Process for manufacturing zirconia-treated titanium dioxide pigments

• US 7,238,231 B1
• Filed: 11/16/2006
• Issued: 07/03/2007
• Est. Priority Date: 11/16/2006
• Status: Active Grant

• Current Assignee: Tronox LLC (Tronox Holdings Plc)
• Original Assignee: Tronox LLC (Tronox Holdings Plc)
• Inventors: Elliott, Jeffrey D., Ray, Harmon E., Craig, Daniel H.
• Primary Examiner(s): Green; Anthony J.
• Application Number:
  US11/600,643
• Time in Patent Office: 229 Days
• Field of Search: 106/436, 106/437, 106/438, 423/598, 427/215, 427/218
• US Class Current: 106/438
• CPC Class Codes: C01G 23/07 Producing by vapour phase processes, e.g. halide oxidation
• CPC Class Codes: C01P 2004/84 one phase coated with the other
• CPC Class Codes: C09C 1/3623 Grinding
• CPC Class Codes: C09C 1/363 Drying, calcination
• CPC Class Codes: C09C 1/3661 Coating
• CPC Class Codes: C09C 1/3692 Combinations of treatments provided for in groups C09C1/3615 - C09C1/3684

Abstract

An improved process is described for manufacturing zirconia-treated titanium dioxide pigments, wherein the zirconia treatment is accomplished in the process of fluidizing a titanium dioxide filter or press cake and then drying the same, through the addition to the filter or press cake of one or more alkaline water-soluble zirconium reagents selected from ammonium zirconyl carbonate, the water-soluble ammonium zirconyl carboxylates and mixtures of these. Aqueous solutions of such zirconium reagents, in addition to being effective for imparting a zirconia surface treatment to the titanium dioxide materials, also prove to be effective fluidizing agents for forming high solids dispersions of the zirconia-treated titanium dioxide pigment materials which can be spray dried without substantial dilution and excessive energy requirements.

Claims

1. A process for manufacturing zirconia-treated titanium dioxide, comprising the steps of:

a) forming a mixture comprising a titanium dioxide material in water;

b) wet milling said mixture;

c) after step b), optionally depositing on said wet milled titanium dioxide material one or more inorganic oxides selected from the group consisting of the oxides of aluminum, boron, cerium, phosphorus, silicon, tin, titanium and zirconium;

d) achieving a pH of the mixture resulting from steps b) or c) between about 5 and about 9, whereby the titanium dioxide material is sufficiently flocculated to be recovered by vacuum or pressure filtration;

e) removing said titanium dioxide material from said mixture by vacuum or pressure filtration;

f) washing the titanium dioxide material recovered by filtration;

g) converting the washed titanium dioxide material to a fluid dispersion by addition of one or more alkaline water-soluble zirconium reagents selected from the group consisting of ammonium zirconyl carbonate, the water-soluble ammonium zirconyl carboxylates and mixtures of these;

h) drying the dispersion to yield a dry zirconia surface treated titanium dioxide powder.

2. A process as defined in claim 1, wherein the titanium dioxide material is a rutile titanium dioxide intermediate produced from titanium tetrachloride using a vapor phase oxidation step.

3. A process as defined in claim 2, wherein the titanium dioxide material acted upon possesses a crystalline lattice, and is further characterized in that, other than any inorganic oxides formed in the crystalline lattice of the titanium dioxide intermediate during the vapor phase oxidation step, substantially no inorganic oxides have been deposited on said titanium dioxide material prior to optional step c) or step g).

4. A process as defined in claim 1, wherein after the addition of one or more alkaline water-soluble zirconium reagents, the resulting fluid dispersion is characterized by a titanium dioxide solids content of at least about 50 percent by weight.

5. A process as defined in claim 4, wherein the resulting fluid dispersion is characterized by a titanium dioxide solids content of at least about 55 percent by weight.

6. A process as defined in claim 5, wherein the resulting fluid dispersion is characterized by a titanium dioxide solids content of at least about 60 percent by weight.

7. A process as defined in claim 1, wherein the one or more alkaline water-soluble zirconium reagents are selected from the group consisting of ammonium zirconyl carbonate, ammonium zirconyl acetate, ammonium zirconyl formate and mixtures thereof.

8. A process as defined in claim 1, wherein the one or more alkaline water-soluble zirconium reagents are added in aqueous solution form, in which the zirconium reagent or reagents are present at a concentration of between about 20 percent and about 50 percent.

9. A process as defined in claim 1, wherein the water-soluble zirconium reagents used represents between about 0.05 percent and 1.5 percent by weight of finished pigment of deposited zirconia.

10. A process as defined in claim 1, wherein the water-soluble zirconium reagents used represents between about 0.1 percent and 0.5 percent by weight of finished pigment of deposited zirconia.

11. A process as defined in claim 1, wherein the drying step is performed by spray drying of the dispersion.