Silicone pressure sensitive adhesive composition

• US 6,890,601 B2
• Filed: 12/10/2002
• Issued: 05/10/2005
• Est. Priority Date: 06/23/2000
• Status: Expired due to Term

• Current Assignee: General Electric Company
• Original Assignee: General Electric Company
• Inventors: Lin, Shaow B., Wengrovius, Jeffrey H., Traver, Frank J., Griswold, Roy
• Primary Examiner(s): Moore, Margaret G.
• Assistant Examiner(s): Zimmer, Marc S.
• Application Number:
  US10/315,386
• Publication Number:
  US 20030166818A1
• Time in Patent Office: 882 Days
• Field of Search: 525/477, 528/34, 528/12, 528/14, 528/21, 428/447, 427/387, 156/329
• US Class Current: 427/387
• CPC Class Codes: C08L 2666/14 Macromolecular compounds according to C08L59/00 - C08L87/00; Derivatives thereof
• CPC Class Codes: C08L 2666/44 Silicon-containing compounds
• CPC Class Codes: C08L 83/00 Compositions of macromolecular compounds obtained by reactions forming in the main chain of the macromolecule a linkage containing silicon with or without sulfur, nitrogen, oxygen or carbon only; Compositions of derivatives of such polymers
• CPC Class Codes: C09J 183/04 Polysiloxanes
• CPC Class Codes: Y10T 428/31663 As siloxane, silicone or silane

Abstract

A silicone pressure sensitive adhesive composition containing the condensation product of a silanol-functional silicone resin, wherein the resin contains M structural units according to the formula R₃SiO_1/2, wherein R is a monovalent hydrocarbon radical, and Q structural units according to the formula SiO_4/2 in a ratio of M units to Q units of less than 1.1:1, a silanol-functional polydiorganosiloxane gum, and a crosslinker exhibits high tack and high lap shear strength.

Claims

1. A method for providing a pressure sensitive adhesive composition, comprising condensing, at an elevated temperature in the presence of a base catalysts a silanol-functional silicone resin, said resin comprising M structural units according to the formula R¹₃SiO_1/2, wherein each R¹ is independently hydroxy or a monovalent hydrocarbon radical, and Q structural units according to the formula SiO_4/2 in a ratio of M units to Q units of less than 1.1:

1, a silanol-functional polydiorganosiloxane gum and a crosslinker selected from the group consisting of alkoxysilane and poly(alkoxysilane).

2. The method of claim 1, wherein the elevated temperature is from about 110 to 130°

C.

3. A method for providing a pressure sensitive adhesive composition, comprising condensing, at an elevated temperature in the presence of a base catalyst, a silanol-functional silicone resin, said resin comprising M structural units according to the formula R¹₃SiO_1/2, wherein each R¹ is independently hydroxy or a monovalent hydrocarbon radical, and Q structural units according to the formula SiO_4/2 in a ratio of M units to Q units of less than 1.1:

1;

a silanol-functional polydiorganosiloxane gum and a crosslinker comprising;

(a) heating a mixture of the resin, gum, crosslinker, base catalyst and an organic solvent to a first elevated temperature to begin condensation of the resin, gum and crosslinker,

(b) adding a molar excess, based on moles of alkoxy groups of the resin, gum and crosslinker of the mixture of step (a), of water to the mixture of step (a),

(c) heating the mixture of step (b), to allow hydrolysis of any remaining alkoxy groups, and

(d) heating the mixture of step (c) to a second elevated temperature from about 110 to 130°

C. to drive condensation of the resin, gum and crosslinker toward completion.

4. The method of claim 3, wherein the mixture of step (a) is heated to a first elevated temperature of from 60 to 80°

C. for a time period of from 2 to 4 hours prior to step (b).

5. A method for providing a pressure sensitive adhesive composition, comprising condensing, at an elevated temperature in the presence of a base catalyst, a silanol-functional silicone resin, said resin comprising M structural units according to the formula R¹₃SiO_1/2, wherein each R¹ is independently hydroxy or a monovalent hydrocarbon radical, and Q structural units according to the formula SiO_4/2 in a ratio of M units to Q units of less than 1.1:

1, a silanol-functional polydiorganosiloxane gum, a crosslinker selected from the group consisting of alkoxysilane and poly(alkoxysiloxane), and water.

6. The method of claim 5, wherein the elevated temperature is from about 110 to 130°

C.

7. A method for making an article, comprising applying a layer of a silicone composition on at least a portion of at least one surface of a substrate, said silicone composition comprising the condensation reaction product of a silanol-functional silicone resin, said resin comprising M structural units according to the R¹₃SiO_1/2, wherein each R¹ is independently hydroxy or a monovalent hydrocarbon radical, and Q structural units according to the formula SiO_4/2 in a ratio of M units to Q units of less than 1.1:

1, a silanol-functional polydiorganosiloxane gum and a crosslinker selected from the group consisting of alkoxysilane and poly(alkoxysilane).

8. The method of claim 7, comprising:

(a) heating a mixture of the resin, gum, crosslinker, base catalyst and an organic solvent to a first elevated temperature to begin condensation of the resin, gum and crosslinker,

(b) adding a molar excess, based on moles of alkoxy groups of the resin, gum and crosslinker of the mixture of step (a), of water to the mixture of step (a),

(c) heating the mixture of step (b) to allow hydrolysis of any remaining alkoxy groups, and

(d) heating the mixture of step (c) to a second elevated temperature from about 110 to 130°

C. to drive condensation of the resin, gum and crosslinker toward completion.

9. The method of claim 7, wherein the mixture of step (a) is heated to a first elevated temperature of from 60 to 80°

C. for a time period of from 2 to 4 hours prior to step (b).

10. The method of claim 7, wherein the mixture of step (d) is heated to a second elevated temperature of from about 110 to 130°

C. for a time period of from about 1 to 3 hours.

11. A method for making an article, comprising applying a layer of a silicone composition on at least a portion of at least one surface of a substrate, said silicone composition comprising the condensation reaction product of a silanol-functional silicone resin, said resin comprising M structural units according to the R¹₃SiO_1/2, wherein each R¹ is independently hydroxy or a monovalent hydrocarbon radical, and Q structural units according to the formula SiO_4/2 in a ratio of M units to Q units of less than 1.1:

1, a silanol-functional polydiorganosiloxane gum, a crosslinker selected from the group consisting of alkoxysilane and poly(alkoxysilane) and water.