Method for treating an object with a laser

• US 6,669,794 B1
• Filed: 09/06/2001
• Issued: 12/30/2003
• Est. Priority Date: 12/04/1998
• Status: Expired due to Fees

• Current Assignee: ETA SA Fabriques d'Ebauches
• Original Assignee: ETA SA Fabriques d'Ebauches
• Inventors: Bellouard, Yves, Clavel, Reymond, Bidaux, Jacques-Eric, Lenhert, Thomas
• Primary Examiner(s): WYSZOMIERSKI, GEORGE P
• Application Number:
  US09/857,437
• Time in Patent Office: 845 Days
• Field of Search: 148/402, 148/563, 148/565, 623/1.18
• US Class Current: 148/563
• CPC Class Codes: C22F 1/006 Resulting in heat recoverable alloys with a memory effect

Abstract

The invention concerns a method whereby at least a predefined zone (A) of the object (2) is irradiated with a laser beam (4) capable of heating said zone sufficiently, to a temperature less than the material melting point, to provoke a change in the microstructure (for example crystallisation or recrystallisation) of said zone, said zone being heated at a temperature and for a time interval not rendering the material amorphous. The invention is applicable for example to reversible actuators and grippers.

Claims

1. Method for treating an object made of a material capable of exhibiting a shape memory effect, but having an amorphous or work-hardened structure with no shape memory before said treating, this method being characterised by:

irradiating at least a pre-defined zone of this object by a laser beam able to heat this zone sufficiently, to a temperature lower than the melting temperature of the material, to cause, in said zone, a microstructure change selected from among a crystallisation, recrystallisation, secondary crystallisation, controlled formation of precipitates and annihilation of crystalline faults; and

heating said zone to a temperature and for a time which are not able to cause amorphisation of the material.

2. Method according to claim 1, wherein said irradiating of the zone is also used to cause permanent deformation of said zone allowing the object to be stressed.

3. Method according to claim 1, wherein, before or during, or after irradiation of the zone, the object is stressed by deforming said object.

4. Method according to claim 1, wherein the non irradiated part of the object is all in one piece.

5. Method according to claim 1, wherein the non irradiated part of the object includes at least two zones which are separated by the irradiated zone.

6. Method according to claim 1, wherein the object is a thin element, and further characterized by irradiating zones of this element, which are distributed over said element, by means of said laser beam in order to rigidify said element.

7. Method according to claim 1, wherein energy transmitted to the material by the laser is varied as a function of the position of the laser beam on the object.