Switchable volume hologram materials and devices
First Claim
1. A switchable wavelength filter for laser protection made by exposing an interference pattern inside a polymer-dispersed liquid crystal material, the polymer-dispersed liquid crystal material comprising, before exposure,:
- (a) a polymerizable monomer;
(b) a liquid crystal;
(c) a cross-linking monomer;
(d) a coinitiator; and
(e) a photoinitiator dye;
whereby the polymer-dispersed liquid crystal material is adapted to reflect radiation after exposure.
3 Assignments
0 Petitions
Accused Products
Abstract
A new photopolymerizable material allows single-step, fast recording of volume holograms with properties that can be electrically controlled. Polymer-dispersed liquid crystals (PDLCs) in accordance with the invention preferably comprise a homogeneous mixture of a nematic liquid crystal and a multifunctional pentaacrylate monomer, in combination with photoinitiator, coinitiator and cross-linking agent. Optionally, a surfactant such as octanoic acid may also be added. The PDLC material is exposed to coherent light to produce an interference pattern inside the material. Photopolymerization of the new PDLC material produces a hologram of clearly separated liquid crystal domains and cured polymer domains. Volume transmission gratings made is with the new PDLC material can be electrically switched between nearly 100% diffraction efficiency and nearly 0% diffraction efficiency. By increasing the frequency of the switching voltage, switching voltages in the range of 50 Vrms can be achieved. The optional use of surfactant allows low switching voltages at lower frequencies than without surfactant. In an alternative embodiment, a PDLC material in accordance with the invention can be utilized to form reflection gratings, including switchable reflection gratings. In still further embodiments, a PDLC material in accordance with the invention can be used to form switchable subwavelength gratings. By further processing, static transmission reflection, and subwavelength PDLC materials can be formed.
163 Citations
18 Claims
-
1. A switchable wavelength filter for laser protection made by exposing an interference pattern inside a polymer-dispersed liquid crystal material, the polymer-dispersed liquid crystal material comprising, before exposure,:
-
(a) a polymerizable monomer;
(b) a liquid crystal;
(c) a cross-linking monomer;
(d) a coinitiator; and
(e) a photoinitiator dye;
whereby the polymer-dispersed liquid crystal material is adapted to reflect radiation after exposure. - View Dependent Claims (2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18)
(a) the liquid crystal comprises 10-40% by total weight of the polymer-dispersed liquid crystal material;
(b) the cross-linking monomer comprises 5-15% by total weight of the polymer-dispersed liquid crystal material;
(c) the amount of coinitiator is 10(−
3) to 10(−
4) gram moles; and
(d) the amount of photoinitiator dye is 10(−
5) to 10(−
6) gram moles.
-
-
4. The switchable wavelength filter for laser protection of claim 1, wherein:
-
(a) the liquid crystal comprises 10-40% by total weight of the polymer-dispersed liquid crystal material;
(b) the cross-linking monomer comprises 10-18% by total weight of the polymer-dispersed liquid crystal material;
(c) the coinitiator comprises 2-3% by total weight of the polymer-dispersed liquid crystal material; and
(d) the photoinitiator dye comprises 0.2-0.4% by total weight of the polymer-dispersed liquid crystal material.
-
-
5. The switchable wavelength filter for laser protection according to claim 2, wherein the surfactant comprises about 6% by total weight of the polymer-dispersed liquid crystal material.
-
6. The switchable wavelength filter for laser protection according to claim 2, wherein the surfactant comprises about 5-10% by total weight of the polymer-dispersed liquid crystal material.
-
7. The switchable wavelength filter for laser protection according to claim 1, wherein the liquid crystal includes a mixture of cyano biphenyls.
-
8. The switchable wavelength filter for laser protection according to claim 1, wherein the cross linking monomer comprises N-vinylpyrrolidone.
-
9. The switchable wavelength filter for laser protection according to claim 1, wherein the coinitiator comprises N-phenylglycine.
-
10. The switchable wavelength filter for laser protection according to claim 1, wherein the photoinitiator dye comprises rose bengal ester.
-
11. The switchable wavelength filter for laser protection according to claim 2, wherein the surfactant comprises octanoic acid.
-
12. The switchable wavelength filter for laser protection of claim 1, wherein the polymerizable monomer comprises dipentarythritol hydroxypentaacrylate.
-
13. The switchable wavelength filter for laser protection according to claim 1, wherein the liquid crystal comprises 4′
- -n-pentyl-4-cyanobiphenyl.
-
14. The switchable wavelength filter for laser protection according to claim 1, wherein the polymer-dispersed liquid crystal material comprises 0.2% by weight to 0.4% by weight of a photoinitiator dye.
-
15. The switchable wavelength filter for laser protection according to claim 1, wherein the polymer-dispersed liquid crystal material comprises a photoinitiator dye comprising rose bengal sodium salt.
-
16. The switchable wavelength filter for laser protection according to claim 1, wherein the polymer-dispersed liquid crystal material comprises about 2% by weight to 3% by weight of a coinitiator.
-
17. The switchable wavelength filter for laser protection according to claim 1, wherein the polymer-dispersed liquid crystal material comprises a coinitiator comprising N-phenyglycine;
- and a photoinitiator dye comprising camphorquinone.
-
18. The switchable wavelength filter for laser protection according to claim 1, wherein the polymer-dispersed liquid crystal material comprises about 10% by weight to 18% by weight of a cross-linking monomer.
Specification