Process for creating a durable EMI/RFI shield between two or more structural surfaces and shield formed therefrom

• US 7,063,767 B1
• Filed: 02/07/2003
• Issued: 06/20/2006
• Est. Priority Date: 02/08/2002
• Status: Expired due to Fees

• Current Assignee: Deborah S. Tyson, Kenneth E. Tyson
• Original Assignee: Proteus Technical Solutions, Inc.
• Inventors: Marzan, Theodore, Tyson, Deborah S., Walker, Ronald B., Tyson, Kenneth E.
• Primary Examiner(s): Ngo, Hung V.
• Application Number:
  US10/360,528
• Time in Patent Office: 1,229 Days
• Field of Search: 174/35.R, 174/35.GC, 174/35.MS, 361/816, 361/818, 156/304.3
• US Class Current: 156/304.3
• CPC Class Codes: H05K 9/0088 comprising a plurality of shielding layers; combining different shielding material structure

Abstract

A method for producing a durable electromagnetic and radio frequency interference shield between two or more structural members of a wall or enclosure and a shielded shelter produced using the method. In one embodiment, joints between structural members are preferably filled with an electrically conductive filler. A base coat of a metal spray that adheres well to the filler and structural member is then applied. At least one layer of a metal spray with magnetic field attenuation properties such as steel, and at least one layer of a metal spray that has plane wave attenuation properties such as tin are applied to the base coat. Optionally, a coat of protective or conductive paint is then applied to the top surface of the metal spray layers. An enclosure with shielded joints according to the present invention has superior shielding capability and durability over the art.

Claims

1. A method for creating an EMI/RFI shield between two or more adjacent metal surfaces, comprising:

bridging adjacent metal surfaces using a metal spray material;

cleaning said adjacent metal surfaces prior to applying said metal spray material;

filling irregularities between adjacent metal surfaces with an adhesive material having conductive properties after said cleaning step.

2. A method as recited in claim 1, further comprising:

minimizing flexure in the bridge of said metal spray material.

3. A method for creating an electromagnetic interference EMI/RFI shield between two or more adjacent metal surfaces, comprising:

cleaning adjacent metal surfaces;

filling irregularities between adjacent metal surfaces with an adhesive material having conductive properties; and

applying a coating of metal spray material to said adjacent metal surfaces.

4. A method for providing a durable EMI/RFI shield between structural members, comprising:

filling seams between structural members with a filler;

depositing a plurality of layers of a metal having magnetic field attenuation characteristics over said structural member and said seams; and

depositing a plurality of layers of a metal having plane wave attenuation characteristics over said structural member and said seams and said deposited metal layer.

5. A method as recited in claim 4, wherein said plurality of layers of metal having plane wave attenuation characteristics are deposited on said structural member prior to the deposition of said plurality of layers of metal having magnetic field attenuation characteristics.

6. A method as recited in claim 4, wherein said layers of metal having magnetic field attenuation characteristics alternate with said layers of a metal having plane wave attenuation characteristics.

7. A method as recited in claim 4, wherein said filler comprises electrically conductive filler.

8. A method as recited in claim 7, wherein said electrically conductive filler comprises a metal particulate impregnated epoxy.

9. A method as recited in claim 8, wherein said metal particulates of said metal particulate impregnated epoxy comprise particulates of at least two different metals.

10. A method as recited in claim 4, further comprising;

applying a coating of paint to a top layer of deposited metal.

11. A method as recited in claim 10, wherein said coating of paint comprises a conductive paint.

12. A method as recited in claim 10, wherein said coating of paint comprises an elastomeric coating.

13. A method for providing an EMI/RFI shield, comprising:

providing a base support layer;

applying a base coat of a metal spray to said base support layer;

applying at least one coat of a first conductive metal spray to said base coat, said metal spray having magnetic field attenuation characteristics; and

applying at least one coat of a second conductive metal spray to said first coat, said metal spray having plane wave attenuation characteristics.

14. A method as recited in claim 13, further comprising the step:

filling seams and surface irregularities of said base support layer with an electrically conductive filler.

15. A method as recited in claim 14, further comprising:

smoothing the surface of said conductive filler; and

cleaning said surface of conductive filler with a solvent.

16. A method as recited in claim 14, wherein said electrically conductive filler comprises a metal particulate impregnated epoxy.

17. A method as recited in claim 13, wherein said base coat of metal spray comprises molybdenum applied a thickness of between approximately 2 millimeters to approximately 3 millimeters.

18. A method as recited in claim 13, wherein said base coat of metal spray comprises an alloy of molybdenum applied to a thickness of between approximately 2 millimeters to approximately 3 millimeters.

19. A method as recited in claim 13, wherein said base coat of metal spray comprises an alloy of nickel.

20. A method as recited in claim 13, wherein said coat of a first conductive metal spray comprises steel metal spray applied to a thickness of between approximately 2 millimeters to approximately 10 millimeters.

21. A method as recited in claim 13, wherein said second coat of conductive metal spray comprises approximately 99% pure tin applied to a thickness of between approximately 2 millimeters to approximately 80 millimeters.

22. A method as recited in claim 13, wherein said second coat of conductive metal spray comprises tin and zinc metal spray having an 8:

2 ratio of tin to zinc applied to a thickness of between approximately 2 millimeters to approximately 80 millimeters.

23. A method as recited in claim 13, further comprising:

applying a foundation coat of a conductive metal spray to said base coat prior to applying said first conductive metal spray.

24. A method as recited in claim 13, wherein said foundation coat of conductive metal spray comprises approximately 99% pure tin applied to a thickness of between approximately 2 millimeters to approximately 10 millimeters.

25. A method as recited in claim 13, wherein said foundation coat of conductive metal spray comprises tin and zinc metal spray having an approximate 8:

2 ratio of tin to zinc applied to a thickness of between approximately 2 millimeters to approximately 10 millimeters.

26. A method as recited in claim 23, wherein said coat of a first conductive metal spray comprises steel metal spray with a thickness of between approximately 2 millimeters to approximately 10 millimeters.

27. A method as recited in claim 23, wherein said coat of second conductive metal spray comprises tin applied to a thickness of between approximately 2 millimeters to approximately 80 millimeters.

28. A method as recited in claim 23, wherein said coat of a second conductive metal spray comprises tin and zinc metal spray having an approximate 8:

2 ratio of tin to zinc applied to a thickness of between approximately 2 millimeters to approximately 80 millimeters.