Hybrid optical/electronic structures fabricated by a common molding process

• US 7,391,572 B2
• Filed: 03/01/2006
• Issued: 06/24/2008
• Est. Priority Date: 03/01/2006
• Status: Expired due to Fees

• Current Assignee: International Business Machines Corporation
• Original Assignee: International Business Machines Corporation
• Inventors: DeCusatis, Casimer, Jacobowitz, Lawrence
• Primary Examiner(s): Ben; Loha
• Application Number:
  US11/365,011
• Publication Number:
  US 20070206288A1
• Time in Patent Office: 846 Days
• Field of Search: 359/619, 359/620, 359/626, 359/456, 359/796, 359/808, 359/809, 359/665, 359/819, 430320-322, 430/397, 430/945, 430/966, 264/1.1, 264/1.2, 264/1.7, 264/2.4, 264/2.5, 264/40.5, 264/219, 264/328.13, 264/328.16, 264/500, 216/8, 216/9, 216/24, 216/39, 216/49, 385/18, 385/119, 205/70, 438/60, 438/70, 425/149, 425/150, 425/542
• US Class Current: 359/619
• CPC Class Codes: B29D 11/00365 Production of microlenses lenticular sheets B29D11/00278
• CPC Class Codes: C03B 19/02 by casting molten glass, e.g. injection moulding

Abstract

Disclosed is a method of fabricating a molded structure including both micro lenses and metallic pins. The method comprises the steps of providing a mold apparatus having a set of first cavities and a set of second cavities, depositing a first material in the first cavities to form a set of metallic pins, and depositing a second material in the second cavities to form a set of micro lenses. The formed molded structure comprises a substrate, a set of molded microlenses on said substrate, and a set of molded metallic pins on that same substrate. The metallic pins may be formed as alignment pins or as electrical connectors. The invention enables the micro lenses and metallic pins to be manufactured by way of molding on a common substrate for the first time.

Claims

1. A method of fabricating a molded structure including both micro lenses and metallic pins, comprising the steps of:

providing a mold apparatus having a set of first cavities and a set of second cavities;

depositing a first material in the first cavities to form a set of metallic pins; and

depositing a second material in the second cavities to form a set of micro lenses.

2. A method according to claim 1, wherein:

said first material has a higher melting point than said second material; and

said first material is deposited in the mold apparatus before the second material.

3. A method according to claim 1, comprising the further step of using non-linear scan paths during injection molding to facilitate selective fill of different cavities with different materials.

4. A method according to claim 1, wherein the step of depositing the first material includes the steps of:

providing a fill mechanism for depositing the first material in the mold apparatus; and

moving said fill mechanism across the mold apparatus to deposit said first material in the set of first cavities.

5. A method according to claim 4, wherein said moving step includes the step of controlling movement of the fill mechanism, during said moving step, to prevent said fill mechanism from moving over the set of second cavities.

6. A method according to claim 4, comprising the further steps of:

covering said set of second cavities during said moving step with a removable sacrificial cover to prevent said first material from being deposited in said set of second cavities; and

removing said sacrificial cover after the step of depositing the first material in the set of first cavities to make way for the second material.

7. A method according to claim 1, comprising the further step of molding an optical polymer to form a substrate of the molded structure, said substrate surrounding portions of the metallic pins and forming a supporting base for the micro lenses.