Porous calcium phosphate networks for synthetic bone material

• US 7,758,896 B2
• Filed: 04/15/2005
• Issued: 07/20/2010
• Est. Priority Date: 04/16/2004
• Status: Expired due to Fees

• Current Assignee: University Of Massachusetts
• Original Assignee: University Of Massachusetts
• Inventors: Hyers, Robert, SanSoucie, Michael
• Primary Examiner(s): PAK, JOHN D
• Application Number:
  US11/107,066
• Publication Number:
  US 20050255159A1
• Time in Patent Office: 1,922 Days
• Field of Search: 424/602, 424/423, 424/484
• US Class Current: 424/602
• CPC Class Codes: A61K 33/42 Phosphorus; Compounds thereof
• CPC Class Codes: A61L 27/12 Phosphorus-containing materials, e.g. apatite
• CPC Class Codes: A61L 27/56 Porous materials, e.g. foams or sponges

Abstract

A porous composition comprising a hydroxyapatite material, as can be made from a mixture of calcium phosphate, calcium oxide and a removable inorganic porogen. In other embodiments, the present invention provides a method of making such a porous hydroxyapatite material or using a ternary system to prepare a two-phase composition enroute to a biomimetic bone material.

Claims

1. A calcium phosphate spinodal decomposition product composition comprising a first phase comprising hydroxyapatite and tricalcium phosphate, and a second phase comprising a removable inorganic porogen, said phases interconnected and having continuous networks, said second phase interconnection having a substantially constant cross-sectional dimension.

2. The composition of claim 1 wherein said removable porogen is a transition metal oxide.

3. The composition of claim 2 wherein said transition metal oxide is selected from the group consisting of iron oxide, nickel oxide, cobalt oxide, manganese oxide and copper oxide.

4. The composition of claim 3 wherein said composition comprises an iron oxide content ranging from about 25 wt. % to about 65 wt. %.

5. The composition of claim 1 wherein each of said first and second phases have a cross-sectional dimension less than about 1.5 μ

m.

6. A calcium phosphate spinodal decomposition product of a molten mixture comprising iron oxide, calcium oxide and calcium phosphate, said product within the immiscibility region of a phase diagram of a CaO—

P₂O₅—

FeO ternary system, said product comprising two interconnected phases having continuous networks.

7. The product of claim 6 comprising an iron oxide content ranging from about 25 wt. % to about 65 wt. %.

8. The product of claim 7 wherein said iron oxide content is about 40 wt. %.

9. The product of claim 6 comprising a Ca/P ratio between about 1.5 and about 2.0.

10. The product of claim 6 wherein each of said phases has a cross-sectional dimension less than about 1.5 μ

m.

11. A method of using a ternary system to prepare a biomimetic bone material, said method comprising:

providing a mixture of a transition metal oxide, calcium oxide and calcium phosphate components, each said component in an amount sufficient to provide a spinodal decomposition product within the immiscibility region of a phase diagram of a CaO—

P₂O₅—

MO ternary system, where MO is selected from the group consisting of transition metal oxides;

heating said mixture over a temperature range and a time sufficient for spinodal decomposition of said mixture, said spinodal decomposition product comprising two interconnected phases having continuous networks; and

removing said MO component from said spinodal decomposition product, to provide a biomimetic bone material.

12. The method of claim 11 wherein said mixture is melted, and cooled at a rate sufficient to affect product microstructure.

13. The method of claim 12 wherein at least one of the amount of said MO and said rate of cooling affects the porosity of said biomimetic bone material.

14. The method of claim 11 wherein said removal comprises contacting said MO component with at least one of an acid and a chelating agent.

15. The method of claim 11 wherein said biomimetic bone material is sterilized.

16. A composition comprising a calcium phosphate spinodal decomposition product comprising a first phase comprising hydroxyapatite and tricalcium phosphate, and a second phase comprising a removable inorganic porogen, said phases interconnected and having continuous networks, said porogen at least partially removed to provide said composition a matrix of interconnected pores.

17. The composition of claim 16 wherein said matrix has a porosity ranging from about 30% to about 60%.

18. The composition of claim 17 wherein said pore size ranges from about 3 μ

m to about 700 μ

m.

19. The composition of claim 18 wherein said porosity ranges from about 55% to about 70%.

20. The composition of claim 19 wherein said matrix has a pore size chosen from a size ranging from about 500 μ

m to about 600 μ

m, a size ranging from about 190 μ

m to about 230 μ

m, and a size ranging from about 3 μ

m to about 30 μ

m.

21. The composition of claim 20 wherein said pores are of a dimension chosen from the pore dimension of a cancellous bone and the pore dimension of a cortical bone.