of claim 14 wherein R₁₅ is a residue of diethylene glycol.

16. The polymerizable composition of claim 13 wherein said first allyl functional monomer (a) is represented by the following general formula,

17. The polymerizable composition of claim 16 wherein the polylactone diol of the polylactone diol bis(allyl carbonate) (b)(ii) is the reaction product of a diol and a lactone;

the diol of the polylactone diol is selected from linear or branched aliphatic diols having from 2 to 20 carbon atoms, poly(C₂-C₄)alkylene glycols, cycloaliphatic diols having from 5 to 8 carbon atoms in the cyclic ring, hydrogenated bisphenols and mixtures thereof; and

the lactone of the polylactone diol is selected from at least one lactone having from 3 to 8 carbon atoms in the cyclic lactone ring.

18. The polymerizable composition of claim 17 wherein the diol of the polylactone diol is diethylene glycol, and the lactone of the polylactone diol is epsilon-caprolactone.

19. The polymerizable composition of claim 13 wherein said first allyl functional monomer is a polyol(allyl carbonate) monomer, and said polymerizable composition is prepared by a method comprising:

(a) preparing separately a first chloroformate intermediate of said first allyl functional monomer, a second chloroformate intermediate of said second allyl functional monomer, and a third chloroformate intermediate of said third allyl functional monomer;

(b) forming a mixture of said first, second and third chloroformate intermediates; and

(c) reacting the chloroformate groups of said mixture of said first, second and third chloroformate intermediates with allyl alcohol, thereby forming said polymerizable composition.

22. The polymerizate of claim 13.