Sealable sterilizing packaging material

• US 6,808,691 B1
• Filed: 08/08/2000
• Issued: 10/26/2004
• Est. Priority Date: 10/12/1998
• Status: Expired due to Term

• Current Assignee: Arjowiggins Sas (UFK Management Holding GmbH)
• Original Assignee: Arjo Wiggins
• Inventors: Paris-Jolly, Agnes, Herve, Philippe
• Primary Examiner(s): JASTRZAB, KRISANNE MARIE
• Application Number:
  US09/555,525
• Time in Patent Office: 1,540 Days
• Field of Search: 531/281, 534/53, 422/294, 422/297, 422/300, 206/363, 206/439, 206/329
• US Class Current: 422/294
• CPC Class Codes: A61B 50/31 Carrying cases or bags, e.g. doctors' bags
• CPC Class Codes: A61L 2/26 Accessories or devices or components used for biocidal treatment
• CPC Class Codes: A61L 2202/18 Aseptic storing means
• CPC Class Codes: A61L 2202/24 Medical instruments, e.g. endoscopes, catheters, sharps

Abstract

A sealable sterilising material for packaging medical devices requiring sterilization, has an average burst strength not less than 200 kPa measured according to ISO 2758 standard, an average tear strength not less than 300 mN measured according to the European standard 21974, an average impact strength not less than 0.4 J measured according to the ASTM standard and a bacterial filtering efficiency (BFE) not less than 85%, with a basic weight ranging between 40 and 250 g/m², preferably between 90 and 250 g/m², measured according to the ISO 536 standard and includes at least two sterilising packaging sheets (F1) and (F2), one of them at least being sealable directly or after being coated with a sealing product. The sheets are bound irreversibly together by one of their surfaces. The invention also concerns a package made from the material.

Claims

1. Sealable sterilizing packaging material for medical devices that have to be sterilized, having a mean burst strength not less than 200 kPa measured according to the ISO 2758 standard, a mean tear strength not less than 300 mN measured according to the European Standard EN 21974, a mean impact strength not less than 0.4 J measured according to the standard ASTM D 3420 and a bacterial filtering efficiency BFE not less than 85%, having a grammage ranging between 40 and 250 g/m²measured according to the ISO 536 standard and comprising at least two sterilizing packaging sheets (F1) and (F2), at least one of the sheets being sealable directly or after being coated with a sealing product, the said sheets being irreversibly bonded together via one of their sides.

2. Material according to claim 1, characterized in that the two sheets of sterilizing packaging (F1) and (F2) are bonded together by bonding points such that the said bonding points are in a discrete form at the bonding interface of the sheets.

3. Material according to claim 1, characterized in that the discrete bonding points are uniformly distributed at the interface of the sheets.

4. Material according to claim 1, characterized in that the sheets (F1) and (F2) are bonded together by an adhesive.

5. Material according to claim 4, characterized in that the adhesive is chosen from pressure-sensitive adhesives.

6. Material according to claim 4, characterized in that the adhesive is chosen from hot-melt adhesives, also called hot-melts.

7. Material according to claim 4, characterized in that the adhesive is a self-sealing adhesive.

8. Material according to claim 4, characterized in that the adhesive is a porous adhesive.

9. Material according to claim 4, characterized in that the amount of adhesive deposited ranges between 1 and 20 g/m².

10. Material according to claim 4, characterized in that the adhesive is deposited by halftone gravure printing.

11. Material according to claim 1, characterized in that one of the sheets (F1) is sealable directly or after it has been coated with a sealing product and the other sheet (F2) has a bacterial filtering efficiency BFE not less than that of the sheet (F1) and in that this bacterial filtering efficiency BFE ranges between 80 and 100%.

12. Material according to claim 1, characterized in that the sheet (F1) is a paper sheet and in that it comprises:

between 5 and 100 parts by weight of cellulose fibres, the cellulose fibers optionally being rayon fibres resulting from sodium hydroxide treatment of viscose or regenerated cellulose fibres in solvent medium;

between 0 and 95 parts by weight of synthetic fibres, the sum of the cellulose fibre parts and the synthetic fibre parts making 100;

between 0 and 5% of a wet-strength agent by dry weight of the total composition of the sheet;

between 0 and 40% of a cohesion agent by dry weight of the total composition of the sheet.

13. Material according to claim 1, characterized in that the sheet (F2) is a paper sheet and in that it comprises:

between 90 and 100 parts by weight of cellulose fibres, the cellulose fibers optionally being rayon fibres resulting from sodium hydroxide treatment of viscose or regenerated cellulose fibres in solvent medium;

between 0 and 10 parts by weight of synthetic fibres, the sum of the cellulose fibre parts and synthetic fibre parts making 100;

between 0 and 5% of a wet-strength agent by dry weight of the total composition of the sheet;

between 0 and 40% of a cohesion agent by dry weight of the total composition of the sheet.

14. Material according to claim 12, characterized in that the synthetic fibres are chosen from fibres homopolymers or copolymers of polyolefins, of polyester, of polyamide.

15. Material according to claim 12, characterized in that the synthetic fibres have a mean length ranging between 1 and 30 mm and a mean linear density ranging between 0.5 and 5 dtex.

16. Material according to claim 12, characterized in that the cohesion agent is chosen from starches, polyvinyl alcohols, acrylicoracrylate polymers.

17. Material according to claim 12, characterized in that the cohesion agent is an adhesive selected from the group consisting of pressure sensitive adhesives, hot-melt adhesives, self-sealing adhesive, natural rubber adhesive, and porous adhesive.

18. Material according to claim 1, characterized in that said material is covered on one of its sides with a sealing adhesive uniformly distributed either continuously over its entire surface or in patterns of grids or zones.

19. Sealable sterilizing package for medical devices that have to be sterilized, characterized in that said package comprises said sterilizing material according to claim 1 configured as a package.

20. Package according to claim 11, characterized in that the sheet (F2) having the greater bacterial filtering efficiency BFE is located on the outside of the package.

21. Package according to claim 19, characterized in that said package consists of the said sterilizing material and a film of gas-impermeable thermoplastic material which is sealed against the said material over at least part of its perimeter.

22. Package according to claim 19, characterized in that it consists of the said sterilizing material sealed against itself or a sheet of paper coated with a sealing product such as a layer of extruded polyethylene or of poly (vinyl acetate).

23. Package according to claim 19, characterized in that it consists of a rigid container and of a cover formed by the said sterilizing material.

24. The packaging material of claim 1 which has a grammage between 90 and 250 gm².

25. The packaging material of claim 7 wherein said self-sealing adhesive is a natural rubber adhesive.

26. The packaging material of claim 9 wherein the amount of adhesive deposited ranges between 5 and 10 g/m².