Drawn gel-spun polyethylene yarns and process for drawing

• US 6,969,553 B1
• Filed: 09/03/2004
• Issued: 11/29/2005
• Est. Priority Date: 09/03/2004
• Status: Active Grant

• Current Assignee: Honeywell International Inc.
• Original Assignee: Honeywell International Inc.
• Inventors: Zhou, Qiang, Tam, Thomas Yiu-Tai, Tan, Chok B., Arnett, Charles R. Jr.
• Primary Examiner(s): EDWARDS, NEWTON O
• Application Number:
  US10/934,675
• Time in Patent Office: 452 Days
• Field of Search: 428/364, 428/394
• US Class Current: 428/364
• CPC Class Codes: D01F 6/04 from polyolefins
• CPC Class Codes: Y10T 428/29 Coated or structually defined flake, particle, cell, strand, strand portion, rod, filament, macroscopic fiber or mass thereof
• CPC Class Codes: Y10T 428/2913 Rod, strand, filament or fiber
• CPC Class Codes: Y10T 428/2967 Synthetic resin or polymer

Abstract

Gel-spun multi-filament polyethylene yarns possessing a high degree of molecular and crystalline order, and to the drawing methods by which they are produced. The drawn yarns are useful in impact absorption and ballistic resistance for body armor, helmets, breast plates, helicopter seats, spall shields, and other applications; composite sports equipment such as kayaks, canoes, bicycles and boats; and in fishing line, sails, ropes, sutures and fabrics.

Claims

1. A polyethylene multi-filament yarn comprising a polyethylene having an intrinsic viscosity in decalin at 135°

C. of from about 5 dl/g to 35 dl/g, fewer than about two methyl groups per thousand carbon atoms, and less than about 2 wt. % of other constituents, said multi-filament yarn having a tenacity of at least 17 g/d as measured by ASTM D2256-02, wherein filaments of said yarn have a peak value of the ordered-sequence length distribution function, F(L), as determined at 23°

C. from the low frequency Raman band associated with the longitudinal acoustic mode (LAM-1), at a straight chain segment length L of at least 40 nanometers.

2. The polyethylene multi-filament yarn of claim 1, wherein the filaments have a peak value at a straight chain segment length L of at least 45 nanometers.

3. The polyethylene multi-filament yarn of claim 1, wherein the filaments have a peak value at a straight chain segment length L of at least 50 nanometers.

4. The polyethylene multi-filament yarn of claim 1, wherein the filaments have a peak value at a straight chain segment length L of at least 55 nanometers.

5. The polyethylene multi-filament yarn of claim 1, wherein the filaments have a peak value at a straight chain segment length L of from 50 to 150 nanometers.