Methods of surface modification of a flexible substrate to enhance cell adhesion

• US 7,198,855 B2
• Filed: 09/12/2003
• Issued: 04/03/2007
• Est. Priority Date: 09/12/2003
• Status: Expired due to Term

• Current Assignee: Becton, Dickinson & Co, North Carolina State University (University of North Carolina System)
• Original Assignee: Becton, Dickinson & Co, North Carolina State University (University of North Carolina System)
• Inventors: Chaney, Bryce, Liebmann-Vinson, Andrea, Efimenko, Kirill, Genzer, Jan
• Primary Examiner(s): Feely; Michael J.
• Application Number:
  US10/660,760
• Publication Number:
  US 20050058842A1
• Time in Patent Office: 1,299 Days
• Field of Search: None
• US Class Current: 428/447
• CPC Class Codes: B05D 1/185 applying monomolecular layers B05D1/204 takes precedence
• CPC Class Codes: B05D 2201/00 Polymeric substrate or laminate
• CPC Class Codes: B05D 3/12 by mechanical means
• CPC Class Codes: B82Y 30/00 Nanotechnology for materials or surface science, e.g. nanocomposites
• CPC Class Codes: C12M 25/14 Scaffolds; Matrices in general C12N5/0068
• CPC Class Codes: C12N 2533/30 Synthetic polymers
• CPC Class Codes: C12N 2533/50 Proteins
• CPC Class Codes: C12N 5/0068 General culture methods using substrates for specific animal cell type C12N5/06
• CPC Class Codes: Y10T 428/31663 As siloxane, silicone or silane

Abstract

The present invention provides methods of producing a surface with enhanced cell-adhesive properties comprising applying a stress to a polymeric matrix. The strained matrix is then modified by grafting a self-assembled monolayer onto the strained matrix, with the self-assembled monolayer comprising at least one exposed functional group. At least one cell-adhesive molecule can then be coupled to the at least one exposed functional group on the self-assembled monolayer to produce a surface with enhanced cell-adhesive properties.

Claims

1. A method for producing a surface with enhanced cell-adhesive properties, comprising:

a. applying a stress to a flexible polymeric matrix wherein said polymeric matrix comprises chemical sensor particles dispersed in said matrix, said particles conferring chemical sensing capability;

b. maintaining said flexible polymeric matrix as a strained matrix;

c. modifying the surface of said strained matrix by grafting a self-assembled monolayer onto said strained matrix, said self-assembled monolayer comprising at least one exposed functional group;

d. activating said at least one functional group of said self-assembled monolayer; and

e. coupling at least one cell-adhesive molecule to said at least one activated functional group on said self-assembled monolayer.

2. The method of claim 1, wherein said strained flexible polymer matrix is released after said self-assembled monolayer becomes grafted on the surface and prior to the addition of said at least one cell-adhesive molecule.

3. The method of claim 1, wherein said strained flexible polymer matrix is maintained as a strained matrix until said at least one cell-adhesive molecule has been coupled to said at least one active functional group of said self-assembled monolayer.

4. The method of claim 1, wherein said self-assembled monolayer comprises an alkylsilane derivative represented by RSiX₃, R₂SiX₂, or R₃SiX, wherein X is chloride or alkoxy, and R is a carbon chain having said at least one functional group.

5. The method of claim 1, wherein said at least one functional group of said self-assembled monolayer are selected from amines, thiols, pyridyl, carboxyl, vinyl, sulfydryl, and aldehyde groups.

6. The method of claim 1, wherein said self-assembled monolayer has native exposed functional groups.

7. The method of claim 1, wherein said self-assembled monolayer has been chemically modified to have exposed functional groups.

8. The method of claim 1, wherein said activating said at least one functional group of said self-assembled monolayer comprises treating said self-assembled monolayer with a carbodiimide and a stabilizing compound to form at least one stabilized activated functional group on said self-assembled monolayer.

9. The method of claim 8, wherein said carbodiimide is ethyldimethylaminopropyl-carbodiimide (EDC).

10. The method of claim 8, wherein said stabilizing compound is selected from the group consisting of N-hydroxysuccinimide (NHS), hydroxysulfosuccinimide, and hydroxybenzotriazolohydrate.

11. The method of claim 10, wherein said stabilizing compound is sulfo-NHS.

12. The method of claim 10 wherein the concentration of each of said EDC and said sulfo-NHS are between about 0.5 mg/ml and about 10 mg/ml.

13. The method of claim 12, wherein said concentrations of said EDC and said sulfo-NUS are each about 4 mg/ml.

14. The method of claim 1, further comprising adjusting the density of said self-assembled monolayer to control the density of said at least one cell-adhesive molecule.

15. The method of claim 1, further comprising adjusting the density of said at least one functional group on said self-assembled monolayer to control the density of subsequently bonded at least one cell-adhesive molecule.

16. A device comprising a surface, said surface comprising

a. a flexible polymer matrix, wherein said matrix comprises chemical sensor particles dispersed in said matrix, said particles conferring chemical sensing capability;

b. a mechanically self-assembled monolayer; and

c. at least one cell-adhesive molecule coupled to said mechanically self-assembled monolayer through at least one functional group on said self-assembled monolayer.

17. The device of claim 16, wherein said chemical sensor particles are oxygen sensor particles, capable of responding to oxygen present in a solution contacting the flexible polymer matrix.

18. The device of claim 16, wherein said flexible polymer matrix comprises a polyorganosiloxane.

19. The device of claim 18, wherein said polyorganosiloxane is polydimethyl siloxane (PDMS).

20. The device of claim 16, wherein said self-assembled monolayer is an alkylsilane derivative represented by RSiX₃, R₂SiX₂, or R₃SiX, wherein X is chloride or alkoxy, and R is a carbon chain comprising said at least one functional group.

21. The device of claim 16, wherein said at least one functional group of the self-assembled monolayer are amines, thiols, pyridyl, carboxyl, vinyl, sulfydryl, or aldehyde groups.

22. The device of claim 21, wherein said self-assembled monolayer is a chlorosilane-based oligomer or polymer.

23. The device of claim 22, wherein said self-assembled monolayer is a trichiorosilane-based oligomer or polymer.

24. The device of claim 16, wherein said cell-adhesive molecule comprises one or more peptides or polypeptides.

25. The device of claim 24, wherein said one or more polypeptides is an extracellular matrix (ECM) molecule.

26. The device of claim 25, wherein said ECM molecule is laminin.

27. The device of claim 25, wherein said ECM molecule is fibronectin.

28. The device of claim 24, wherein said one or more polypeptides is an antibody or antigen-binding fragment thereof.

29. The device of claim 24, wherein said one or more polypeptides is a growth factor.

30. The device of claim 16, wherein said polymer matrix is in the form of a three-dimensional scaffold having internal surfaces to which the self-assembled monolayer is grafted and the cell-adhesive molecule is bonded.

31. The device of claim 16, wherein said polymer matrix is characterized by a strain of up to about 200% in response to an effective stress.

32. The device of claim 16, wherein said polymer matrix is characterized by a strain of up to about 100% in response to an effective stress.

33. The device of claim 32, wherein said polymer matrix is characterized by a strain of between about 40% and about 80% in response to an effective stress.

34. The device of claim 32, wherein said polymer matrix is characterized in that it undergoes an elastic stress-strain response in which the polymer matrix returns to approximately its original length after application and cessation of the stress.

35. The device of claim 16, which is susceptible to deformation upon application of mechanical forces such that adherent cells cultured in said device are subjected to the mechanical forces applied to and through the polymer matrix.