Polymer-based orthopedic screw and driver system with increased insertion torque tolerance and associated method for making and using same

• US 6,921,402 B2
• Filed: 12/27/2001
• Issued: 07/26/2005
• Est. Priority Date: 12/27/2001
• Status: Active Grant

• Current Assignee: Ethicon Incorporated (Johnson & Johnson)
• Original Assignee: Ethicon Incorporated (Johnson & Johnson)
• Inventors: Contiliano, Joseph H., Yuan, J. Jenny, Tenhuisen, Kevor S.
• Primary Examiner(s): Philogene, Pedro
• Application Number:
  US10/033,543
• Publication Number:
  US 20030125744A1
• Time in Patent Office: 1,307 Days
• Field of Search: 606/73, 606/104, 606/72, 606/76, 606/77, 606/74, 606/75, 606/232, 248/650, 248/656, 248/188.4, 294/47, 738/613.55, 228/135
• US Class Current: 606/916
• CPC Class Codes: A61B 17/864 hollow, e.g. with socket or cannulated
• CPC Class Codes: A61B 17/8645 Headless screws, e.g. ligament interference screws
• CPC Class Codes: A61B 17/866 Material or manufacture
• CPC Class Codes: A61B 17/8875 Screwdrivers, spanners or wrenches
• CPC Class Codes: A61B 2017/00004 (bio)absorbable, (bio)resorbable, resorptive for implantable prostheses A61F2210/0004
• CPC Class Codes: A61F 2/0811 Fixation devices for tendons or ligaments
• CPC Class Codes: Y10S 606/916 Tool for installing or removing orthopedic fastener

Abstract

An orthopedic screw with an internal bore and mating driver has a bioabsorbable polymer component. To increase the torque tolerance of the screw and to minimize the likelihood of the driver stripping inside the bore of the screw, the screw and driver are heat treated together to shrink fit the screw onto the driver thereby increasing the driver-to-screw contact and distributing the loading force over a greater area to protect against material failure. The heat treatment involves heating the screw to an elevated temperature and holding that temperature for a period to promote stress relaxation and/or crystallization of the material.

Claims

1. A method for increasing driver-to-screw contact in a medical screw and driver system having an elongated screw formed at least partially from a bioabsorbable material and having external threads and an internal bore with a non-circular cross-sectional shape extending through at least a portion of the length of said screw and an elongated driver having a non-circular cross-sectional shape approximating the cross-sectional shape of said bore, said driver being insertable into said bore and being matingly received therein to transfer rotational motion of said driver to said screw, said method comprising the steps of:

(A) inserting said driver into said bore of said screw;

(B) heating said screw

(C) allowing said screw to cool, said steps (B) and (C) inducing said screw to shrink whereby said bore molds itself to said driver such that the cross-sectional shape of said bore is closely mated to the cross-sectional shape of said driver; and

(D) withdrawing said driver from said bore without altering said cross-sectional shape of said bore.

2. The method of claim 1, wherein said screw is heated in said step (B) to a temperature at least equal to the glass transition temperature of said screw.

3. The method of claim 1, further comprising the step (B2) of maintaining said screw at an elevated temperature after said step (B) and prior to said step (C).

4. The method of claim 3, wherein said driver is heated simultaneously with said screw during said step (B).

5. The method of claim 3, wherein said steps (B), (B2) and (C) result in the relaxation of the internal stress of said screw.

6. The method of claim 3, wherein said steps (B), (B2) and (C) result in a partial crystallization of said screw.

7. The method of claim 3, wherein said screw is composed of 15/85 (vol/vol) blend of TCP/PLA.

8. The method of claim 7 wherein said step (B) includes the step of raising the temperature of said screw from room temperature to said elevated temperature, said elevated temperature being about 70°

C. and said step (B2) includes the step of holding said elevated temperature of said screw at about 70°

C. for about 4 hours.

9. The method of claim 7 wherein said step (B) includes raising the temperature of said screw from room temperature to said elevated temperature, said elevated temperature being about 70°

C. and said step (B2) includes holding said elevated temperature of said screw at about 70°

C. for about 4 hours, and further comprising the steps (B3) of heating the screw to a temperature of 100°

C. and (B4) maintaining the 100°

C. temperature for 8 hours before said step (C).

10. The method of claim 2, wherein said screw is heated during said step (B) to a temperature of about 5°

C. to 15°

C. above the glass transition temperature of said screw.

11. The method of claim 1, further comprising the step (E) of replacing said screw on said driver in the same relative orientation that said screw and said driver were in when said step (B) was conducted.