Process and apparatus for highway marking

• US 6,969,214 B2
• Filed: 06/08/2004
• Issued: 11/29/2005
• Est. Priority Date: 02/06/2004
• Status: Expired due to Fees

• Current Assignee: GJL Patents, LLC
• Original Assignee: George Jay Lichtblau
• Inventors: Lichtblau, George Jay
• Primary Examiner(s): PECHHOLD, ALEXANDRA K
• Application Number:
  US10/863,651
• Publication Number:
  US 20050175411A1
• Time in Patent Office: 539 Days
• Field of Search: 404 12- 16, 404/72, 404/75, 404/79, 404/101, 404/108, 404/111, 404/84.05, 404/77, 427/422, 427/426, 427/427, 427/201, 427/287, 427/140, 427/142, 264/30, 264/31, 264/82, 523/172
• US Class Current: 404/79
• CPC Class Codes: E01C 23/206 by applying fusible particulate material to the surface, e.g. by means of a gaseous stream

Abstract

A process and apparatus for forming a coherent refractory mass on the surface of a road wherein one or more non-combustible materials are mixed with one or more metallic combustible powders and an oxidizer, igniting the mixture so that the combustible metallic particles react in an exothermic manner with the oxidizer and release sufficient heat to form a coherent mass under the action of the heat of combustion and projecting this mass against the surface of the road so that the mass adheres durably to the surface of the road.

Claims

1. A process for forming a coherent refractory mass on the surface of a road comprising the steps of:

mixing one or more non-combustible materials with one or more metallic combustible powders and an oxidizer;

igniting the mixture in a combustion chamber so that combustible particles react in an exothermic manner with the oxidizer inside the combustion chamber and release sufficient heat to form a high temperature coherent refractory mass under the action of the heat of combustion; and

projecting said high temperature mass from the combustion chamber onto the surface of the road so that the mass adheres durably to the surface of the road.

2. The process of claim 1 wherein the non-combustible material is selected from the group consisting of titanium dioxide, aluminum oxide, chromium oxide, silicon dioxide, magnesium oxide, iron oxide, crushed colored glass, or a mixture of two or more thereof;

and

and wherein the combustible powder is selected from the group consisting of aluminum, silicon, zinc, magnesium, zirconium, and chromium or a mixture of two or more thereof.

3. The process of claim 1 wherein the oxidizer is selected from the group consisting of air, oxygen, ammonium perchlorate, ammonium nitrate, potassium perchlorate, potassium nitrate, sodium perchlorate, sodium nitrate, potassium chlorate and sodium chlorate or a mixture of two or more thereof.

4. The process of claim 1 wherein the non-combustible material is chromium oxide produced from refused grain brick.

5. The process of claim 1 wherein the non-combustible material is refused grain brick known commercially as CORHART RFG or CORHART 104 Grades.

6. The process of claim 1 wherein the non-combustible material is magnesite regenerate.

7. The process of claim 1 wherein the non-combustible material is CORHART-ZAC refractory material.

8. The process of claim 1 wherein the non-combustible material is Al₂O₃-/Bauxite-Regenerate.

9. The process of claim 1 wherein the oxidizer contains an anti-caking or flow agent.

10. The process of claim 9 wherein the flow agent is TCP (Tricalcium Phosphate).

11. The process of claim 1 wherein Iron Oxide (Fe₂O₃) is used as a catalyst in the mixture.

12. The process of claim 1 wherein the mixing step includes introducing a coloring material to the mixture which when heated in the presence of the other materials causes the color of the refractory mass to be a predetermined color.

13. The process of claim 12 wherein the color is white, yellow, red, or blue.

14. The process of claim 12 wherein the coloring material is tungsten, zirconium, or iron oxide (Fe₂O₃).

15. The process of claim 12 wherein the coloring material is crushed colored glass.

16. The process of claim 1 including the step of supplying oxygen to the combustion chamber to assist in the burning of the one or more metallic combustible powders.

17. The process of claim 1 wherein the mixing step is accomplished in the combustion chamber.

18. The process of claim 1 wherein the mixing step is accomplished prior to entry of the mixture into the combustion chamber.

19. The process of claim 1 including the step of preheating the surface of the road prior to projection of the refractory mass onto the surface of the road.

20. The process of claim 1 including the step of adding retroreflective beads to the refractory mass prior to projecting the mass onto the surface of the road.

21. The process of claim 1 including the step of depositing retroreflective beads upon the refractory mass after the mass has been projected onto the road surface.

22. The process of claim 1 including the step of controlling the rate of deposition of the refractory mass such that the mass projected upon the road surface has a substantially uniform thickness.

23. The process of claim 20 wherein the retroreflective beads added to the mixture are softened by the heat of reaction to cause the beads to adhere durably to the surface of the road.