Process for the manufacturing of a decorative laminate, a decorative laminate obtained by the process and use thereof

• US 6,773,799 B1
• Filed: 12/30/1999
• Issued: 08/10/2004
• Est. Priority Date: 05/06/1997
• Status: Expired due to Term

• Current Assignee: Decorative Surfaces Holding AB
• Original Assignee: Decorative Surfaces Holding AB
• Inventors: Rasmusson, Dennis, Persson, Stefan, Andersson, Thord, Sjöstedt, Börje
• Primary Examiner(s): Jackson, Monique R.
• Application Number:
  US09/423,270
• Time in Patent Office: 1,685 Days
• Field of Search: 428/323, 428/535, 428/537.1, 428/326, 428/524, 428/530, 264/129, 264/109, 264/112, 156/307.4, 156/244.11, 156/62.2
• US Class Current: 428/323
• CPC Class Codes: B27N 3/26 characterised by using continuously acting presses having a heated press drum and an endless belt to compress the material between belt and drum
• CPC Class Codes: B27N 3/28 characterised by using extrusion presses
• CPC Class Codes: B27N 7/005 Coating boards, e.g. with a finishing or decorating layer
• CPC Class Codes: B30B 15/308 in a continuous manner, e.g. for roller presses, screw extrusion presses
• CPC Class Codes: B32B 21/02 the layer being formed of fibres, chips, or particles , e.g. MDF, HDF, OSB, chipboard, particle board, hardboard
• CPC Class Codes: B32B 2260/028 Paper layer
• CPC Class Codes: B32B 2260/046 Synthetic resin
• CPC Class Codes: B32B 2305/70 Scrap or recycled material
• CPC Class Codes: B32B 2307/558 Impact strength, toughness
• CPC Class Codes: B32B 2451/00 Decorative or ornamental articles wall paper B32B2607/02
• CPC Class Codes: B32B 27/04 as impregnant, bonding, or embedding substance not used
• CPC Class Codes: B32B 29/04 next to a particulate layer
• CPC Class Codes: B32B 3/06 for securing layers together; for attaching the product to another member, e.g. to a support , or to another product, e.g. groove/tongue, interlocking
• CPC Class Codes: B44C 5/0469 comprising a decorative sheet and a core formed by one or more resin impregnated sheets of paper
• CPC Class Codes: Y10T 428/25 Web or sheet containing structurally defined element or component and including a second component containing structurally defined particles
• CPC Class Codes: Y10T 428/253 Cellulosic [e.g., wood, paper, cork, rayon, etc.]
• CPC Class Codes: Y10T 428/31942 Of aldehyde or ketone condensation product
• CPC Class Codes: Y10T 428/31964 Paper
• CPC Class Codes: Y10T 428/31982 Wood or paper
• CPC Class Codes: Y10T 428/31989 Of wood

Abstract

A process for manufacturing a decorative mainly isometric thermosetting laminate (1) comprising an isometric core (2), a primary surface layer (10) and optionally a secondary surface layer (20). 85 parts by weight of preferably organic particles are mixed with 15-85 parts by weight of a thermosetting resin such as phenol-formaldehyde resin, melamine-formaldehyde resin, urea-formaldehyde resin or mixtures thereof under powerful kneading in an extruder sot hat friction heat forms. The thermosetting resin is hereby bonded to or impregnating the particles. The particles possibly bonded to one another are parted whereby an agglomerate of resin and particles is formed. The particle/resin mixture is then dried to a water content of below 10%. The dried particle/resin mixture is then evenly distributed and continuously or discontinuously compressed in one or more steps under heat and pressure so that the resin finally cures, whereby an isometric core (2) is formed. The core (2) is during or after the pressing provided with a primary (10) and optionally a secondary (20) surface layer. The invention also relates to a laminate obtained through the process and use thereof.

Claims

1. A process for manufacturing a decorative substantially isometric thermosetting laminate (1) comprising an isometric core (2), a primary surface layer (10) and optionally a secondary surface layer (20), comprising

i) A. mixing 85 parts by weight of particles, which particles have an average particle size of 5-3000 μ

m with 15-85 parts by weight of a thermosetting resin in the form of a powder, wherein the resin is selected from the group consisting of a phenol-formaldehyde resin, a melamine formaldehyde resin, a urea-formaldehyde resin and a mixture thereof, wherein the mixing takes place in an extruder;

B. kneading the mixture energetically so that friction heat is formed, which friction heat is not allowed to exceed 150°

C.; and

C. bonding the soft thermosetting resin to or impregnating the particles,

D. those particles that possibly are joined by the thermosetting resin are divided and an agglomerate of thermoplastic resin and particles is formed which agglomerate has an average particle size of 200-3000 μ

m and a resin content of 10-50% by weight;

ii) drying the particle/resin mixture to a water content below 10% by weight;

iii a) distributing the dried particle/resin mixture evenly on one member selected from the group consisting of a carrier (30);

a pressing belt (41) of a continuous laminate press (40); and

a press plate (51) of a discontinuous laminate press (50), and is thereafter continuously or discontinuously compressed at a temperature of 60-120°

C., and a pressure of 15-400 bars so that the particle/resin agglomerate flows out without completely curing the resin whereby a pre-fabricated isometric core (2) is obtained, that the pre-fabricated core is fed in between one member selected from the group consisting of the press belts (41) of a continuous laminate press (40) and a press plate (51) of a discontinuous laminate press (50) together with a primary surface layer (10), which is provided with a decorative layer, and optionally a secondary layer (20) and is thereafter continuously or discontinuously compressed at a temperature of 120-200°

C., and a pressure of 15-300 bar, so that the resin cures, whereby a decorative thermosetting laminate provided with an isometric core is obtained, or

b) drying the dried particle resin/mixture evenly on one member selected from the group consisting of a carrier (30), a pressing belt (41) of a continuous laminate press (40) and on a press plate (51) of a discontinuous laminate press (50) and is thereafter continuously or discontinuously compressed at a temperature of 120-200°

C., and a pressure of 15-300 bar, so that the resin cures, whereby an isometric core (2) is formed, and that the core (2) is provided with a primary surface layer (10) and optionally a secondary surface layer (20) simultaneously with or after the pressing.

2. A process according to claim 1 wherein the particles completely or partly consist of wood parts or fruit parts from plants.

3. A process according to claim 1 wherein the particles completely or partly consist of recycled material.

4. A process according to claim 1 wherein the particles completely or partly consist of lime.

5. A process according to claim 1 wherein the particles are dried to a water content below 10% by weight, before the mixing.

6. A process according to claim 1 wherein the dried particle/resin mixture is distributed such that the particle weight per unit area in any one part of the core does not exceed the particle weight per unit area in any other area by more than 10%.

7. A process according to claim 1 wherein the carrier (30) is formed by the primary surface layer (10) or the secondary surface layer (20).

8. A process according to claim 1 wherein the pressing process is initiated at a low initial pressure of the final pressure during which initial pressure the particle/resin mixture is allowed to flow as the resin softens due to the temperature.

9. A process according to claim 1 wherein the primary surface layer (10) consists of at least one or more decorative papers (12) one or more underlying base paper (14), impregnated with a thermosetting resin and one or more so-called overlay paper (11) placed on top and impregnated with melamine-formaldehyde resin or urea-formaldehyde resin, and optionally a diffusion preventing foil (13) placed closest to the core (2).

10. A process according to claim 9 wherein the diffusion preventing foil (13) consists of a metal or of a plastic material.

11. A process according to claim 1 wherein the secondary surface layer (20) consists of at least one or more base paper (21) impregnated with thermosetting resin.

12. A process according to claim 1 wherein the secondary surface layer (20) consists of at least one or more decorative paper (22) impregnated with thermosetting resin.

13. A process according to claim 1 wherein the secondary surface layer (20) consists of at least one diffusion preventing foil (23) placed closest to the core (2).

14. A process according to claim 13 wherein the diffusion preventing foil (23) consists of a metal or of a plastic material.

15. A process according to claim 10 comprising treating the surfaces of the diffusion preventing foil such that the adhesion to the laminate (1) is increased by surface enlargement or surface activation.

16. A process according to claim 10 wherein the diffusion preventing foil has a thickness of 5-2000 μ

m.

17. A process according to claim 16 wherein the diffusion preventing foil consists of a metal having a thickness of 5-200 μ

m.

18. A process according to claim 16 wherein the diffusion preventing foil (13 and 23) consists of a thermoplastic material having a thickness of 0.2-2 mm.

19. A process according to claim 10 wherein the diffusion preventing foil (13 and 23) has a thermal coefficient of expansion in the range of 15×

10<sup>−

6</sup>/K and 100×

10<sup>−

6</sup>/K.

20. A process according to claim 1 wherein the thermosetting laminate (1) is provided with three-dimensional functional parts.

21. A process according to claim 15 comprising treating the surfaces of the diffusion preventing foil by at least one coating selected from the group consisting a primer, micro-etched, blasted, corona treated, spark milled, brush plated, and electro-plated.

22. A process according to claim 1, wherein the particles in the mixing step are organic particles.

23. A process according to claim 1, wherein the particles in the mixing step have an average particle size of 5-200 μ

m.

24. A process according to claim 1, wherein the thermosetting particles form 22-37 parts by weight.

25. A process according to claim 1, wherein the friction heat in the kneading step is maintained below 110°

C.

26. A process according to claim 25, wherein the friction heat in the kneading step is maintained below 90°

C.

27. A process according to claim 1, wherein the agglomerate in the bonding step has a resin content of 20-30% by weight.

28. A process according to claim 1, wherein the first compressing in the distributing step (iii a) is at a temperature of 80-100°

C.

29. A process according to claim 1, wherein the first compressing in the distributing step (iii a) is at a pressure of 30-120 bar.

30. A process according to claim 1, wherein the second compressing in the distributing step (iii a) is at a temperature of 140-180°

C.

31. A process according to claim 1, wherein the second compressing in the distributing step (iii a) is at a pressure of 30-150 bar.

32. A process according to claim 1, wherein the compressing in the drying step (iii b) is at a temperature of 140-180°

C.

33. A process according to claim 1, wherein the compressing in the drying step (iii b) is at a pressure of 30-150 bar.

34. A process according to claim 3, wherein the recycled material is waste paper, cardboard or rejects from thermosetting laminate manufacturing.

35. A process according to claim 5, wherein the particles are dried to a water content below 6% by weight.

36. A process according to claim 8, wherein the initial pressure is 10-50% of the final pressure.

37. A process according to claim 10, wherein the metal is selected from the group consisting of aluminium, steel, copper and zinc.

38. A process according to claim 10, wherein the plastic material is at least one selected from the group consisting of polyethylene, polypropylene, polyalkylene terephthalate, acrylic polymer, polyvinyl chloride and fluorinated thermoplastic.

39. A process according to claim 11, wherein the thermosetting resin is at least one selected from the group consisting of melamine-formaldehyde resin and urea-formaldehyde resin.

40. A process according to claim 12, wherein the thermosetting resin is at least one selected from the group consisting of melamine-formaldehyde resin and urea-formaldehyde resin.

41. A process according to claim 14, wherein the metal is selected from the group consisting of as aluminium, steel, copper and zinc.

42. A process according to claim 14, wherein the plastic material is selected from the group consisting of polyethylene, polypropylene, polyalkylene-terephthalate, acryl, polyvinyl chloride and fluorinated thermoplastic.

43. A process according to claim 16, wherein the foil has a thickness of 10-1000 μ

m.

44. A process according to claim 17, wherein the foil consists of a metal having a thickness of 10-100 μ

m.

45. A process according to claim 18, wherein the foil consists of a thermoplastic material having a thickness of 0.3-1 mm.

46. A process according to claim 19 wherein the diffusion preventing foil has a thermal coefficient of expansion in the range of 15×

10<sup>−

6</sup>/K and 50×

10<sup>−

6</sup>/K.

47. A process according to claim 20, wherein the three-dimensional functional parts are at least one selected from the group consisting of a tenon, groove and a lattice structure.

48. A process according to claim 6 wherein the dried particle/resin mixture is distributed such that the particle weight per unit area in any one part of the core does not exceed the particle weight per unit area in any other area by more than 3%.

49. A process according to claim 1, wherein the particle/resin mixture is dried to a water content of less than 5% by weight.

50. A process according to claim 2, wherein the wood parts comprise at least one selected from the group consisting of saw dust, wood powder and finely chopped straw.

51. A process according to claim 2, wherein the fruit parts consist of a cereal in the form of a flour.

52. A process according to claim 51, wherein the flour is selected from the group consisting of corn, wheat and rice flour.

53. A process according to claim 9, wherein the at least 1 or more decorative papers comprise α

-cellulose.

54. The process according to claim 53, wherein the thermosetting resin impregnated into the α

-cellulose is one or more selected from the group consisting of melamine-formaldehyde resin and urea-formaldehyde resin.

55. A process according to claim 12, wherein the at least 1 or more decorative papers comprise α

-cellulose.

56. The process according to claim 55, wherein thermosetting resin impregnated into the α

-cellulose is one or more selected from the group consisting of melamine-formaldehyde resin and urea-formaldehyde resin.

57. A thermosetting laminate (1) made by the process of claim 1 wherein the thermosetting laminate (1) is mainly isometric with a difference in coefficient of expansion between the length and the cross direction of the laminate of less than 10%.

58. The thermosetting laminate (1) according to claim 57 wherein the thermosetting laminate (1) has a water absorption ability which is lower than 10% by weight after 100 h in water at 23°

C.

59. A thermosetting laminate according to claim 58, wherein the water absorption ability is lower than 6% by weight after 100 h in water at 23°

C.

60. The thermosetting laminate (1) according to claim 57 wherein the thermosetting laminate (1) has an impact resistance of greater than 2 kJ/m².

61. A thermosetting laminate according to claim 60, wherein the thermosetting laminate has an impact resistance greater than 3 kJ/m².

62. The thermosetting laminate (1) according to claim 57 wherein the primary surface layer (10) includes at least one thermosetting resin impregnated paper which is coated with hard particles with an average size of 1-100 μ

m.

63. A thermosetting laminate according to claim 62, wherein the impregnated paper is the uppermost paper.

64. A thermosetting laminate according to claim 62, wherein the hard particles comprise at least one selected from the group consisting of silicon oxide, aluminium oxide and silicon carbide.

65. A thermosetting laminate according to claim 62, wherein the hard particles have an average particle size of around 5-60 μ

m.

66. A process of using a thermosetting laminate (1) according to claim 57, comprising providing the thermosetting laminate in a form selected from the group consisting of a covering material on floors, inner walls, ceilings, table tops, work tops, facade boarding, roofs, and doors in dry and wet spaces as well as in wet spaces.