Urethane based coating applied in-line for improved ink adhesion

• US 7,378,155 B2
• Filed: 03/18/2004
• Issued: 05/27/2008
• Est. Priority Date: 03/25/2003
• Status: Active Grant

• Current Assignee: Taghleef Industries, Inc. (Al Ghurair Family)
• Original Assignee: Applied Extrusion Technologies Incorporated (Al Ghurair Family)
• Inventors: Gillie, James Kevin
• Primary Examiner(s): TRAN, THAO T
• Application Number:
  US10/803,360
• Publication Number:
  US 20040191529A1
• Time in Patent Office: 1,531 Days
• Field of Search: 428/423.1, 428/424.8, 428/424.2, 428/523
• US Class Current: 428/424.8
• CPC Class Codes: B32B 2038/0028 Stretching, elongating
• CPC Class Codes: B32B 2255/10 on synthetic resin layer or on natural or synthetic rubber layer
• CPC Class Codes: B32B 2255/26 Polymeric coating
• CPC Class Codes: B32B 2307/518 bi-axially
• CPC Class Codes: B32B 2323/10 Polypropylene
• CPC Class Codes: B32B 27/08 of synthetic resin
• CPC Class Codes: B32B 27/18 characterised by the use of special additives
• CPC Class Codes: B32B 27/32 comprising polyolefins comprising vinyl (co)polymers or acrylic (co)polymers B32B27/30
• CPC Class Codes: C08J 2323/12 Polypropene
• CPC Class Codes: C08J 2475/00 Characterised by the use of polyureas or polyurethanes; Derivatives of such polymers
• CPC Class Codes: C08J 7/0427 with only one layer of a composition containing a polymer binder with more layers C08J7/042
• CPC Class Codes: C08J 7/043 Improving the adhesiveness of the coatings per se, e.g. forming primers adhesives in the form of films or foils characterised by the primer layers between the polymer carriers and the adhesives C09J7/50
• CPC Class Codes: Y10T 428/31573 Next to addition polymer of ethylenically unsaturated monomer
• CPC Class Codes: Y10T 428/31587 Hydrocarbon polymer [polyethylene, polybutadiene, etc.]
• CPC Class Codes: Y10T 428/31935 Ester, halide or nitrile of addition polymer
• CPC Class Codes: Y10T 428/31938 Polymer of monoethylenically unsaturated hydrocarbon

Abstract

A printable, coated, biaxially oriented film is provided that includes a polypropylene base film having a first and a second side, and a urethane coating on the first side. The coating has been applied to the base film between a machine direction orientation and a transverse direction orientation of a two step tentering operation. A method for manufacturing the film is also provided which includes the steps of forming a base film of a substantially uniform film layer of polypropylene, uniaxially orienting the base film by machine direction stretching, applying a coating of urethane to a first side of the uniaxially oriented base film, and biaxially orienting the coated film by stretching the film transversely to the machine direction.

Claims

1. A printable, coated, biaxially oriented film, comprising:

(a) a polymeric base film having a predominant polymer, and a first and a second side, said predominant polymer being polypropylene; and

(b) a urethane coating on said first side, said coating having been applied to said base film between a machine direction orientation and a transverse direction orientation of a two step tentering operation.

2. The film of claim 1, wherein the base film additionally comprises a base film antiblock agent.

3. The film of claim 2, wherein the base film antiblock agent is present at up to 1% by weight of the film.

4. The film of claim 2, wherein the base film antiblock agent is present at up to 0.5% by weight of the film.

5. The film of claim 2, wherein the base film antiblock agent is an antiblock agent selected from the group consisting of silica-based, silicone-based, and a blend of silica-based and silicone-based antiblock agents.

6. The film of claim 1, wherein the urethane coating comprises a waterborne urethane dispersion.

7. The film of claim 1, wherein the urethane coating comprises a waterborne urethane dispersion blended with waterborne acrylic dispersions.

8. The film of claim 1, wherein the urethane coating comprises a crosslinking agent.

9. The film of claim 8, wherein the crosslinking agent is present in the coating at up to 1% by dry weight.

10. The film of claim 8, wherein the crosslinking agent is polyfunctional aziridine crosslinking agent at up to 1% by dry weight of the coating.

11. The film of claim 1, wherein the urethane coating comprises a coating antiblock agent.

12. The film of claim 11, wherein the urethane coating comprises up to 1% coating antiblock agent based on dry component weight of the coating.

13. The film of claim 11, including a base film antiblock agent selected from the group consisting of silica-based, silicone-based, and a blend of silica-based and silicone-based antiblock agents.

14. The film of claim 1, including a surface treatment on the first side beneath the urethane coating.

15. The film of claim 14, wherein the surface treatment on the first side comprises an oxidative treatment.

16. The film of claim 1, including a surface treatment on the second side.

17. The film of claim 16, wherein the surface treatment on the second side comprises an oxidative treatment.

18. The film of claim 1, wherein the polypropylene is a polypropylene homopolymer.

19. The film of claim 1, wherein the polypropylene is a copolymer of propylene.

20. The film of claim 1, wherein the polypropylene is a blend of homopolymers and copolymers.

21. The film of claim 1, wherein the base film is a coextruded structure.

22. The film of claim 21, wherein the coextruded structure has at least three layers.

23. The film of claim 21, wherein the coextruded structure includes a core and at least one skin layer.