Heating apparatus and process for drawing polyolefin fibers

• US 7,370,395 B2
• Filed: 11/01/2006
• Issued: 05/13/2008
• Est. Priority Date: 12/20/2005
• Status: Active Grant

• Current Assignee: Honeywell International Inc.
• Original Assignee: Honeywell International Inc.
• Inventors: Tam, Thomas Yiu-Tai
• Primary Examiner(s): VANATTA, AMY B
• Application Number:
  US11/591,090
• Publication Number:
  US 20070137064A1
• Time in Patent Office: 559 Days
• Field of Search: 282/45, 282/46, 282/40, 282/19, 282/20, 281/722, 261/06, 26/99, 572/87, 34/60, 346/23, 342/09, 264/211.14, 264/211.15, 264/211.17, 264/211.18, 264/210.8, 264/290.5, 428/401, 428/364
• US Class Current: 28/246
• CPC Class Codes: D02J 1/22 Stretching or tensioning, shrinking or relaxing, e.g. by use of overfeed and underfeed apparatus, or preventing stretch stretch spinning D01D5/12
• CPC Class Codes: D02J 13/00 Heating or cooling the yarn, thread, cord, rope, or the like, not specific to any one of the processes provided for in this subclass heating, cooling or drying during spinning or twisting D01H; drying of yarns or the like, in general F26B

Abstract

A heating apparatus and process useful for drawing ultrahigh molecular weight polyolefin fibers, such as polyethylene fibers. The heating apparatus includes a first set of rolls and a plurality of aligned ovens. The apparatus includes a second set of rolls at the exit of the ovens which rolls are adapted to provide the desired drawing of the polyolefin fibers. The apparatus and process provide a single draw step in a heated environment, with the use of preferably four or six horizontal ovens.

Claims

1. A heating apparatus for drawing ultrahigh molecular weight polyolefin fibers in a one stage draw with continuous heating, said heating apparatus consisting essentially of:

a first set of rolls;

a plurality of horizontally aligned ovens, said plurality of ovens having one end adjacent to said first set of rolls and an opposite end, said ovens being arranged such that their respective ends are in abutting relationship to thereby provide a relatively long continuous oven such that said fibers are conveyed from said one end of said continuous oven to said opposite end of said continuous oven, and

a second set of rolls adjacent to said opposite end of said plurality of ovens, said first and second set of rolls being adapted to provide the desired drawing of said polyolefin fibers and to convey said fibers through said continuous oven.

2. The heating apparatus of claim 1 wherein said fibers comprise ultrahigh molecular weight polyethylene fibers.

3. The heating apparatus of claim 1 wherein only a portion of said first set of rolls are heated.

4. The heating apparatus of claim 1 wherein said ovens are hot air circulating ovens.

5. The heating apparatus of claim 1 comprising at least four horizontally aligned ovens.

6. The heating apparatus of claim 1 comprising at least six horizontally aligned ovens.

7. The heating apparatus of claim 2 wherein each of said first set and said second set of rolls comprises 7 rolls.

8. The heating apparatus of claim 2 wherein each of said first set and said second set of rolls comprises 9 rolls.

9. The heating apparatus of claim 1 including means for transporting said fibers through said ovens in an approximate straight line.

10. The heating apparatus of claim 1 wherein said first and second sets of rolls comprise the only rolls in said heating apparatus and said fibers are unsupported between said first set of rolls and said second set of rolls.

11. A process for drawing ultrahigh molecular weight polyolefin fibers, said process comprising passing said fibers through a heating apparatus, said heating apparatus consisting essentially of:

a first set of rolls;

a plurality of horizontally aligned ovens, said ovens being arranged such that their respective ends are in abutting relationship to thereby provide a relatively long continuous oven, said plurality of ovens having one end adjacent to said first set of rolls and an opposite end; and

a second set of rolls adjacent to said opposite end of said plurality of ovens, said first and second set of rolls being operated under conditions to provide the desired drawing of said polyolefin fibers, and

drawing said fibers between said first set of rolls and said second set of rolls to a predetermined draw ratio in a one stage draw with continuous heating of said fibers, with said fibers being conveyed from said one end of said continuous oven to said opposite end of said continuous oven and through said continuous oven.

12. The process of claim 11 wherein said fibers comprise polyethylene fibers.

13. The process of claim 11 wherein only a portion of said first set of rolls are heated.

14. The process of claim 11 wherein said ovens are hot air circulating ovens.

15. The process of claim 11 wherein said apparatus comprises at least four horizontally aligned ovens.

16. The process of claim 11 wherein said apparatus comprises at least six horizontally aligned ovens.

17. The process of claim 12 wherein each of said first set and said second set of rolls comprises 7 rolls.

18. The process of claim 12 wherein each of said first set and said second set of rolls comprises 9 rolls.

19. The process of claim 11 wherein said fibers are transported through said ovens in an approximate straight line.

20. The process of claim 11 wherein said fibers are not supported by any structure in said ovens.

21. The process of claim 11 wherein said fibers are drawn to a draw ratio of from about 1.1:

1 to about 15;

1.

22. The process of claim 11 wherein said fibers are drawn to a draw ratio of from about 1.2:

1 to about 10;

1.

23. The process of claim 11 wherein said process operates at a line speed of from about 20 to about 100 meters/min.

24. The process of claim 11 wherein the temperature in said ovens is from about 125°

C. to about 160°

C.

25. The process of claim 11 wherein the temperature in said ovens is from about 130°

C. to about 150°

C.

26. The process of claim 11 wherein said first and second sets of rolls comprise the only rolls in said heating apparatus and wherein said fibers are unsupported between said first set of rolls and said second set of rolls.

27. The process of claim 11 wherein the fibers resulting from said process have a tenacity of at least about 30 grams per denier.

28. The process of claim 12 wherein the fibers resulting from said process have a tenacity of at least about 35 grams per denier and a initial tensile modulus of at least about 1,200 g/d.

29. A product formed by the process of claim 11.