Broad band-cholesteric liquid crystal film and process for producing the same, circularly polarizing plate, linearly polarizing element, illuminator, and liquid-crystal display

• US 7,294,303 B2
• Filed: 01/08/2004
• Issued: 11/13/2007
• Est. Priority Date: 01/10/2003
• Status: Expired due to Fees

• Current Assignee: Nitto Denko Corporation
• Original Assignee: Nitto Denko Corporation
• Inventors: Hara, Kazutaka, Takahashi, Naoki, Fukuoka, Takahiro
• Primary Examiner(s): Dye; Rena
• Assistant Examiner(s): HON, SOW FUN
• Application Number:
  US10/542,065
• Publication Number:
  US 20060119783A1
• Time in Patent Office: 1,405 Days
• Field of Search: 428/1.1, 428/1.3, 252/585, 252/299.01, 349/96, 349/98, 349/113, 349/115, 349/176, 349/194, 349/118, 430/20, 522 1- 2, 264/494, 264/496
• US Class Current: 264/494
• CPC Class Codes: C09K 2323/03 Viewing layer characterised by chemical composition
• CPC Class Codes: G02B 5/3016 involving passive liquid crystal elements optical properties of liquid crystals G02F1/0063; polarising elements associated with active liquid crystal devices G02F1/133528

Abstract

A broad band cholesteric liquid crystal film of the present invention comprises a cholesteric liquid crystal film obtained by polymerizing a liquid crystal mixture containing a polymerizable mesogen compound (a), a polymerizable chiral agent (b) and a photopolymerization initiator (c) between two substrates with ultraviolet light, and has a reflection bandwidth of 200 nm or more. The broad band cholesteric liquid crystal film of the present invention has a broad reflection band and is excellent in durability.

Claims

1. A manufacturing method for a broad band cholesteric liquid crystal film comprising:

polymerizing a liquid crystal mixture that is free of an ultraviolet absorbent, containing a polymerizable mesogen compound (a), a polymerizable chiral agent (b) and a photopolymerization initiator (c) between two substrates, by irradiation of one side with ultraviolet light having an intensity of 1 to 20mW/cm², wherein the two substrates are made of the same material, the broad band cholesteric liquid crystal film has a reflection bandwidth of 300 nm or more, a pitch length in the cholesteric liquid crystal film changes so as to narrow continuously from a side irradiated with ultraviolet light, and the pitch length is changed such that the difference in pitch length between the side of ultraviolet light irradiation and the opposite side is made at least 100 nm.

2. The manufacturing method for a broad band cholesteric liquid crystal film according to claim 1, wherein the polymerizable mesogen compound (a) has one polymerizable functional group and the polymerizable chiral agent (b) has two or more polymerizable functional groups.

3. The manufacturing method for a broad band cholesteric liquid crystal film according to claim 1, wherein the molar absorption coefficient of the polymerizable mesogen compound (a) is 50 to 500 dm³·

mol<sup>−

1</sup>·

cm<sup>−

1</sup> at 365 nm.

4. The manufacturing method for a broad band cholesteric liquid crystal film according to claim 1, wherein the polymerizable mesogen compound (a) is a compound represented by the following general formula (1):

5. The manufacturing method for a broad band cholesteric liquid crystal film according to claim 1, wherein the coating thickness of the liquid crystal mixture is in the range of from 5 to 20 μ

m.

6. The manufacturing method for a broad band cholesteric liquid crystal film according to claim 1, wherein the polymerization temperature upon ultraviolet light irradiation is 140°

C. or less.

7. The manufacturing method for a broad band cholesteric liquid crystal film according to claim 1, wherein the irradiation time of ultraviolet light is 5 minutes or less.

8. The manufacturing method for a broad band cholesteric liquid crystal film according to claim 1, wherein a mixing amount of the polymerizable chiral agent (b) is in the range of from 3 to 7 parts by weight relative to 100 parts by weight of a total amount of the polymerizable mesogen compound (a) and the polymerizable chiral agent (b).

9. The manufacturing method for a broad band cholesteric liquid crystal film according to claim 1, wherein a mixing amount of the photopolymerization initiator (c) is in the range of from 0.01 to 10 parts by weight relative to 100 parts by weight of a total amount of the polymerizable mesogen compound (a) and the polymerizable chiral agent (b).

10. The manufacturing method for a broad band cholesteric liquid crystal film according to claim 1, wherein a mixing amount of the photopolymerization initiator (c) is in the range of from 0.05 to 5 parts by weight relative to 100 parts by weight of a total amount of the polymerizable mesogen compound (a) and the polymerizable chiral agent (b).